Environment-friendly industrial briquette composite binder and preparation method thereof

An environmentally friendly, binder technology, used in the petroleum industry, solid fuels, fuels, etc., can solve the problems of low spheroidization rate, many combustion products, long production cycle, etc., to improve thermal strength and thermal stability. Stability, wide application range, and the effect of enhancing cold strength

Inactive Publication Date: 2014-05-21
GUANGXI LIUZHOU JUNYE TECH
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be divided into two types: inorganic binder and organic binder. The briquettes produced with inorganic binders have high thermal stability, but have a lot of ash, and the fixed carbon content of briquettes has a large decrease in combustion efficiency. Low, such as briquettes produced by using lime as a binder, not only has a lot of ash, but also has a fixed carbon reduction of more than 18%; briquettes produced by using organic binders have high cold strength, but high volatile content and poor thermal stability , there are many combustion products, and the process is relatively complicated. For example, the production of briquettes using asphalt requires dry distillation at 500-550°C, and the high volatile content causes secondary pollution to the environment.
Using the above-mentioned existing binders to make briquettes, the pelleting rate is not very high, only 60-80%, and the production cycle is long

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1: each raw material component and its weight / number ratio are: 36 parts of humic acid, 36 parts of bauxite, 50 parts of plant phenol eugenol, 20 parts of furfuryl alcohol, 2 parts of potassium hydroxide and 8 parts of inert Solvent diols (can also be replaced by diol derivatives).

[0030] The production method is:

[0031] 1, humic acid is ground into powder more than 60 orders;

[0032] II, the powder of step I is prepared, and the bauxite is ground into a powder of more than 100 meshes simultaneously, and the mixture powder and bauxite powder are mixed in a ratio of 36:36 by weight;

[0033] Ⅲ. On the basis of the mixture obtained in step II, add 50 parts of plant phenols according to the weight ratio and add 2 parts of catalyst when the temperature is raised to 40 ° C ~ 60 ° C,

[0034] Ⅳ. Raise the temperature to 100°C-120°C, keep it warm for 0.5-1.5 hours, continue to heat up to 280°C-350°C, keep it warm for 1.5-3.5 hours,

[0035] Ⅴ. Lower the temp...

Embodiment 2

[0039] Example 2: 48 parts of humic acid, 48 parts of alumina, 60 parts of guaiacol, 30 parts of furfuryl alcohol, 6 parts of barium hydroxide and 14 parts of inert solvent ester.

[0040] The production method is:

[0041] 1, humic acid is ground into powder more than 60 orders;

[0042] II, the powder of step I is prepared, and the bauxite is ground into a powder of more than 100 mesh at the same time, and the mixture powder and bauxite powder are mixed in a weight ratio of 48:48;

[0043] Ⅲ. On the basis of the mixture obtained in step II, add 60 parts of plant phenols according to the weight ratio and add 6 parts of catalyst when the temperature is raised to 40 ° C ~ 60 ° C,

[0044] Ⅳ. Raise the temperature to 100°C-120°C, keep it warm for 0.5-1.5 hours, continue to heat up to 280°C-350°C, keep it warm for 1.5-3.5 hours,

[0045] Ⅴ. Lower the temperature to 40°C-60°C, adjust the pH value to 4-5.5, add 30 parts of furfuryl alcohol, raise the temperature to 80°C-110°C, an...

Embodiment 3

[0049] Example 3: a mixture of 60 parts of humic acid, 60 parts of alumina, 70 parts of cardanol, 40 parts of furfuryl alcohol, 10 parts of potassium hydroxide and 20 parts of inert solvent water and ethanol.

[0050] The production method is:

[0051] 1, humic acid is ground into powder more than 60 orders;

[0052] II, the powder of step I is prepared, and the bauxite is ground into a powder of more than 100 mesh at the same time, and the mixture powder and bauxite powder are mixed in a ratio of 60:60 by weight;

[0053] Ⅲ. On the basis of the mixture obtained in step II, add 70 parts of plant phenols according to the weight ratio and add 10 parts of catalyst when the temperature is raised to 40 ° C ~ 60 ° C,

[0054] Ⅳ. Raise the temperature to 100°C-120°C, keep it warm for 0.5-1.5 hours, continue to heat up to 280°C-350°C, keep it warm for 1.5-3.5 hours,

[0055] Ⅴ. Lower the temperature to 40°C-60°C, adjust the pH value to 4-5.5, add 40 parts of furfuryl alcohol, raise ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thermal stabilityaaaaaaaaaa
thermal stabilityaaaaaaaaaa
thermal stabilityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly industrial briquette composite binder and a preparation method thereof. Humic acid, alumina, common seepweed herb seed cake meal, water and the like are used as raw materials; the preparation process is simple and convenient; the briquette prepared by the method has the advantages of little drop of the solid carbon content, good binding property, high pelletizing rate, high cold / hot strength, good thermal stability, low cost, short production cycle and the like.

Description

technical field [0001] The invention relates to an industrial briquette binder and a preparation method thereof, in particular to an environment-friendly industrial briquette composite binder and a preparation method thereof. Background technique [0002] The existing binders for producing industrial briquettes mainly take white mud, lime, clay, coal tar, asphalt, cement, starch, etc. as raw materials. It can be divided into two types: inorganic binder and organic binder. The briquettes produced with inorganic binders have high thermal stability, but have a lot of ash, and the fixed carbon content of briquettes has a large decrease in combustion efficiency. Low, for example, briquettes produced by using lime as a binder not only have a lot of ash, but also have a fixed carbon reduction of more than 18%; briquettes produced by using organic binders have high cold strength, but high volatile content and poor thermal stability , There are many combustion products, and the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10L5/10
Inventor 林国友罗永城梁剑徐国华
Owner GUANGXI LIUZHOU JUNYE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com