Dithienylbenzotriazole side chain-containing polymer, preparation method thereof, and organic solar cell device

A technology of benzotriazole and dithiophene, applied in the field of organic semiconductor materials, can solve problems such as low conversion efficiency, and achieve the effects of improved energy conversion efficiency, high electron mobility and novel structure

Inactive Publication Date: 2015-05-06
OCEANS KING LIGHTING SCI&TECH CO LTD +2
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Research in this area has made rapid progress in recent years, but the conversion efficie

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dithienylbenzotriazole side chain-containing polymer, preparation method thereof, and organic solar cell device
  • Dithienylbenzotriazole side chain-containing polymer, preparation method thereof, and organic solar cell device
  • Dithienylbenzotriazole side chain-containing polymer, preparation method thereof, and organic solar cell device

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0031] Example 1:

[0032] The polymer containing dithiophene benzotriazole side chains of this embodiment, namely poly{6,6,12,12-tetra-n-octyl-2,8-diyl-6,12-dihydroindeno[ 1,2-b:1',2'-e)pyrazine-co-4-(2-(2,5-diylthiophen-3-yl)vinyl)-N-(4-(n-octyloxy (Phenyl)-N-phenylaniline}(P1), (wherein, R1 is n-octyl group, R2 is n-octyl group, n=58), its structural formula is as follows:

[0033]

[0034] The preparation steps of the above polymer are as follows:

[0035] The reaction formula is as follows:

[0036]

[0037] Under the protection of argon, 6,6,12,12-tetran-octyl-2,8-dipinacol borate-6,12-dihydroindeno[1,2-b:1' ,2'-e)pyrazine (191mg, 0.2mmol), 4-(2-(2,5-dibromothiophen-3-yl)vinyl)-N-(4-(n-octyloxy)benzene) -N-Phenylaniline (128mg, 0.2mmol) was added to the flask containing 10ml of toluene solvent, after fully dissolved, potassium carbonate (2mL, 2mol / L) solution was added to the flask, vacuumed to remove oxygen and filled with argon , Then add bistriphenylphosphine palladium di...

Example Embodiment

[0040] Example 2:

[0041] The polymer containing dithiophene benzotriazole side chains of this embodiment is poly{6,6,12,12-tetramethyl-2,8-diyl-6,12-dihydroindeno[1, 2-b: 1',2'-e)pyrazine-co-4-(2-(2,5-diylthiophen-3-yl)vinyl)-N-(4-(n-eicosanoxy (Phenyl)-N-phenylaniline}(P2), (wherein, R1 is methyl, R2 is n-eicosyl, n=12), its structure is as follows:

[0042]

[0043] The preparation steps of the above polymer are as follows:

[0044] The reaction formula is as follows:

[0045]

[0046] Under the protection of a mixture of nitrogen and argon, 6,6,12,12-tetramethyl-2,8-dipinacol borate-6,12-dihydroindeno[1,2-b:1 ',2'-e)pyrazine (169mg, 0.3mmol), 4-(2-(2,5-dibromothiophen-3-yl)vinyl)-N-(4-(n-eicosyloxy ) Benzene)-N-phenylaniline (242mg, 0.3mmol) and 15mL of tetrahydrofuran were added to a 50mL two-necked flask. After being fully dissolved, a mixture of nitrogen and argon was introduced to exhaust the air for about 20 minutes, and then tetratriphenylene Phosphine palladium (4mg, 0...

Example Embodiment

[0048] Example 3:

[0049] The polymer containing dithiophene benzotriazole side chains of this embodiment is poly{6,6,12,12-tetran-eicosyl-2,8-diyl-6,12-dihydroindeno [1,2-b:1',2'-e]pyrazine-co-4-(2-(2,5-diylthiophen-3-yl)vinyl)-N-(4-(methoxy (Phenyl)-N-phenylaniline}(P3), (wherein, R1 is n-eicosyl, R2 is methyl, n=84), its structure is as follows:

[0050]

[0051] The preparation steps of the above polymer are as follows:

[0052] The reaction formula is as follows:

[0053]

[0054] Under the protection of nitrogen, the 6,6,12,12-tetran-eicosyl-2,8-dipinacol borate-6,12-dihydroindeno[1,2-b:1', 2'-e) pyrazine (488mg, 0.3mmol), 4-(2-(2,5-dibromothiophen-3-yl)vinyl)-N-(4-(methoxy)benzene)-N -Phenylaniline (179mg, 0.33mmol), palladium acetate (3.5mg, 0.015mmol) and tris (o-methylphenyl) phosphine (21mg, 0.06mmol) were added to 12mL of N,N-dimethylformaldehyde Add potassium carbonate (3mL, 2mol / L) solution to the amide flask after fully dissolving, and then purge the flask with nit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of organic semiconductors, and discloses a dithienylbenzotriazole side chain-containing polymer, a preparation method thereof, and an organic solar cell device. The structural general formula of the above host material is shown in the specification. In the formula, R1 and R2 respectively represent C1-C20 alkyl groups, and n is an integer in a range of 12-97. In the dithienylbenzotriazole side chain-containing polymer, triphenylamine is an excellent hole transport unit; and diindenopyrazine is a heterocyclic compound with a rigid planar structure, and has high heat stability and electron mobility. The above triphenylamine side chain-containing copolymer can be applied in solar cells in order to improve the phototransformation efficiency.

Description

technical field [0001] The invention relates to the field of organic semiconductor materials, in particular to a polymer containing dithiophene benzotriazole side chains and a preparation method thereof. The invention also relates to an organic solar cell device using the polymer containing dithiophene benzotriazole side chains as an electron donor material for an active layer. Background technique [0002] The preparation of low-cost and high-efficiency solar cells using cheap materials has always been a research hotspot and difficulty in the field of photovoltaics. Organic semiconductor materials have attracted much attention for their advantages such as easy availability of raw materials, low price, simple process, strong stability, and good photovoltaic effect. Since 1992, N.S. Sariciftci et al. reported on SCIENCE (N. S Sariciftci, L. Smilowitz, A.J. Heeger, et al. Science, 1992, 258, 1474) that conjugated polymers and C 60 After the light-induced electron transfer ph...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G61/12H01L51/46
CPCY02E10/549
Inventor 周明杰张振华王平钟铁涛
Owner OCEANS KING LIGHTING SCI&TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap