Rubber material for sealing automobile door and preparation method of rubber material

A technology for sealing rubber and automobile doors, applied in the field of automobile door sealing rubber materials, which can solve the problems of poor aging resistance and achieve good aging resistance and sealing performance

Inactive Publication Date: 2015-05-06
LIUZHOU YINGHANG AUTO PARTS
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing automobile door sealing rubber materials have poor aging resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] The formula of the automobile door sealing rubber material of the present invention is as follows:

[0011] Natural rubber 75kg, hydrogenated nitrile rubber 25kg, stearic acid 4kg, methyl hydrogen silicone oil 2.5kg, light calcium carbonate 1.6kg, oleic acid diethanolamine borate 0.5kg, drying oil alkyd resin 4kg, paraffin 1.5kg kg, glass fiber 0.6kg, zinc diethyldithiocarbamate 1kg, diacetyl peroxide 3kg, alumina 9kg, silica 12kg, antioxidant 1.2kg, sulfur 2kg.

[0012] The preparation method of the automobile door sealing rubber material of the present invention is as follows:

[0013] The natural rubber and hydrogenated nitrile rubber of the formula amount are respectively thinned, mixed and added to the open mill, and then the remaining components are added to the open mill for mixing until uniform, and then the sheet is produced to obtain a mixed rubber. Carry out one-stage vulcanization, control the vulcanization temperature to be 160°C, the vulcanization time to...

Embodiment 2

[0015] The formula of the automobile door sealing rubber material of the present invention is as follows:

[0016] Natural rubber 70kg, hydrogenated nitrile rubber 20kg, stearic acid 3kg, methyl hydrogen silicone oil 2kg, light calcium carbonate 1.5kg, oleic acid diethanolamine borate 0.4kg, dry oil alkyd resin 5kg, paraffin 1kg, Glass fiber 0.5kg, zinc diethyldithiocarbamate 0.8kg, diacetyl peroxide 2kg, alumina 8kg, silica 10kg, antioxidant 1.5kg, sulfur 1kg.

[0017] The preparation method of the automobile door sealing rubber material of the present invention is as follows:

[0018] The natural rubber and hydrogenated nitrile rubber of the formula amount are respectively thinned, mixed and added to the open mill, and then the remaining components are added to the open mill for mixing until uniform, and then the sheet is produced to obtain a mixed rubber. Carry out one-stage vulcanization, control the vulcanization temperature to be 150°C, the vulcanization time to be 40 m...

Embodiment 3

[0020] The formula of the automobile door sealing rubber material of the present invention is as follows:

[0021] Natural rubber 80kg, hydrogenated nitrile rubber 30kg, stearic acid 5kg, methyl hydrogen silicone oil 3kg, light calcium carbonate 1.8kg, oleic acid diethanolamine borate 0.6kg, dry oil alkyd resin 3kg, paraffin 2kg, Glass fiber 0.8kg, zinc diethyldithiocarbamate 1.2kg, diacetyl peroxide 4kg, alumina 10kg, silica 15kg, antioxidant 0.8kg, sulfur 3kg.

[0022] The preparation method of the automobile door sealing rubber material of the present invention is as follows:

[0023] The natural rubber and hydrogenated nitrile rubber of the formula amount are respectively thinned, mixed and added to the open mill, and then the remaining components are added to the open mill for mixing until uniform, and then the sheet is produced to obtain a mixed rubber. Carry out one-stage vulcanization, control the vulcanization temperature to be 170°C, the vulcanization time to be 30 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a rubber material for sealing an automobile door. The rubber material is composed of the following components in parts by mass: 70-80 parts of natural rubber, 20-30 parts of hydrogenated butadiene-acrylonitrile rubber, 3-5 parts of stearic acid, 2-3 parts of methyl hydrogen silicon oil, 1.5-1.8 parts of light calcium carbonate, 0.4-0.6 part of oleic diethanolamide borate, 3-5 parts of drying alkyd resin, 1-2 parts of paraffin, 0.5-0.8 part of glass fiber, 0.8-1.2 parts of zinc diethyldithiocarbamate, 2-4 parts of acetyl peroxide, 8-10 parts of aluminum oxide, 10-15 parts of white carbon black, 0.8-1.5 parts of an anti-ageing agent and 1-3 parts of sulfur. The invention also provides a preparation method of the rubber material. The rubber material provided by the invention has favorable ageing resistance and sealing performance and can be favorably applied to sealing of the automobile door.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to an automobile door sealing rubber material. Background technique [0002] Automobile rubber seal strip is one of the important parts of the car, widely used in the door, window, body, seat, sunroof, engine box and trunk, etc., with waterproof, sealing, sound insulation, dustproof , antifreeze, shock absorption, warmth and energy saving. It must have strong tensile strength, good elasticity, and relatively good high temperature resistance and aging resistance. The existing automobile door sealing rubber material has poor aging resistance. Contents of the invention [0003] The invention provides an automobile door sealing rubber material; therefore, the invention also provides a preparation method thereof. [0004] The invention provides an automobile door sealing rubber material. The rubber material is composed of the following components in parts by ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L15/00C08L83/05C08L67/08C08L91/06C08K13/04C08K7/14C08K5/09C08K3/26C08K5/55C08K5/39C08K5/14C08K3/22C08K3/36C08K3/06B29C35/02
CPCC08L7/00C08L2205/035C08L15/005C08L83/04C08L67/08C08L91/06C08K13/04C08K5/09C08K5/55C08K2003/265C08K7/14C08K5/39C08K5/14C08K2003/2227C08K3/36C08K3/06
Inventor 莫海燕
Owner LIUZHOU YINGHANG AUTO PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap