Method for preparing polyacrylic ester/nanoSiO2 coating printing adhesive by using Pickering emulsion polymerization method

A technology of polyacrylate and emulsion polymerization, which is used in dyeing, textile and paper making, etc., to achieve the effect of less stickiness and simple preparation process

Active Publication Date: 2014-11-19
广州麦吉高分子新材料科技有限公司
View PDF3 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, some researchers have prepared organic-inorganic composite materials by Pickering emulsion polymerization, but

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] In a 250mL three-neck flask equipped with a stirrer and a condensing 2 Sol and water total 40.694g, nano-SiO 2 The mass fraction of the sol is 30%, nano-SiO 2 The amount of sol accounted for 2.1wt% of the water amount, and stirred for 10 minutes;

[0020] Add 4.294g of methyl methacrylate, 0.53g of glycidyl methacrylate, 12.857g of butyl acrylate and 0.265g of acrylic acid dropwise, and control the dropping time for 10min;

[0021] After the dropwise addition, the temperature was raised to 75°C, 0.264g of ammonium persulfate was dissolved in 16.792g of water, and added into a three-necked flask at one time, kept for 2 hours, cooled naturally, and filtered out.

Embodiment 2

[0023] In a 250mL three-neck flask equipped with a stirrer and a condensing 2 Sol and water total 47.187g, nano-SiO 2 The mass fraction of the sol is 30%, nano-SiO 2 The amount of sol accounted for 40.94wt% of the water amount, stirring for 40min;

[0024] Add 18.927g of methyl methacrylate, 0.78g of glycidyl methacrylate, 31.532g of butyl acrylate and 0.39g of acrylic acid dropwise, and control the dropping time for 40min;

[0025] After the dropwise addition, the temperature was raised to 80°C, 0.583g of ammonium persulfate was dissolved in 23.106g of water, and added into a three-necked flask at one time, kept for 4 hours, cooled naturally, and filtered out.

Embodiment 3

[0027] In a 250mL three-neck flask equipped with a stirrer and a condensing 2 Sol and water total 40.7g, nano-SiO 2 The sol accounts for 2.5wt% of the water consumption, stirring for 20min;

[0028] Then add 17.60 g of methyl methacrylate, 0.70 g of glycidyl methacrylate, 16 g of butyl acrylate, and 0.30 g of acrylic acid, and control the dropping time for 30 minutes;

[0029] After the dropwise addition, raise the temperature to 75~80°C, dissolve 0.25g of ammonium persulfate in 18.0g of water, add it into a three-necked flask at one time, keep it warm for 4 hours, cool naturally, and filter out.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing a polyacrylic ester/nanoSiO2 coating printing adhesive by using a Pickering emulsion polymerization method. During preparation of a polyacrylic acid emulsion, the problems of poor washing fastness and poor wet rubbing fastness are caused by adding a surfactant. The method comprises the following steps: mixing and stirring nanoSiO2 sol with water, and dropwise adding methyl methacrylate, glycidyl methacrylate, butyl acrylate and acrylic acid; and raising the temperature, adding an ammonium persulfate solution, preserving heat for reacting, naturally cooling a reaction product, filtering the cooled reaction product, and discharging the filtered reaction product. The polyacrylic ester/nanoSiO2 coating printing adhesive is prepared by taking the nanoSiO2 sol, an acrylic acid monomer and the glycidyl methacrylate as raw materials through Pickering emulsion polymerization. The method has the advantages of simple process, avoidance of the use of the surfactant and environmental friendliness. Meanwhile, nanoparticles are introduced, so that a film is prevented from sticking at a high temperature.

Description

technical field [0001] The present invention relates to a kind of adhesive, be specifically related to a kind of Pickering emulsion polymerization method to prepare polyacrylate / nanometer SiO 2 Method of Pigment Printing Binder. Background technique [0002] In the printing and dyeing industry, the pigment printing process uses a polymer compound as a binder to adhere non-affinity and reactive pigments to the surface of the fiber to form the desired pattern. The process is simple, no waste water discharge, complete color spectrum, and bright colors. The pattern outline is clear, the light fastness is good, and it is suitable for various fibers and blended fabrics, so it is favored by users at home and abroad. Polyacrylic acid emulsion is a kind of pigment printing adhesive widely used. When preparing polyacrylic acid emulsion, surfactants are usually added. In the process of subsequent use, the presence of surfactants will cause poor washing fastness and wet The problem o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F220/18C08F220/14C08F220/32C08F220/06C08F2/44C08F2/22C08K3/36D06P1/52D06P1/673
Inventor 高党鸽段羲颖冯军芳吕斌马建中
Owner 广州麦吉高分子新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap