Rare earth recro 3 Magnetic wave absorbing material and preparation method thereof

A magnetic wave-absorbing and rare-earth technology, applied in chemical instruments and methods, and other chemical processes, can solve problems such as poor temperature stability, easy corrosion, and high density of magnetic wave-absorbing materials, and achieve good corrosion resistance and temperature stability , Anti-oxidation and corrosion resistance, the effect of wide absorption frequency band

Active Publication Date: 2016-08-17
GUILIN UNIV OF ELECTRONIC TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the rare earth intermetallic compound magnetic wave-absorbing material has a high density (about 7.3g / cm 2 ), easy to corrode, poor temperature stability and other shortcomings, so it will be limited in practical application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rare earth recro <sub>3</sub> Magnetic wave absorbing material and preparation method thereof
  • Rare earth recro <sub>3</sub> Magnetic wave absorbing material and preparation method thereof
  • Rare earth recro <sub>3</sub> Magnetic wave absorbing material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Preparation of SmCrO 3 The specific steps are:

[0034] 1) Sm with a purity ≥ 99.50% 2 o 3 、Cr 2 o 3 Powder as raw material, according to SmCrO 3 Stoichiometric ratio ingredients of molecular formula;

[0035] 2) Grind in an agate bowl mill for half an hour to mix well;

[0036] 3) Press the uniformly mixed powder into flakes with a diameter of 1.5cm and a thickness of 0.3~0.8cm, with a pressure of 20~30MPa;

[0037] 4) After the powder is mixed evenly, the pressed flakes are sintered in the atmosphere at a temperature of 1500 °C;

[0038] 5) Carry out 1500℃×24 sintering heat treatment on the thin slice in the atmosphere, that is, the sintering temperature is 1500℃ for 24h;

[0039] 6) Break the sintered flakes into fine powder with particle size less than 0.3mm.

[0040] Product testing by SmCrO 3 Powder: paraffin wax = 4:1 (mass ratio) mixed to make coaxial samples with outer and inner diameters of 7mm and 3mm respectively, and thicknesses of 1.3mm, 1.5mm an...

Embodiment 2

[0046] Preparation of EuCrO 3 The specific implementation steps are:

[0047] 1) Eu with purity ≥ 99.50% 2 o 3 、Cr 2 o 3 Powder as raw material, according to EuCrO 3 Stoichiometric ratio ingredients of molecular formula;

[0048] 2) Grind in an agate bowl mill for half an hour to mix well;

[0049] 3) Press the uniformly mixed powder into flakes with a diameter of 1.5cm and a thickness of 0.3~0.8cm, with a pressure of 20~30MPa;

[0050] 4) After the powder is mixed evenly, the pressed flakes are sintered in the atmosphere at a temperature of 1500 °C;

[0051] 5) Carry out 1500℃×24 sintering heat treatment on the thin slice in the atmosphere, that is, the sintering temperature is 1500℃ for 24h;

[0052] 6) Break the sintered flakes into fine powder with particle size less than 0.3mm.

[0053] Product testing: by EuCrO 3 Powder: paraffin wax = 4:1 (mass ratio) mixed to make coaxial samples with outer and inner diameters of 7mm and 3mm respectively, and thicknesses of 1...

Embodiment 3

[0057] Preparation of DyCrO 3 The specific implementation steps are:

[0058] 1) Dy with a purity ≥ 99.50% 2 o 3 、Cr 2 o 3 Powder as raw material, according to DyCrO 3 Stoichiometric ratio ingredients of molecular formula;

[0059] 2) Grind in an agate bowl mill for half an hour to mix well;

[0060] 3) Press the uniformly mixed powder into flakes with a diameter of 1.5cm and a thickness of 0.3~0.8cm, with a pressure of 20~30MPa;

[0061] 4) After the powder is mixed evenly, the pressed flakes are sintered in the atmosphere at a temperature of 1500 °C;

[0062] 5) Carry out 1500℃×24 sintering heat treatment on the thin slice in the atmosphere, that is, the sintering temperature is 1500℃ for 24h;

[0063] 6) Break the sintered flakes into fine powder with particle size less than 0.3mm.

[0064] Product Test: By DyCrO 3 Powder: paraffin wax = 4:1 (mass ratio) mixed to make coaxial samples with outer and inner diameters of 7mm and 3mm respectively, and thicknesses of 1....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The rare earth ReCrO3 magnetic wave-absorbing material and its preparation method of the present invention are prepared by mixing Re2O3 and Cr2O3 powders with a molecular ratio of 1:1 with a purity of ≥99.50%, and grinding them in an agate bowl mill for half an hour to mix Evenly, after mixing evenly, the powder is pressed into flakes, and the flakes are sintered at 1500°C for 24 hours under the protection of vacuum or argon, and then cooled with the furnace. The invention has the advantages of simple preparation process, good microwave absorption characteristics in the 2-18 GHz microwave band, wide absorption frequency band, good oxidation resistance and good temperature stability, and does not contain strategic metal elements such as Co and Ni, and has the characteristics of low price and the like. . It is more suitable for preparing microwave absorbing products with high microwave absorption efficiency, low material density, good non-oxidation and corrosion resistance, and good thermal stability.

Description

technical field [0001] The invention relates to magnetic wave-absorbing materials, specifically rare earth ReCrO 3 Magnetic wave-absorbing material and its preparation method. Background technique [0002] In recent years, with the rapid development of radar technology, the requirements for stealth technology will become higher and higher, and microwave absorbing materials are one of the frontier topics in stealth technology. In addition, a large number of electronic devices have entered daily life, and the deteriorating electromagnetic environment will interfere with the normal operation of electronic instruments and equipment and affect human health. Absorbing electromagnetic waves with microwave absorbing materials is an effective protective measure. It can be seen that the research on microwave absorbing materials has far-reaching significance in both military and civilian applications. In addition, in modern warfare, information acquisition and anti-acquisition have ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/12C04B35/622C09K3/00
Inventor 潘顺康刘烨成丽春饶光辉林培豪
Owner GUILIN UNIV OF ELECTRONIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More