A kind of activated carbon and a technology for preparing activated carbon, applied in chemical instruments and methods, inorganic chemistry, non-metallic elements, etc., can solve the problems of long preparation process, high cost, limited supply of raw materials, etc., and achieve increased additional economic value and low cost , The effect of broadening the source of raw materials

Active Publication Date: 2016-06-08
SHENZHEN ACAD OF ENVIRONMENTAL SCI
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention aims at the disadvantages of high cost, limited supply of raw materials, and long time-consuming preparation process of the existing activated carbon preparation technology, and provides a simple and environmentally friendly method for preparing activated carbon from reed bamboo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of activated carbon preparation method and reed bamboo activated carbon

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0014] In the following examples, the production of reed bamboo activated carbon comprises the following steps:

[0015] Step (1), preprocessing. After the reed bamboo is harvested, the leaves are removed, the stems are taken out, dried in the sun for 1 to 2 days to remove moisture, then crushed into powder, and sieved to 20 mesh.

[0016] Step (2), carbonization. Mix Arundis powder and carbonization furnace bottom ash in a certain proportion, and send them to the carbonization furnace for carbonization. The carbonization furnace bottom ash used can be the bottom ash after burning various biomass fuels (such as sawdust, abandoned wetland plants) that provide heat for the carbonization process. The mixing amount (mass fraction) of bottom ash is 10-30%. The carbonization process is carried out under the condition of cutting off the air, the temperature of the carbonization furnace is 400-600°C, and the carbonization time is 10-30 minutes.

[0017] Step (3), activation. Cont...

Embodiment 1

[0023] Naturally sun-dried reed bamboo was crushed into powder, sieved to 20 mesh, mixed with 30% carbonization furnace bottom ash, and then carbonized. The temperature of the carbonization furnace was 600°C, and the carbonization time was 10 minutes. Continue to pass in the mixed gas of air and water vapor for activation, the concentration of water vapor is 15%, the activation temperature is 800°C, and the activation time is 30 minutes. After the carbonization furnace is naturally cooled to room temperature, the carbonized material is taken out, subjected to winnowing and separation, pickling and deashing, rinsing, and drying to obtain the finished Arundis activated carbon.

Embodiment 2

[0025] Naturally sun-dried reed bamboo was crushed into powder, sieved to 20 mesh, mixed with 20% carbonization furnace bottom ash, and then carbonized. The temperature of the carbonization furnace was 500°C, and the carbonization time was 20 minutes. Continue to pass in the mixed gas of air and water vapor for activation, the water vapor concentration is 10%, the activation temperature is 800°C, and the activation time is 60 minutes. After the carbonization furnace is naturally cooled to room temperature, the carbonized material is taken out, subjected to winnowing and separation, pickling and deashing, rinsing, and drying to obtain the finished Arundis activated carbon.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of activated carbon and activated carbon prepared from reed bamboo as a raw material, and uses furnace ash as an additive, and utilizes the rich alkali metal salt in the furnace ash to greatly accelerate the precipitation rate of volatile matter in the raw material, thereby shortening carbonization time and improve product quality. The preparation process includes several steps of carbonization, activation, winnowing separation, pickling and deashing, rinsing and drying. The preparation method of reed bamboo activated carbon of the present invention not only makes full use of the plant resources discarded in artificial wetlands, improves the additional economic value of wetland plants, widens the raw material source channels of activated carbon production, but also shortens the time-consuming of the preparation process to a certain extent, improves It has the advantages of low cost and simple manufacturing process.

Description

technical field [0001] The invention relates to a preparation method of activated carbon and Arundos reeds activated carbon, in particular to Arundos reeds activated carbon with large specific surface area and iodine adsorption value, which can be used in the technical fields of water treatment and waste gas treatment. Background technique [0002] Activated carbon is an excellent adsorption material, widely used in pharmaceutical, chemical, food, metallurgy and other fields. As people pay more attention to environmental protection, the demand for activated carbon in various industries is also increasing. At present, the raw materials for preparing activated carbon are still mainly coal, wood, and fruit shells. However, due to the limitation of raw material sources, the supply price of activated carbon remains high. Therefore, more and more attention has been paid to the development of cheap and easy-to-obtain activated carbon raw materials and to reduce the production cost...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01B31/10C01B32/336
Inventor 成功林静尹魁浩卢建李琼辉李明杰
Owner SHENZHEN ACAD OF ENVIRONMENTAL SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap