FAM-B-methanol-gasoline-resistant low-temperature-resistant low-compressive-deformation ethylene-acrylate rubber material and preparation method thereof

A technology for changing ethylene acrylate and methanol gasoline is used in the field of environmentally friendly ethylene acrylate rubber materials for automotive engine thermostats, which can solve problems such as poor performance and achieve low compression set, small swelling, and excellent resistance to FAMB methanol gasoline. performance effect

Inactive Publication Date: 2015-08-12
南京金三力高分子科技有限公司
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the fuel oil resistance performance of existing rubber sealing materials for automobile engines, especially the poor performance of resistance to FAM B methanol gasoline, and to provide a low-pressure variable ethylene acrylic acid resistant to FAM B methanol gasoline and low temperature resistance Ester rubber material and preparation method thereof; the technical scheme provided by the invention can meet the requirements of FAM B methanol gasoline resistance without being used in combination with other rubbers, improves the safety of use of automobile engines, and has the characteristics of low temperature resistance and low compression set advantage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • FAM-B-methanol-gasoline-resistant low-temperature-resistant low-compressive-deformation ethylene-acrylate rubber material and preparation method thereof
  • FAM-B-methanol-gasoline-resistant low-temperature-resistant low-compressive-deformation ethylene-acrylate rubber material and preparation method thereof
  • FAM-B-methanol-gasoline-resistant low-temperature-resistant low-compressive-deformation ethylene-acrylate rubber material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of resistance to FAM B methanol gasoline of the present embodiment, the low-pressure variable ethylene acrylate rubber material of low temperature resistance, comprises following component:

[0029]

[0030] Acrylate raw rubber in this embodiment is ethylene acrylate rubber produced by DuPont, the U.S., and the quick-extrusion carbon black is N550 quick-extrusion carbon black produced by Cabot Company; the thermal cracking carbon black is Maple Leaf brand N990 produced in Canada Carbon black; stearic acid was produced by Malaysia Southern Oil Company; 4,4'bis(phenylisopropyl)diphenylamine was anti-aging agent 445 (CAS No.: 10081-67-1) produced by Jiangsu Huada Chemical Group Co., Ltd. ); processing aid VAM (CAS No.: 63231-60-7), processing aid 18D (CAS No.: 124-30-1), softening plasticizer TP-795 (CAS No.: 141-17-3), Cross-linking aid HMDC-1 (CAS No.: 143-06-6) and vulcanizing agent 1,8-diazabicyclo[5.4.0]undec-7-ene (CAS No.: 6674-22-2) The suppliers are Sha...

Embodiment 2

[0043] A kind of resistance to FAM B methanol gasoline of the present embodiment, the low-pressure variable ethylene acrylate rubber material of low temperature resistance, comprises following component:

[0044]

[0045] The source of each component raw material of this embodiment is the same as that of Example 1.

[0046] The process of preparing the low-pressure variable ethylene acrylate rubber material resistant to FAM B methanol gasoline and low temperature resistance in this embodiment is as follows:

[0047] Step 1. Masterbatch mixing: send the raw materials except crosslinking aid HMDC-1 and vulcanizing agent 1,8-diazabicyclo[5.4.0]undec-7-ene to Put it into the internal mixer for internal mixing to obtain the masterbatch;

[0048] Step 2. Put the masterbatch that has been parked for 8 hours, the crosslinking aid HMDC-1, and the vulcanizing agent 1,8-diazabicyclo[5.4.0]undec-7-ene into the internal mixer together Carry out two-stage mixing, and discharge the glue...

Embodiment 3

[0057] A kind of resistance to FAM B methanol gasoline of the present embodiment, the low-pressure variable ethylene acrylate rubber material of low temperature resistance, comprises following component:

[0058]

[0059]

[0060] The source of each component raw material of this embodiment is identical with embodiment 1.

[0061] The process of preparing the low-pressure variable ethylene acrylate rubber material resistant to FAM B methanol gasoline and low temperature resistance in this embodiment is as follows:

[0062] Step 1. Masterbatch mixing: send the raw materials except crosslinking aid HMDC-1 and vulcanizing agent 1,8-diazabicyclo[5.4.0]undec-7-ene to Put it into an internal mixer for internal mixing to obtain a masterbatch.

[0063] Step 2. Put the masterbatch that has been parked for 8 hours, the crosslinking aid HMDC-1, and the vulcanizing agent 1,8-diazabicyclo[5.4.0]undec-7-ene into the internal mixer together Carry out two-stage mixing, and discharge t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
hardnessaaaaaaaaaa
tensile strength at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses an FAM-B-methanol-gasoline-resistant low-temperature-resistant low-compressive-deformation ethylene-acrylate rubber material and a preparation method thereof, belonging to the technical field of rubber preparation. The preparation method comprises the following steps: sending 90-110 parts of ethylene-acrylate rubber, 1-4 parts of 4,4'-di(phenylisopropyl)diphenylamine, 0.2-1.4 parts of processing assistant 18D, 0.5-1.8 parts of stearic acid, 0.5-1.3 parts of processing assistant VAM, 0-130 parts of thermo-cracking carbon black N990, 0-70 parts of quick-extrusion carbon black N550 and 2-17 parts of softening and plasticizing agent TP-759 into a Banbury mixer, and banburying to obtain a master batch; and sending the master batch, 1.2-1.9 parts of crosslinking assistant HMDC-1 and 1-3 parts of vulcanizing agent into the Banbury mixer, carrying out secondary compounding, discharging the rubber when the temperature reaches 100 DEG C, and finally, carrying out molding, primary vulcanization and secondary vulcanization. The rubber material has the advantages of excellent FAM B methanol gasoline resistance, low temperature resistance and low compressive permanent deformation.

Description

technical field [0001] The invention relates to the technical field of rubber preparation, and more specifically relates to an environmentally friendly ethylene acrylate rubber material for automobile engine thermostats that is resistant to methanol gasoline and low temperature, and has low compression set performance. Background technique [0002] With the continuous improvement of automobile emission standards and the shortage of petroleum resources, fuel substitution and low emission are the development trends of the automobile industry. At present, some countries such as Europe and the United States have begun to replace or mix the use of a new generation of methanol gasoline (FAM experimental liquid, in line with DIN51 604-B). This fuel can not only alleviate the oil resource crisis, but also has low price, low energy consumption, and low emissions. The advantages. [0003] However, the use of the above-mentioned fuels also puts forward higher requirements on chemical ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08K13/02C08K5/18C08K3/04C08K5/09C08K5/17C08K5/3462B29B7/00B29C35/02
CPCC08K13/02B29B7/002B29C35/02C08K3/04C08K5/09C08K5/17C08K5/18C08K5/3462C08K2201/003C08K2201/006C08L23/0869
Inventor 徐海潮吴会会
Owner 南京金三力高分子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap