Degradable foam packaging material and preparation method thereof

A technology of packaging materials and foaming agents, applied in the field of degradable foaming packaging materials and its preparation, can solve the problems of no substitutes and achieve the effects of reducing production costs and prices, not polluting the environment, and simplifying processing procedures

Active Publication Date: 2017-11-10
江西禾尔斯环保科技有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no ideal substitute

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Degradable foam packaging material and preparation method thereof
  • Degradable foam packaging material and preparation method thereof
  • Degradable foam packaging material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The degradable foam packaging material is composed of the following raw materials in parts by weight: 8 parts of degradable resin, 1.5 parts of modifier, 2.5 parts of foaming agent, 70 parts of plant fiber, and 5 parts of inorganic powder.

[0034] Table 1

[0035] name

material

parts by weight

Degradable resin

PLA

8 servings

modifier

terminal amino group

1.5 servings

Foaming agent

sodium bicarbonate

2.5 servings

plant fibres

rice husk powder

70 copies

Inorganic powder

Talc powder

5 copies

[0036] The preparation method of degradable foam packaging material comprises the following steps:

[0037] Step 1: Prepare raw materials according to the formula: degradable resin, modifier, foaming agent, plant fiber and inorganic powder;

[0038] Step 2: Put the plant fibers in an oven and dry them at a temperature of 50°C for 15 minutes;

[0039] Step 3: Perform ultrafine treatment...

Embodiment 2

[0045] The degradable foam packaging material is composed of the following raw materials in parts by weight: 9 parts of degradable resin, 2 parts of modifier, 3 parts of foaming agent, 75 parts of plant fiber, and 4.5 parts of inorganic powder.

[0046] Table 2

[0047] name

material

parts by weight

Degradable resin

PBAT, PBSA

9 servings

modifier

terminal amino group

2 copies

Foaming agent

Azodicarbonamide

3 copies

plant fibres

Corn stalks

75 copies

Inorganic powder

Talc powder

4.5 servings

[0048] The preparation method of degradable foam packaging material comprises the following steps:

[0049] Step 1: Prepare raw materials according to the formula: degradable resin, modifier, foaming agent, plant fiber and inorganic powder;

[0050] Step 2: Put the plant fibers in an oven and dry them at a temperature of 80°C for 10 minutes;

[0051] Step 3: Perform ultrafine treatment on...

Embodiment 3

[0057] The degradable foam packaging material is composed of the following raw materials in parts by weight: 8 parts of degradable resin, 1 part of modifier, 2 parts of foaming agent, 70 parts of plant fiber, and 19 parts of inorganic powder.

[0058] table 3

[0059] name

material

parts by weight

Degradable resin

PLA, PBSA

10 copies

modifier

terminal amino group

1 copy

Foaming agent

sodium bicarbonate

2 copies

plant fibres

sawdust

80 copies

Inorganic powder

limestone

4 parts

[0060] The preparation method of degradable foam packaging material comprises the following steps:

[0061] Step 1: Prepare raw materials according to the formula: degradable resin, modifier, foaming agent, plant fiber and inorganic powder;

[0062] Step 2: Put the plant fibers in an oven and dry them at a temperature of 65°C for 12 minutes;

[0063] Step 3: Perform ultrafine treatment on the dried plant ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a degradable foam packaging material and its preparation method. The packaging material comprises, by weight, 8-10 parts of degradable resin, 1-2 parts of a modifier, 2-3 parts of a foaming agent, 70-80 parts of vegetable fiber and 4-5 parts of inorganic powder. The preparation method comprises the following steps: 1, preparing raw materials according to the above formula; 2, drying the vegetable fiber; 3, carrying out ultrafine treatment on the vegetable fiber, and preparing a modified vegetable fiber composite base material; 4, carrying out low temperature high shearing on the modified vegetable fiber composite base material; 5, pre-foaming the modified vegetable fiber composite base material; 6, carrying out foaming extrusion on the modified vegetable fiber composite base material; and 7, cooling and fixing to obtain the degradable foam packaging material. The degradable foam packaging material has the advantages of high strength, good toughness, low density, economy, environmental protection and the like.

Description

technical field [0001] The invention belongs to a packaging material, in particular to a degradable foam packaging material and a preparation method thereof. Background technique [0002] With the gradual deepening of human's understanding of their own living environment and its influencing factors, people's awareness of environmental protection has rapidly increased. strict restrictions. At present, the cushioning packages of various industrial products in the world are mostly made of polyolefin foam materials, such as expanded polystyrene EPS, polyvinyl chloride PVC, etc. Due to the non-degradability of these materials, their waste has caused quite serious pollution to the environment. Moreover, the chlorofluorocarbon gas released by these materials during the production process has caused serious damage to the atmospheric ozone layer that humans are resistant to care. For many years, people have been [0003] There is a tireless search for biodegradable, lightweight a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L97/02C08L67/04C08L67/02C08J9/10C08J9/08C08K3/34C08K3/26B65D65/46B29C44/00
CPCY02W90/10
Inventor 高婉琴翟国强邵羽静文杨洋
Owner 江西禾尔斯环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More