One-component self-drying water-based anti-rust primer for electrical equipment shell and preparation method thereof

Abstract

The invention discloses single component air-drying water-based rust inhibiting primer with curtaining capacity and used for an electrical equipment housing. The primer comprises components in percentage by weight as follows: 30%-50% of water-based resin, 1%-5% of a wetting dispersant, 0.1%-1% of a pH regulator, 5%-15% of rust inhibiting pigment, 15%-30% of pigment packing, 1%-8% of a coalescing agent, 0.5%-1.5 % of a wetting levelling agent, 0.5%-2% of a flash rust remover, 0.1%-1.5% of an antifoaming agent, 0.5%-2% of a thickener, 0.1%-1% of a mould-proof sterilizing agent and 5%-20% of deionized water. The invention further discloses a preparation method of the water-based rust inhibiting primer. The water-based rust inhibiting primer has lower film forming temperature, any cross-linking agent and curing agent is not required to be added, the primer can be rapidly dried and cured at normal temperature or a low-temperature baking environment ranging from 50 DEG C to 80 DEG C, construction is simple and convenient, and the product performance is comparable with that of solvent based paint.

Description

Technical field [0001] The invention relates to a water-based paint, in particular to a single-component self-drying water-based anti-corrosion primer for the shell of electrical equipment. The invention also relates to a preparation method of the water-based anti-rust primer. Background technique [0002] Electrical equipment, such as servo motors, CNC machine tools, industrial robots, terminal distribution boxes for substations and power distribution stations, distribution lines for urban communication systems, and box-type substations that have been popularized in recent years, mostly use metal Shell protection, but because of the high cost of aluminum alloy, its use is restricted, so in practical applications, the surface of steel plate is coated with paint for protection. [0003] Due to the complex structure of the electrical equipment shell, the multi-faceted and porous workpieces, the complicated parts and overall coating process, the many procedures, and the demanding per...

AI Technical Summary

Problems solved by technology

[0004] At present, most of the coating systems for the protection of electrical equipment shells are solvent-based paints, and water-based paints only account for less than 5-10% of the market share. Most of the water-based products come from foreign technologies, such as Akzo-Nobel, Nippon, and DuPont. , Kansai and other well-known international companies mainly focus on water-based two-component products. The price is 50%~200% more expensive than the same type of oil-based products, and the performance is also inferior to similar oil-based coating products. Moreover, water-based two-component products are due to There are restrictions on the effective period of construction, and the flow coating process cannot be used. These unfavorable factors hinder the promotion of water-based coating products in this industry

Images