A method for preparing ceramic sealing rings from waste materials

A technology of ceramic sealing and waste ceramics, which is applied in the sealing of engines, the removal of solid waste, mechanical equipment, etc., can solve the problems of poor sealing performance and limited use, and achieve the highest temperature resistance and thermal conductivity. Good performance and easy industrial production

Active Publication Date: 2017-11-07
黎清弟
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Ceramic sealing ring is the focus of current research. Some people put alumina 50-70wt%; zirconia 10-20wt%; ethylene glycol 3-7wt%; polyethylene 5-9wt%; silica sol, aluminum sol or soft clay One or more kinds of 2-5wt% made of refractory cement sealing ring, but its use is limited, and the sealing performance needs to be improved; and the introduction of nano-ceramics into the field of ceramics is a research hotspot now, due to the excellent physical and chemical properties of nano-materials Performance, will greatly improve the mechanical, electrical and mechanical properties of nano-ceramics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A method for preparing a ceramic sealing ring using waste raw materials, the sealing ring is divided into two parts, the inner part is a ceramic part, and the outer part is a rubber part, and the ceramic part is arranged in the rubber through a heat vulcanization process.

[0045] The parts by weight of the nano ceramic part consist of:

[0046] 50 parts of industrial waste ceramic raw materials

[0047] Nano silicon dioxide 30 parts

[0048] Nano silicon carbide 20 parts

[0049] Fused magnesia 15 parts

[0050] Nano boron carbide 10 parts

[0051] Nano zinc oxide 10 parts

[0052] Nano titanium oxide 10 parts

[0053] Carbon black 10 parts

[0054] Yttrium stabilized zirconia 20 parts

[0055] Andalusite 10 parts

[0056] Tempered fiber 5 parts

[0057] 3 parts of PVA

[0058] 3 parts of aluminate cement;

[0059] The parts by weight of the rubber part consist of:

[0060] 40 parts of waste silicone rubber

[0061] Bromobutyl rubber 50 parts

[0062] N66...

Embodiment 2

[0075] A method for preparing a ceramic sealing ring using waste raw materials, the sealing ring is divided into two parts, the inner part is a ceramic part, and the outer part is a rubber part, and the ceramic part is arranged in the rubber through a heat vulcanization process.

[0076] The parts by weight of the nano ceramic part consist of:

[0077] 70 parts of industrial waste ceramic raw materials

[0078] Nano silicon dioxide 10 parts

[0079] Nano silicon carbide 10 parts

[0080] Fused magnesia 10 parts

[0081] Nano boron carbide 5 parts

[0082] Nano Zinc Oxide 5 parts

[0083] Nano titanium oxide 5 parts

[0084] Carbon black 5 parts

[0085] Yttrium stabilized zirconia 10 parts

[0086] Andalusite 6 parts

[0087] Tempered fiber 1 part

[0088] 1 piece of PVA

[0089] 1 part of aluminate cement;

[0090] The parts by weight of the rubber part consist of:

[0091] 60 parts of waste silicone rubber

[0092] Bromobutyl rubber 30 parts

[0093] N660 carbo...

Embodiment 3

[0106] A method for preparing a ceramic sealing ring using waste raw materials, the sealing ring is divided into two parts, the inner part is a ceramic part, and the outer part is a rubber part, and the ceramic part is arranged in the rubber through a heat vulcanization process.

[0107] The parts by weight of the nano ceramic part consist of:

[0108] 60 parts of industrial waste ceramic raw materials

[0109] Nano silicon dioxide 10 parts

[0110] Nano silicon carbide 10 parts

[0111] Fused magnesia 10 parts

[0112] Nano boron carbide 5 parts

[0113] Nano Zinc Oxide 5 parts

[0114] Nano titanium oxide 5 parts

[0115] Carbon black 5 parts

[0116] Yttrium stabilized zirconia 10 parts

[0117] Andalusite 6 parts

[0118] Tempered fiber 1 part

[0119] 1 piece of PVA

[0120] 1 part of aluminate cement;

[0121] The parts by weight of the rubber part consist of:

[0122] 50 parts of waste silicone rubber

[0123] Bromobutyl rubber 30 parts

[0124] N660 carbo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
wear coefficientaaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing a ceramic sealing ring by using waste materials, by means of taking industrial waste ceramic materials, silicon dioxide, silicon carbide, boron carbide, zinc oxide, titanium oxide and the like as green body materials, and taking waste silicone rubber, brominated butyl rubber, N660 carbon black, glass fiber, activating agent and PEG20000 as rubber components, the sealing ring is obtained through heat vulcanization process, the preparation process is simple and easy to industrialize, and the sealing ring prepared has excellent physical and chemical properties.

Description

technical field [0001] The invention belongs to the field of sealing rings, and in particular relates to a method for preparing ceramic sealing rings from waste materials. Background technique [0002] With the development of science and technology in our country, various processes have higher and higher demands for mechanical seals and motion seals. In metallurgy, machinery, chemical industry, medicine, food, corrosion-resistant pumps, automobiles and pneumatic components, etc. High precision, good mechanical strength, good high temperature wear resistance, good chemical corrosion resistance, and high performance sealing rings such as impervious to water when the temperature changes suddenly. [0003] Ceramic sealing ring is the focus of current research. Some people put alumina 50-70wt%; zirconia 10-20wt%; ethylene glycol 3-7wt%; polyethylene 5-9wt%; silica sol, aluminum sol or soft clay One or more kinds of 2-5wt% made of refractory cement sealing ring, but its use is li...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): F16J15/00F16J15/16C04B35/00B09B3/00
CPCC08L23/283C08L83/04C08L2205/03F16J15/00C08L71/00C08K7/14C08K3/04
Inventor 梁尤平
Owner 黎清弟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap