PTT polyester flame retardation composition with excellent mechanical properties

A technology of flame retardant composition and mechanical properties, applied in the field of PTT polyester flame retardant composition, can solve the problems of low notched impact strength, low tensile strength, high notch sensitivity, etc., and achieve good shape and good processability , the effect of excellent flame retardant properties

Inactive Publication Date: 2015-08-26
QINGDAO XINZHAN PLASTIC
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polytrimethylene terephthalate (PTT), as a new type of polyester polymer material with excellent comprehensive properties, has been widely used in the fields of fibers, films, engineering plastics, etc., but unmodified PTT has low notched impact strength, The defects of high notch sensitivity, low tensile strength and poor flame retardancy greatly limit the wider application of PTT in various fields

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A PTT polyester flame retardant composition with excellent mechanical properties, its components are proportioned by mass percentage: PTT 62%, glass fiber 12%, calcium carbonate composite particles 10%, MBS 6%, polyphenylphosphonic acid di 8% of phenylsulfone ester, 1.5% of 2-hydroxy-4-methoxybenzophenone, 0.2% of antioxidant 1010, 0.3% of modified ethylene bis fatty acid amide, and the PTT is an intrinsic viscosity of 0.7-1.2dL / g of polytrimethylene terephthalate, the glass fibers are alkali-free chopped glass fibers whose surface has been treated with a silane coupling agent, and the nano-calcium carbonate composite particles are surface-grafted styrene and methyl acrylate double-single Calcium carbonate nanoparticles, the MBS is a methacrylic acid-butadiene-styrene copolymer with a core-shell structure, and its relative density is 1.09-1.11g / cm3.

[0022] Preparation method: (1), place PTT in a forced air circulation oven, dry at 110°C-120°C for 6-8 hours, and set a...

Embodiment 2

[0024] A PTT polyester flame retardant composition with excellent mechanical properties. 6% of phenylsulfone ester, 0.8% of 2-hydroxy-4-n-octyloxybenzophenone, 0.1% of the compound of antioxidant 1076 and antioxidant 168, and 0.1% of modified ethylene bis fatty acid amide. The PTT is polytrimethylene terephthalate with an intrinsic viscosity of 0.7-1.2dL / g, the glass fiber is alkali-free chopped glass fiber whose surface has been treated with a silane coupling agent, and the nano-calcium carbonate composite particles are surface Calcium carbonate nanoparticles grafted with styrene-styrene and methyl acrylate dual monomers, the MBS is a methacrylic acid-butadiene-styrene copolymer with a core-shell structure, and its relative density is 1.09-1.11g / cm3.

[0025] Preparation method: (1), place PTT in a forced air circulation oven, dry at 110°C-120°C for 6-8 hours, and set aside; (2), prepare nano-calcium carbonate composite particles: prepare nano-calcium carbonate 75wt% Use dei...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a PTT polyester flame retardation composition with excellent mechanical properties. The composition comprises the following ingredients, by weight, 60%-80% of PTT, 8%-12% of glass fibers, 2%-10% of calcium carbonate composite particles, 4%-8% of MBS, 4%-8% of flame retardants, 0.5%-2% of light stabilizing agents, 0.1%-0.5% of anti-oxidants and 0.1%-1% of lubricants. The calcium carbonate composite particles are calcium carbonate nanoparticles with surfaces after grafting of styrene and methyl acrylate dual monomers. The beneficial effects are that the PTT polyester flame retardation composition has excellent flame retardation performance and heat resistance, and also has good integrated mechanical properties of tensile strength, bending strength and impact intensity; the processability is good, the chemical resistant stability is excellent, the cost is low, and the appearance is good.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a PTT polyester flame-retardant composition with excellent mechanical properties. Background technique [0002] Polytrimethylene terephthalate (PTT), as a new type of polyester polymer material with excellent comprehensive properties, has been widely used in the fields of fibers, films, engineering plastics, etc., but unmodified PTT has low notched impact strength, The defects of high notch sensitivity, low tensile strength, and poor flame retardancy greatly limit the wider application of PTT in various fields. Contents of the invention [0003] The object of the present invention is to provide a PTT polyester flame retardant composition with excellent mechanical properties. [0004] The technical solution adopted by the present invention to solve the technical problem is: a PTT polyester flame retardant composition with excellent mechanical properties, and its compo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L51/10C08L51/04C08L85/02C08K13/06C08K9/06C08K7/14C08K5/134C08K5/526C08F292/00C08F212/08C08F220/14B29C47/92B29C48/92
Inventor 不公告发明人
Owner QINGDAO XINZHAN PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com