Glass fiber reinforced prepreg prepared from toughened environment-friendly phenolic resin

An environmentally friendly phenolic resin and prepreg technology, which is applied in the field of glass fiber reinforced prepreg to achieve the effects of high bending strength, low heat release value and high tensile strength

Inactive Publication Date: 2014-12-10
BENGBU HIGH TEMPERATURE RESISTANT RESIN FACTOR
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to overcome the existing technical defects and provide a kind of glass fiber-reinforced preform of toughened environmental protection phenolic resin with reasonable method, clear ratio, high electric strength, high tensile strength and high bending strength. Dip cloth

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass fiber reinforced prepreg prepared from toughened environment-friendly phenolic resin
  • Glass fiber reinforced prepreg prepared from toughened environment-friendly phenolic resin
  • Glass fiber reinforced prepreg prepared from toughened environment-friendly phenolic resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] In order to make the technical means, creative features, objectives and effects achieved by the present invention easy to understand, the present invention will be further elaborated below.

[0015] A kind of glass fiber reinforced prepreg cloth of toughening type environment-friendly phenolic resin, it is characterized in that: comprise following composition,

[0016] The distribution ratio of each group is as follows in weight fraction,

[0017]

[0018]

[0019] The internal release agent is oleic acid;

[0020] A kind of glass fiber reinforced prepreg cloth of toughening type environment-friendly phenolic resin, it is characterized in that: preparation method comprises the following steps,

[0021] Step 1. Synthesis of environmentally friendly phenolic resin: phenol: aniline: solid formaldehyde = 1:0.1~0.2:1.2~1.8mol ratio, the operation steps are as follows: melt 80~120g of phenol, add 1~5g of magnesium oxide, and stir for 20min , then add 1-10g of aniline,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses glass fiber reinforced prepreg prepared from toughened environment-friendly phenolic resin and relates to the technical field of processing and manufacturing of materials for synthetic resin. The glass fiber reinforced prepreg is characterized by comprising environment-friendly phenolic resin, alkali-free glass fiber cloth, a coupling agent KH-560, an internal releasing agent, pigments, silica, industrial alcohol, graphite and silicone lime. The glass fiber reinforced prepreg is reasonable in method, clear in proportion, high in electric strength, high in tensile strength and high in bending strength.

Description

Technical field: [0001] The invention relates to the technical field of material processing and production of synthetic resins, in particular to a glass fiber reinforced prepreg cloth of toughened environment-friendly phenolic resin. Background technique: [0002] As one of the three thermosetting resins, phenolic resin has a development history of more than 100 years. Its remarkable features are low price, heat resistance, ablation resistance, flame retardancy, and less smoke when burning. With the development of electronics, machinery, transportation, etc. With the rapid development of transportation and national defense industry, phenolic resin and its composite materials have also been developed rapidly, but the weakness of ordinary phenolic resin is that hydroxyl and methylene are easily oxidized, and phenolic hydroxyl generally does not participate in chemical reactions in resin synthesis. There are many hydroxyl groups, and the phenolic hydroxyl group is a polar group...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L61/10C08K7/00C08K7/14C08K3/36C08K3/04C08G8/10C08J5/04
Inventor 陈士年陈树陈瑞
Owner BENGBU HIGH TEMPERATURE RESISTANT RESIN FACTOR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap