Nanometer surface modifier and preparation method and using method thereof
A surface modifier, nanotechnology, applied in chemical instruments and methods, porphine/acridine porphine, inorganic pigment treatment, etc., can solve the problems of poor mutual solubility, reduce oil absorption, improve uniform stability, and improve gloss degree of effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0019] Example 1: Weigh the stabilizer sodium phosphate and the thickener sodium carboxymethyl cellulose, the dosages are 4 parts and 1 part respectively, put them into the reaction kettle, and then add 85 parts of water. Heating up to 90°C, high-speed emulsification (stirring speed 10,000 rpm) for 10 min. Add nano TiO 2 powder, the particle size is 200 nm, the feeding weight is 5 parts, the temperature is raised to 90 ° C, and the high-speed emulsification (stirring speed is 10000 rpm) for 5 min. Add ammonia water, adjust the pH to 10, and emulsify at high speed for 5 min. A nanometer surface modifier with a solid content of 10% was prepared. Weigh the lead chrome yellow pigment and pigment orange P013 and put them into the reaction kettle, the ingredient ratio is 1:5, add distilled water, the solid-to-liquid ratio is 1:10, stir at high speed for 10 min, add nano surface modifier, the dosage is 1%, and mix at high speed After emulsification for 15 minutes, the finished pr...
Embodiment 2
[0023] Example 2: Weigh the stabilizer sodium phosphate and the thickener sodium carboxymethyl cellulose in amounts of 10 parts and 5 parts respectively, add them into the reaction kettle, and then add 70 parts of water. Heating up to 50°C, high-speed emulsification (stirring speed 10,000 rpm) for 30 min. Add nano TiO 2 Sol, the particle size is 50 nm, the feeding weight is 15 parts, high-speed emulsification (stirring speed 10000 rpm) for 30 min. Add ammonia water, pH is 8, emulsify at high speed for 5 min. A nanometer surface modifier with a solid content of 30% was prepared. Weigh the lead chrome yellow pigment and pigment orange P013 and put them into the reaction kettle, the ingredient ratio is 3:5, add distilled water, the solid-to-liquid ratio is 1:10, stir at high speed for 10 min, add nano surface modifier, the dosage is 10%, and stir at high speed After emulsification for 30 minutes, the finished product is obtained. It is measured that the oil absorption of th...
Embodiment 3
[0024] Example 3: Weigh the mixture of stabilizer sodium phosphate, polyethylene glycol-1000 and thickener polyvinylpyrrolidone in amounts of 15 parts, 5 parts and 0.2 parts respectively, and add them into the reaction kettle, and then add 70 parts of water. Heating up to 90°C, high-speed emulsification (stirring speed 10,000 rpm) for 60 min. Add nano TiO 2 Sol, the particle size is 10 nm, the feeding weight is 10 parts, high-speed emulsification (stirring speed 10000 rpm) for 60 min. Add ammonia water, pH is 8, emulsify at high speed for 5 min. A nanometer surface modifier with a solid content of 30% was prepared. Weigh molybdenum chrome red and pigment red PR254 and put them into the reaction kettle, the ratio of ingredients is 1:10, add distilled water, the ratio of solid to liquid is 1:10, stir at high speed for 10 min, add nanometer surface modifier, the dosage is 5%, and stir at high speed After emulsification for 30 minutes, the finished product is obtained. The m...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims