High-glass metal powder coating and preparation method thereof

A metal powder, high-gloss technology, used in powder coatings, polyester coatings, epoxy resin coatings, etc., can solve the problems of complicated coating process, increase product coating cost, difficult to remove perspiration, etc., and achieve enhanced shape control. effect, product cost reduction, product quality improvement effect

Inactive Publication Date: 2015-01-07
晁兵
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main problem of the current high-gloss metal powder coatings is that the surface of the coating has poor finger-touch resistance, that is, after human hands touch the coating, the sweat stains left on the coating surface are not only difficult to remove, but also cause rapid oxidation and discoloration of the metal flakes , seriously affects the appearance of the coated product, and also restricts the popula

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Each raw material and its weight fraction are as follows:

[0023] E-12 epoxy resin 30, indoor polyester resin 30, GLP588 leveling agent 1.5, MPP-620 degassing agent 0.1, R902 titanium dioxide 5, ultrafine barium sulfate 20, Chromal IV metallic pigment 1, fumed silica 0.1, cellulose acetate butyrate (200 mesh) 0.01.

[0024] Weigh epoxy resin E-12, indoor polyester resin, GLP588, MPP-620, R902, and ultra-fine barium sulfate, and mix them at high speed in a mixing tank, then use existing powder coating melt extrusion production equipment and technology, The base material is prepared by mixing, extruding, tablet crushing, grinding and sieving with a 180-mesh sieve. Then put 70% of the total amount of the base material and PC100 pigment into the dry mixing equipment for dry mixing and heating bonding treatment. When the bonding process is basically completed, add fumed silica, cellulose acetate butyrate and the remaining 30% base material, after being uniformly mixed at ...

Embodiment 2

[0026] E-12 epoxy resin 30, indoor polyester resin 30, PV88 leveling agent 1, MPP-620 degassing agent 0.1, ultrafine barium sulfate 40, Chromal X metal pigment 1.2, fumed silica 0.1, acetate butyric acid Cellulose (200 mesh) 0.02.

[0027] Weigh epoxy resin E-12, indoor polyester resin, PV88, MPP-620, and ultra-fine barium sulfate, and mix them at high speed in a mixing tank. , extrusion, tablet crushing, milling and sieving with a 200-mesh sieve to obtain the base material. Then put 80% of the total amount of the base material and PC100 pigment into the dry mixing equipment for dry mixing and heating bonding treatment. When the bonding process is basically completed, add fumed silica, cellulose acetate butyrate and the remaining 20% of the base material, after being uniformly mixed at a high speed, the material is discharged and sieved. When the above powder coating is lowered to room temperature, it is measured and packaged to obtain the striped powder coating product. Aft...

Embodiment 3

[0029] Each raw material and its weight fraction are as follows:

[0030] Polyester resin 60, TGIC curing agent 5, PV88 leveling agent 1, MPP-620 degassing agent 0.15, superfine barium sulfate 10, PC metal pigment 1, fumed silica 0.2, cellulose acetate butyrate (200 mesh) 0.02.

[0031] First weigh polyester resin, TGIC, PV88, MPP-620, ultra-fine barium sulfate, mix at high speed in the mixing tank, use existing powder coating melt extrusion production equipment and technology, mix, extrude, tablet and crush 1. Grinding and sieving with a 200-mesh sieve to obtain the base material. Then put 90% of the total base material and PC100 into the dry mixing equipment for dry mixing and heating bonding treatment. When the bonding process is basically completed, add fumed silica, cellulose acetate butyrate and the remaining 10 % of the base material, after being uniformly mixed at a high speed, the material is discharged and sieved. When the above-mentioned powder coating is lowered ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-glass metal powder coating which is prepared from a base material, a floating metal pigment, a powder treatment agent and a functional auxiliary by adopting a dry-mixing method, wherein the base material comprises resin, a curing agent, a flatting agent, filler and pigments and a degassing agent and is prepared by high-speed mixing, melt extrusion and abrasive powder sieving. Then, the product provided by the invention is prepared by adopting a dry-mixing and adhering process with the base material which is added in two steps. By virtue of granular control of a cellulose acetate butyrate material and the two-step dry-mixing process, the appearance effect and the distinctness of a coating are remarkably improved while the dispersing effect of cellulose acetate butyrate and metal pigments is improved and the adhering effect and efficiency of the metal pigments are enhanced, the glossiness of the coating reaches over 50% (60 DEG C), and particularly, the touch pollution resisting capability of the surface of the metal coating is remarkably enhanced. The whole quality of the product is comprehensively enhanced.

Description

technical field [0001] The invention relates to a thermosetting metal powder coating with a smooth coating appearance and high gloss, in particular to a high-gloss metal powder coating and a preparation method thereof, belonging to the technical field of powder coatings. Background technique [0002] The metal powder coating film has a metallic luster, a gorgeous multi-color effect and outstanding protection functions, providing a colorful appearance decoration for high-end industrial products such as automobiles, home appliances, and instruments. Existing high-gloss metallic powder coatings generally refer to dry-mixed powder coatings mixed with metallic pigments that have a coating appearance similar to chrome plating, stainless steel, and silver plating. They have gorgeous multi-color effects and outstanding protective functions. , instrumentation and other high-end industrial products provide a colorful appearance decoration. [0003] The glossiness of high-gloss coatin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D167/00C09D175/04C09D7/12C09D5/03
CPCC09D163/00C08L2205/03C08L2205/035C08L2205/18C09D5/032C09D5/033C09D167/00C08L67/00C08L1/14C08L23/06C08K3/00C08K2003/2241C08K2003/3045C08K3/36C08L63/00
Inventor 晁兵
Owner 晁兵
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka