Carving gravure ink and preparation method and safety product thereof

A technology of gravure printing ink and pigment preparation, which is applied in the printing field, can solve problems such as no relevant reports, achieve good transparency, improve layer expressiveness and anti-counterfeiting level, and improve visual effect and aesthetic sense

Active Publication Date: 2014-12-24
中钞印制技术研究院有限公司 +1
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the composition and property requirements of the existing high-saturation inks used in inkjet printing are only designed and researched for inkjet printing technology, and there are no relevant reports for inks used in engraving gravure printing technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] According to the formula in Table 1, after mixing and stirring the vehicle composition, composite filler, wax, and composite surfactant, roll it into base oil on a three-roll ink grinder. Among them, the linking material components include isocyanate modified alkyd resin, acid anhydride modified alkyd resin, pure alkyd resin, vegetable oil modified phenolic resin oil and rosin modified phenolic resin oil (note: isocyanate modified alkyd resin, acid anhydride The preparation method of modified alkyd resin refers to patent CN101362871, the same below); the composite filler is a composition of fumed silica and nano-calcium carbonate; the composite surfactant is a combination of polyether phosphate ester salt and fatty alcohol polyoxyethylene ether object, and the color value of the composite surfactant is 6 (measured by an iron-cobalt colorimeter, the same below).

[0045] The above base oil, acid value 10mgKOH / g saponified rosin modified phenolic resin and rosin ester mod...

Embodiment 2

[0052] According to the formula in Table 3, after mixing and stirring the vehicle composition, composite filler, wax, and composite surfactant, roll it into base oil on a three-roll ink grinder. Among them, the linking material components include isocyanate modified alkyd resin, anhydride modified alkyd resin, pure alkyd resin, vegetable oil modified phenolic resin oil; composite filler is a composition of nano calcium carbonate and nano barium sulfate; composite surface active The agent is a composition of fatty acid polyoxyethylene ester and dodecylbenzenesulfonate, and the color value of the composite surfactant is 3.

[0053] The above base oil, acid value 12mgKOH / g saponified rosin modified phenolic resin and oxide modified red pigment (CS-R200Y) were mixed and rolled to form a base ink with a fineness of ≤12μm.

[0054] Table 3 base ink 2 recipe

[0055] components

Dosage (%)

Anhydride modified alkyd resin

41

Isocyanate modified alkyd resi...

Embodiment 3

[0060] According to the formula in Table 5, after mixing and stirring the vehicle composition, composite filler, wax and composite surfactant, roll it into base oil on a three-roll ink grinder. Among them, the linking material components include isocyanate modified alkyd resin, anhydride modified alkyd resin, pure alkyd resin, vegetable oil modified phenolic resin oil, rosin modified phenolic resin oil; the composite filler is fumed silica and nano sulfuric acid Composition of barium; composite surfactant is the composition of polyoxyethylene sorbitan monooleate and polyamine polyamide salt, and the color value of this composite surfactant is 5.

[0061] The above base oil, saponified rosin modified phenolic resin with an acid value of 13 mgKOH / g and polyester resin modified red pigment (Hostacopy FBB02-M101) were mixed and rolled to form a base ink with a fineness of ≤12 μm.

[0062] Table 5 Base Ink 3 Recipe

[0063] components

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Acid valueaaaaaaaaaa
Login to View More

Abstract

The invention provides a carving gravure ink and a preparation method and a safety product thereof. The carving gravure ink comprises the following components by the weight percentage: 40-70% of a connecting material composition, 10-25% of a colorant, 5-20% of a composite filler, 5-15% of wax, 1-8% of a composite surfactant, 0.5-5% of an ink regulator, 0.5-3% of a drying agent, and 1-6% of a composite solvent. The invention also provides the preparation method and the safety product of the carving gravure ink. The carving gravure ink is obtained through selection and matching of the connecting material system, the colorant, the composite filler, the composite surfactant, the composite solvent and the related accessories; and the ink can effectively enhance the printing product color expressive force and increase the printing product appearance visual effects and aesthetic sense.

Description

technical field [0001] The invention relates to an engraving gravure printing ink, a preparation method and a security product, belonging to the technical field of printing. Background technique [0002] Engraving gravure printing technology is used for the printing of high-end products due to its unique pattern structure and outstanding gravure touch, especially for the printing of security products with anti-counterfeiting functions such as banknotes and special tickets. In recent years, in order to improve the unique public anti-counterfeiting technology of security products, while ensuring the feel of engraved gravure ink prints, the color saturation of engraved gravure ink prints has also attracted more and more attention. The existing engraving gravure ink, due to the selection of the used binder, the color value of the auxiliary agent, the poor transparency of the filler or the poor color saturation of the colorant, will affect the color and color saturation of the in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D11/50C09D11/105C09D11/103
Inventor 周树荣吕建英高瑞刘义龙麻宝成武建国
Owner 中钞印制技术研究院有限公司
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com