Nest type thermal insulation board and preparation method

A thermal insulation board and nest-type technology, applied in the direction of chemical instruments and methods, hydraulic material layered products, layered products, etc., can solve the problems of shortened service life, poor waterproofness, hidden safety hazards, etc., and achieve energy saving Low energy consumption, good water resistance, and the effect of saving construction time

Inactive Publication Date: 2015-10-07
CHONGQING YUDING ENERGY SAVING BUILDING MATERIAL
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the fireproof performance of inorganic thermal insulation materials can be guaranteed, their defects such as high density, low strength, and poor water resistance limit their application and promotion, especially because of their relatively high weight. Once they become loose due to thermal expansion and contraction, they are easy to fall off. Not only shorten the service life, but also bring safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nest type thermal insulation board and preparation method
  • Nest type thermal insulation board and preparation method
  • Nest type thermal insulation board and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] To make a nest-type thermal insulation board, first prepare the attachment slurry: add 10kg of foaming agent and 450kg of water to the foaming mixing system, and stir for 6 minutes at a speed of 700r / min; in addition, add dry powder silicon to the dry powder mixing system Salt cement 300kg, calcium hydroxide 90kg, perlite micropowder 300kg, fly ash 30kg, hypromellose 4kg, stir at 100r / min for 10 minutes; then put the foamed and stirred materials into the mixing In the mixing system, when feeding, first pour the liquid foaming material in the foaming mixing system, pour half of it, and then feed it with the dry powder material in the dry powder mixing system at the same time, add 1kg of water reducer and 50kg of acrylic emulsion at the same time, Stir while feeding at the speed of 1 / min, and continue to stir for 5 minutes after the feeding is completed to obtain the connecting slurry.

[0041] Preparation of bridge-blocking slurry: Mix 20 kg of acrylic emulsion and 10 kg...

Embodiment 2

[0049] To make nest-type thermal insulation boards, first prepare the attachment slurry: add 15kg of foaming agent and 500kg of water to the foaming mixing system, and stir for 6 minutes at a speed of 800r / min; in addition, add dry powder silicon to the dry powder mixing system Salt cement 300kg, calcium hydroxide 120kg, perlite micropowder 350kg, fly ash 35kg, hypromellose 5kg, stir at 125r / min for 10 minutes; then put the foamed and stirred materials into the mixing In the mixing system, when feeding, pour the liquid foaming material in the foaming mixing system first, pour half of it, and then feed it with the dry powder material in the dry powder mixing system at the same time, add 1.5kg of water reducer and 60kg of acrylic emulsion at the same time, Stir while feeding at a speed of 500r / min, and continue stirring for 5 minutes after the feeding is completed to obtain a connecting slurry.

[0050] Preparation of bridge-blocking slurry: Mix 25kg of acrylic acid emulsion and...

Embodiment 3

[0058] To make a nest-type thermal insulation board, first prepare the attachment slurry: add 20kg of foaming agent and 550kg of water to the foaming mixing system, and stir for 6 minutes at a speed of 900r / min; in addition, add dry powder silicon to the dry powder mixing system Salt cement 300kg, calcium hydroxide 150kg, perlite micropowder 400kg, fly ash 40kg, hypromellose 6kg, stir at 150r / min for 10 minutes; then put the foamed and stirred materials into the mixing In the mixing system, when feeding, pour the liquid foaming material in the foaming mixing system first, pour half of it, and then feed it with the dry powder material in the dry powder mixing system at the same time, add 2kg of water reducer and 70kg of acrylic emulsion at the same time, Stir while feeding at the speed of 1 / min, and continue to stir for 5 minutes after the feeding is completed to obtain the connecting slurry.

[0059] Preparation of bridge-blocking slurry: Mix 30kg of acrylic emulsion and 20kg ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Dry apparent densityaaaaaaaaaa
Thermal conductivityaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nest type thermal insulation board and belongs to the technical field of building external wall materials. A board body of the board is constituted by an assembling layer, a resistor bridge layer, a thermal insulation layer, a crack resisting layer and a decoration layer in sequence from the bottom surface layer to the external surface layer, and a preparation method comprises the steps of fabricating materials such as expanded perlite, cement, glass fibers and other accessory materials into different slurry materials, making a structure provided with multiple cone-tower-shaped nests out of the bottom surface, then continuing with the steps of formation, curing, trimming, steam curing, drying and the like, and obtaining the nest type thermal insulation board. The nest type thermal insulation board has the advantages that the dry surface of the thermal insulation board is low in density, the thermal conductivity coefficient is low, the compressive strength is high, the combustion-resisting perform level is high, the board has the fireproof function, and the board has the advantages of being low in weight, heat preservative, high in dimension stability, aging resistant, frost resistant, convenient to install, simple to construct, beautiful in appearance and the like. In the construction process, the flowing dust pollution caused by application of powder materials is reduced, approximately 60% of construction time is saved in the construction cycle, the construction cost is greatly reduced, and the energy consumption is saved in the building construction in the real sense.

Description

technical field [0001] The invention relates to the technical field of building exterior walls, in particular to a nest-type thermal insulation board capable of preventing expansion and falling off and a preparation method thereof. Background technique [0002] In my country, building energy consumption has become one of the three major energy consumers together with industrial energy consumption and transportation energy consumption. The energy-saving potential is huge. The building energy-saving industry has become an important organic part of the energy-saving and environmental protection industry. Building energy conservation is mainly accomplished through two aspects, one is to reduce building energy consumption, and the other is to improve the energy utilization efficiency of building energy consumption systems. The use of thermal insulation building materials is the main way to achieve building energy conservation. [0003] In the building energy-saving system, the h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B13/04
Inventor 莫世朋谭俊李阳洲黄清尧
Owner CHONGQING YUDING ENERGY SAVING BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products