Green rapid-hardening early-strength magnesium phosphate-based healant and preparation method thereof
A technology of magnesium phosphate and repair agent, applied in the direction of climate sustainability, sustainable waste treatment, solid waste management, etc., can solve problems such as strength shrinkage, increase compactness, reduce preparation conditions, and increase impermeability The effect of grade
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0028] Example 1
[0029] A green quick-hardening early-strength magnesium phosphate-based repair agent, and its preparation method includes the following steps:
[0030] 1) Weighing of raw materials: Prepare material A and material B separately. The mass percentages of each component in material A are: potassium dihydrogen phosphate 88% (mass purity greater than 95%), borax 3.3%, and fine steel fiber 8.0% , Lithium carbonate 0.04%, cellulose ether 0.06%, FDN9000 polycarboxylic acid water reducing powder 0.5%, triethanolamine 0.1%; the mass percentages of each component of B material are: magnesium oxide 68%, fly ash 6%, silicon Ash 2%, steel slag powder 5%, ferrochrome tailings slag powder 10.5%, anhydrite 2.4%, UEA expansion agent 6%, triethanolamine 0.1%; mix material A and material B evenly, and dry them for later use;
[0031] 2) Weigh material A and material B at a mass ratio of 1:5.0;
[0032] 3) Weigh the water according to the water-to-glue ratio of 0.3, first put the B mate...
Example Embodiment
[0034] Example 2
[0035] A green quick-hardening early-strength magnesium phosphate-based repair agent, and its preparation method includes the following steps:
[0036] 1) Weighing of raw materials: according to the component ratio in Example 1, the A and B materials are mixed uniformly, and dried for use;
[0037] 2) Weigh material A and material B at a mass ratio of 1:4.0;
[0038] 3) Weigh the water according to the water-to-glue ratio of 0.3, control the water-to-gel ratio to 0.30, put the A and B materials in a portable mixer and mix them for 1 to 2 minutes, and then add water to continue mixing for 2 to 3 minutes to mix evenly. Vibrate and flatten the plastered surface within 10 minutes, maintain under standard conditions, green fast hardening early strength magnesium phosphate-based repair agent test block.
[0039] The prepared green quick-hardening early-strength magnesium phosphate-based repair agent test block is subjected to compressive and flexural strength, initial flui...
Example Embodiment
[0040] Example 3
[0041] A green quick-hardening early-strength magnesium phosphate-based repair agent, and its preparation method includes the following steps:
[0042] 1) Weighing of raw materials: Prepare material A and material B separately. The mass percentages of each component in material A are: 81% potassium dihydrogen phosphate (mass purity greater than 95%), 6.3% borax, and 12.0% fine steel fiber , Lithium carbonate 0.02%, cellulose ether 0.08%, FDN9000 polycarboxylic acid water reducing powder 0.4%, triethanolamine 0.2%; the mass percentages of each component of B material are: magnesium oxide 61%, fly ash 7.5%, silicon Ash 3%, active steel slag powder 6.5%, ferrochrome tailings slag powder 15%, anhydrite 1.8%, UEA expansion agent 5%, triethanolamine 0.2%; mix A and B materials evenly, and dry them for later use;
[0043] 2) Weigh material A and material B at a mass ratio of 1:5.0;
[0044] 3) Weigh the water according to the water-to-glue ratio of 0.28, first put the B m...
PUM
Property | Measurement | Unit |
---|---|---|
Compressive strength | aaaaa | aaaaa |
Compressive strength | aaaaa | aaaaa |
Flexural strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology