2,4,6-diethyl triphosphate hydroxymethylphenoxy-1,3,5-triazine flame retardant and preparation method thereof

A technology of diethyl triphosphate hydroxymethylphenoxy and trialdehyde phenoxy is applied in the field of flame retardant, which can solve the problems of deteriorating the basic physical properties of materials, affecting the durability of flame retardant materials, and uneven dispersion, etc. The effect of strong practicability, high thermal stability, simple preparation process and easy operation

Active Publication Date: 2015-12-09
CHANGZHOU UNIV
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, when this kind of flame retardant is used in thermosetting polymer materials such as polyurethane and epoxy resin, it will cause obvious problems such as uneven dispersion and easy migration.
These problems will not only deteriorate the basic physical properties of the material, but also affect the flame retardant durability of the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 2,4,6-diethyl triphosphate hydroxymethylphenoxy-1,3,5-triazine flame retardant and preparation method thereof
  • 2,4,6-diethyl triphosphate hydroxymethylphenoxy-1,3,5-triazine flame retardant and preparation method thereof
  • 2,4,6-diethyl triphosphate hydroxymethylphenoxy-1,3,5-triazine flame retardant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] In a 500mL dry three-neck flask equipped with a mechanical stirrer, a constant pressure dropping funnel and a condensing reflux device, add 31.8g of potassium carbonate, 36.6g of p-hydroxybenzaldehyde and 250mL of refined tetrahydrofuran in sequence, and stir at room temperature for 1h under nitrogen protection Make it dissolve; Then take by weighing 18.45g cyanuric chloride (the molar ratio of cyanuric chloride and p-Hydroxybenzaldehyde is 1:3) and dissolve in 100mL refined tetrahydrofuran, slowly add it dropwise in the above-mentioned reaction system, Adding time is 1h; after 0.5h, slowly heat up to 60°C, reflux and stir for 24h, after the reaction is completed, change it to a distillation device, distill off the solvent under reduced pressure, pour it into a large amount of deionized water, and immediately precipitate a white precipitate; again Filter and wash the product repeatedly with deionized water for 3 times; vacuum-dry at 50°C for 12 hours to obtain a white po...

Embodiment 2

[0030] In a 500mL dry three-neck flask equipped with a mechanical stirrer, a constant pressure dropping funnel and a condensing reflux device, add 31.8g of potassium carbonate, 36.6g of p-hydroxybenzaldehyde and 250mL of refined tetrahydrofuran in sequence, and stir at room temperature for 1h under nitrogen protection Make it dissolve; Then take by weighing 18.45g cyanuric chloride (the molar ratio of cyanuric chloride and p-Hydroxybenzaldehyde is 1:4) and dissolve in 100mL refined tetrahydrofuran, slowly add it dropwise in the above-mentioned reaction system, Adding time is 1h; after 0.5h, slowly heat up to 60°C, reflux and stir for 24h, after the reaction is completed, change it to a distillation device, distill off the solvent under reduced pressure, pour it into a large amount of deionized water, and immediately precipitate a white precipitate; again Filter and wash the product repeatedly with deionized water for 3 times; vacuum-dry at 50°C for 12 hours to obtain a white po...

Embodiment 3

[0033] In a 500mL dry three-neck flask equipped with a mechanical stirrer, a constant pressure dropping funnel and a condensing reflux device, add 31.8g of potassium carbonate, 36.6g of p-hydroxybenzaldehyde and 250mL of refined tetrahydrofuran in sequence, and stir at room temperature for 1h under nitrogen protection Make it dissolve; Then take by weighing 18.45g cyanuric chloride (the molar ratio of cyanuric chloride and p-Hydroxybenzaldehyde is 1:3) and dissolve in 100mL refined tetrahydrofuran, slowly add it dropwise in the above-mentioned reaction system, Adding time is 1h; after 0.5h, slowly raise the temperature to 80°C, reflux and stir for 24h, after the reaction is completed, change it to a distillation device, distill off the solvent under reduced pressure, pour it into a large amount of deionized water, and immediately precipitate a white precipitate; again Filter and wash the product repeatedly with deionized water for 3 times; vacuum-dry at 50°C for 12 hours to obt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
decomposition temperatureaaaaaaaaaa
oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a 2,4,6-diethyl triphosphate hydroxymethylphenoxyl-1,3,5-triazine flame retardant and a preparation method thereof and belongs to the technical field of flame retarding. The preparation method comprises following steps: 1) adding cyanuric chloride, p-hydroxybenzaldehyde and a catalyst to an organic solvent, performing a heat reflux reaction and performing after-treatment to obtain a white solid powder 2,4,6-trialdehydephenoxyl-1,3,5-triazine; and 2) adding the 2,4,6-trialdehydephenoxyl-1,3,5-triazine, diethyl phosphite and triethylamine to an organic solvent, performing a heat reflux reaction, and performing pressure-reduced distillation to a reaction product to remove the organic solvent and the triethylamine to obtain the 2,4,6-diethyl triphosphate hydroxymethylphenoxyl-1,3,5-triazine flame retardant. The flame retardant is simple in preparation method, is high in yield, is good in practicability, is environment-friendly and pollution-free, and is available in large-scale industrial production.

Description

technical field [0001] The invention relates to a synthesis method of a flame retardant 2,4,6-diethyl triphosphate hydroxymethylphenoxy-1,3,5-triazine, in particular to a reactive flame retardant containing nitrogen and phosphorus The invention relates to a preparation method of a synergistic flame retardant element compound, which belongs to the field of flame retardant technology. Background technique [0002] Intumescent flame retardant (IFR) is a composite flame retardant mainly composed of nitrogen and phosphorus. It has the characteristics of high efficiency and low toxicity. It can prevent oxygen from entering the combustion area, and can also prevent the gaseous or liquid products generated by degradation from overflowing the surface of the material, thereby preventing further combustion of the material. This kind of flame retardant not only has high flame retardant efficiency but also has the characteristics of high efficiency, low toxicity and environmental protec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08K5/523C07F9/6521C08L75/08C08G18/48C08J9/04
Inventor 李锦春马彬彬杨荣张鑫胡文田
Owner CHANGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com