Method for preparing metavanadate
A technology of metavanadate and calcium vanadate, applied in chemical instruments and methods, vanadium compounds, calcium carbonate/strontium/barium, etc., can solve the problem of low vanadium yield, difficult control of vanadium precipitation process, and large acid consumption and other problems, to achieve the effect of reducing the preparation process and achieving significant economic and environmental benefits
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0030] A method for preparing metavanadate: 1) Take the sodiumized vanadium-extracting leachate after impurity removal, put it in a reactor, heat it to 80°C, and add it to the sodiumized vanadium-extracting leachate according to the molar ratio of Ca:V=1.5:1 Calcium oxide was added to the mixture, and after reacting for 30 minutes, after liquid-solid separation, washing, filtration, and drying, a calcium vanadate solid containing V=20%, Ca=40% was obtained; 2) Take the calcium vanadate solid obtained in step 1). Add 300g and 500mL of water into the beaker together, and start stirring and heating, add 92g of sodium bicarbonate according to the molar ratio of Na:V=1:1, and pass in carbon dioxide gas, the ventilation rate is 0.8L / (minKg), Heating to 80°C and reacting for 6 hours, the pH is 8.3; 3) Liquid-solid separation to obtain calcium carbonate solid and sodium metavanadate solution, the solution concentration is 200g / L; place it in a container, turn on and stir for natural cr...
Embodiment 2
[0032] A method for preparing metavanadate: 1) Take the impurity-removed sodium vanadium extraction leaching solution and the reactor, heat it to 100°C, and pour it into the sodium vanadium extraction leaching solution according to the molar ratio of Ca:V=2:1 Add calcium hydroxide slurry, react for 40 minutes, and obtain solid calcium vanadate containing V=19%, Ca=43% after liquid-solid separation, washing, filtration and drying; 2) Take the vanadic acid obtained in step 1) Add 300g of calcium solids and 500mL of water into the beaker together, and turn on stirring and heating, add 88g of sodium bicarbonate according to the molar ratio of Na:V=0.8:1, and pass in carbon dioxide gas, the ventilation rate is 0.1L / (minKg ), heated to 100°C, and measured after 2 hours of reaction, the pH is 8.2; 3) Liquid-solid separation to obtain calcium carbonate solid and sodium metavanadate solution, the solution concentration is 80g / L; put it in the container, turn on and stir Natural crystal...
Embodiment 3
[0034] A method for preparing metavanadate: 1) Take the impurity-removed sodium vanadium extraction leaching solution and the reactor, heat it to 93°C, and pour it into the sodium vanadium extraction leaching solution according to the molar ratio of Ca:V=1.8:1 Add calcium hydroxide slurry, react for 35 minutes, and obtain solid calcium vanadate containing V=19%, Ca=43% after liquid-solid separation, washing, filtration and drying; 2) Take the vanadic acid obtained in step 1) Add 300g of calcium solid and 500mL of water into the beaker together, and turn on stirring and heating, and add sodium bicarbonate according to the molar ratio of Na:V=0.9:1 99 g, and pass in carbon dioxide gas, the ventilation rate is 0.5L / (minKg), heated to 88 ° C, and measured after 1 hour of reaction, the pH is 8.5; 3) liquid-solid separation to obtain calcium carbonate solid and sodium metavanadate solution, the solution The concentration is 120g / L; put it in a container, turn on and stir for natural...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap