Composite gold leaching agent and preparation method thereof

The technology of a gold leaching agent and a complex is applied in the field of the complex gold leaching agent and its preparation, which can solve the problems that the gold leaching agent cannot be applied to gold mines, the use of the gold leaching agent is restricted, and the sodium cyanide is highly toxic, and the product quality is stable, The effect of short gold immersion cycle and non-corrosive equipment

Inactive Publication Date: 2016-03-23
刘书志
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing gold leaching agent is sodium cyanide, which is highly toxic and cannot be applied to all gold mines, which limits the use of gold leaching agents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] The preparation method of composite gold leaching agent of the present invention comprises the steps:

[0023] (1) Use urea as the main raw material to add catalyst, flux, complexing agent, and stabilizer to heat in a high-temperature-resistant stainless steel industrial electric furnace for high-temperature pyrolysis and compounding reaction, and the reaction temperature is controlled at about 850 degrees Celsius;

[0024] (2) After the reaction of the reactants is completed, the molten body in the furnace is released, and the temperature is naturally lowered to obtain a composite gold leaching agent.

[0025] The complex formed by urea in the process of pyrolysis, condensation, and compound reaction includes: calcium cyanamide, calcium polysulfide, sodium cyanurate, sodium cyanurate, alkaline thiourea, etc. Among them, cyanurate is an inhibitor that can effectively control the passivation in the gold leaching process; calcium polysulfide has a strong anion in activity...

Embodiment 1

[0027] Selected raw materials: urea 600kg, calcium oxide 100Kg, calcium carbonate 50kg, sodium bicarbonate 50kg, sodium sulfide 50kg, zinc oxide 5kg, sodium pyrophosphate 5kg, sodium silicate 5kg, aluminum oxide 1kg, ammonium sulfate 5kg.

[0028] After the above raw materials are fully stirred and mixed, they are added to a stainless steel high-temperature furnace to heat up for pyrolysis and condensation reaction. When the temperature rises to about 850 degrees Celsius, observe that the raw materials in the furnace are completely melted, and the reaction is completed. Immediately discharge the materials and naturally cool down. After cooling, the composite gold leaching agent product is obtained.

Embodiment 2

[0030] Selected raw materials: urea 680kg, calcium oxide 150kg, sodium bicarbonate 190kg, sodium tripolyphosphate 10kg, alumina 2kg, ammonium chloride 10kg.

[0031] After the above raw materials are fully stirred and mixed, they are added to a stainless steel high-temperature furnace to heat up for pyrolysis and condensation reaction. When the temperature rises to about 850 degrees Celsius, observe that the raw materials in the furnace are completely melted, and the reaction is completed. Immediately discharge the materials and naturally cool down. After cooling, the composite gold leaching agent product is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a composite gold-leaching agent which possesses wide application scope and is safe and realible and a preparation method thereof. The composite gold-leaching agent is prepared by employing 65-70 wt% of urea, 0.5-2 wt% of a catalyst, 0.5-5 wt% of a complexing agent, 5-20 wt% of a stabilizer, and 10-20 wt% of a fluxing agent and performing high-temperature pyrolysis combination reaction. The composite gold-leaching agent is capable of forming complexes with multiple noble metal ions, is capable of rapidly forming ligands with noble metals such as gold, silver and the like for dissolving, is applicable to all gold-containing minerals such as oxidation ore, primary gold ore, gold-sivler ore, limonite, high-sulfur ore, high-arsenic high-iron oxidation ore, cyanidation tailings, gold concentrate and the like, and also is applicable to electronic waste gold-plated materials.

Description

technical field [0001] The invention relates to a gold leaching agent and a preparation method thereof, in particular to a composite gold leaching agent and a preparation method thereof. Background technique [0002] The existing gold leaching agent is sodium cyanide, which is highly toxic and cannot be applied to all gold mines, which limits the use of the gold leaching agent. Contents of the invention [0003] The invention provides a safe and reliable complex gold leaching agent with wide application range and a preparation method thereof. [0004] Realize one of the object of the present invention composite gold leaching agent, adopt urea 65~70wt%, catalyzer 0.5~2wt%, complexing agent 0.5~5wt%, stabilizing agent 5~20wt%, flux 10~20wt% after high-temperature heating Decomposition reaction; [0005] The catalyst is one or more of ammonium sulfate, ammonium chloride, zinc oxide; [0006] The complexing agent is sodium pyrophosphate and / or sodium tripolyphosphate; [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22B11/00C22B3/04
CPCY02P10/20
Inventor 刘书志
Owner 刘书志
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap