High-low temperature and static resistant PE corrugated pipe filling master batch as well as preparation method thereof

A technology of high and low temperature resistance, filling masterbatch, applied in the field of bellows filling masterbatch, can solve the problem of low ring stiffness, achieve high ring stiffness, increase thermal deformation temperature, and increase compatibility.

Inactive Publication Date: 2015-12-09
安徽玉发塑业有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the biggest problem plaguing large-diameter double-wall bellows at present is the low ring stiffness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] A high and low temperature resistant and antistatic PE bellows filler masterbatch, made of the following components by weight (kg): low density polyethylene 56, carbon black 34, silicon calcium magnesium (SCM) whisker 6, coconut oil acid Diethanolamide 1, lauric acid diethanolamide 2, sodium gluconate 1.5, cold-resistant plasticizer 0.3, barium stearate 2, talcum powder 7, antioxidant 2150.3, enhancer 14,

[0019] Among them, the reinforcing agent is made of the following components by weight (kg): high-density polyethylene 13, alkali-free glass fiber 25, superfine talc powder 25, ABS high rubber powder 11, paraffin wax 5, graphene oxide 14, silane Coupling agent 0.9, stearic acid 1.5, elastomer POE14.

[0020] The preparation method of the high and low temperature resistant antistatic PE corrugated pipe filling masterbatch comprises the following steps:

[0021] (1) Weigh the raw materials of each component according to the formula ratio;

[0022] (2) Add low-density...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-low temperature and static resistant PE corrugated pipe filling master batch which is prepared from the following raw material components in parts by weight: 50-60 parts of low density polyethylene, 30-40 parts of carbon black, 4-6 parts of silicon-calcium-magnesium (SCM) whiskers, 1-2 parts of coconut diethanolamide, 1-2 parts of lauric diethanolamide,1-2 parts of sodium gluconate, 0.1-0.5 part of a coldproof plasticizer, 1-2 parts of barium stearate, 5-8 parts of talcum powder, 0.2-0.4 part of an anti-oxidant 215 and 10-15 parts of an enhancer. The master batch can be subjected to extruding pelletization by a conventional double-screw extruder, and added for processing of a corrugated pipe, so that the processed corrugated pipe has the advantages of being resistant to high-low temperature, high in ring stiffness, light in weight, high in oxidation resistance, low in material consumption, convenient for construction and mounting, and high in static-resistant performance.

Description

technical field [0001] The invention relates to the field of bellows filling masterbatch, in particular to a high-low temperature resistant and antistatic PE bellows filling masterbatch and a preparation method thereof. Background technique [0002] With the development of the national economy and urban construction, the demand for large-diameter plastic drainage pipes to replace traditional cement pipes has become increasingly strong. However, the ring stiffness of large-diameter plastic pipes over 1 meter is an urgent problem to be solved. In order to meet the requirements of the project for the rigidity of the pipe ring, the manufacturer generally adopts the method of lining the steel plate or thickening the pipe wall, which is costly and complicated. [0003] Silicon-calcium-magnesium (SCM) whisker is a new type of silicate material with a one-dimensional single crystal structure, a diameter of 0.2-0.8 μm, and a length of 20-60 μm. It has extremely high mechanical prope...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08L55/02C08L91/06C08K13/06C08K9/06C08K3/04C08K7/10C08K7/14C08K3/34C08K5/098C08J3/22B29C47/92B29C48/92
CPCC08L23/06B29C48/92B29C2948/9258B29C2948/92704C08J3/226C08J2423/06C08K2201/014C08L2201/04C08L2203/18C08L2205/025C08L2205/035C08L2207/062C08L2207/066C08L23/0815C08L55/02C08L91/06C08K13/06C08K9/06C08K3/04C08K7/10C08K7/14C08K3/34C08K5/098
Inventor 舒玉法张宗运舒峰王克兰姚艳芳季琨
Owner 安徽玉发塑业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap