Emulsion type antisticking slipping agent for powderless PVC glove coating and preparation method thereof

An emulsion-type, slip agent technology, applied in the direction of coating, etc., can solve the problems of affecting glove quality, sticking back, glove sticking back and increasing the rate of defective products, so as to achieve industrial utilization value, improve economic benefits, and improve the production process. easy effect

Active Publication Date: 2015-12-09
LUOYANG SHENGJIA CHEM CO LTD
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These inorganic hardeners are usually light calcium carbonate, silicon powder, aluminum silicate powder and titanium dioxide, etc., because these inorganic powder hardeners themselves have a larger density, when the coating is highly diluted (paint: water = 1:10~15 dilution) It is very easy to precipitate when diluted and applied, which will seriously affect the quality of gloves, causing a series of problems such as twisting, sticking back, surface pollution, etc.
Waxes or silicone oils are often used as slip agents in glove coatings, but these slip agents often cause serious defects such as surface shrinkage cavities and increased surface tension of diluents
[0004] In the existing technology, the patent CN103013321A uses silicon dioxide as a hard agent, because the density of silicon dioxide is high, which will inevitably lead to a large amount of precipitation
Patent CN104419313A does not use inorganic hard agents, but only uses wax slurry as a slip agent, which will lead to increased stickiness and defective rate of gloves

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Emulsion type antisticking slipping agent for powderless PVC glove coating and preparation method thereof
  • Emulsion type antisticking slipping agent for powderless PVC glove coating and preparation method thereof
  • Emulsion type antisticking slipping agent for powderless PVC glove coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] A. Preparation of pre-emulsion

[0048] Take 5-40 parts of the synthesized water-based silicon-containing polyurethane, add 20-40 parts of deionized water and 1-5 parts of emulsifier, stir thoroughly for 20-30 minutes, and then add 10-60 parts of methacrylate The monomer, 5-20 parts of acrylate monomer, 0.1-3 part of diacrylate cross-linking agent monomer and 0.5-5 part of hydrophilic monomer are fully stirred and emulsified to obtain a pre-emulsion.

[0049] B. Preparation of compound emulsion by seed method

[0050] Add 10-20 parts of water-based silicon-containing polyurethane, add 40-60 parts of deionized water and 1-5 parts of emulsifier, add 10-20 parts of pre-emulsion after stirring, and add 1-2 parts of 10% ammonium persulfate , heated to 60-65°C for 30-40 minutes, began to drop the remaining pre-emulsion, and began to drop the remaining 8-10 parts of 10% ammonium persulfate, and finished the drop within 3-4 hours, and then raised the temperature to 85 ℃ for 1...

Embodiment 1

[0076] (1) Synthesis of waterborne silicon-containing polyurethane

[0077] Add 33.5 parts of Pol-2356 (hydroxyl value 54-56mgKOH / g, produced by Qingdao Yutian Chemical Industry), 22.4 parts of polysiloxane diol H-Si2311 (hydroxyl value 40-50mgKOH / g, Degussa Company), 1 part of trimethylolpropane (Sweden Pastor Company), 4 parts of dimethylol propionic acid hydrophilic agent (Sweden Pastor Company), heated up to 70 °C under full stirring, and added 20 parts For isophorone diisocyanate, heat up to 75-85°C to react for 3-5 hours, then cool down to 50°C, add 2 parts of salt-forming agent, form salt for 10 minutes, add 120 parts of deionized water, and then immediately add 3 parts The chain extender is discharged after 60 minutes of reaction to obtain the required water-based silicon-containing polyurethane.

[0078] (2) Synthesis of polyacrylate / silicon-containing polyurethane composite emulsion

[0079] A. Preparation of pre-emulsion

[0080] Take 10 parts of the synthesized ...

Embodiment 2

[0084] Repeat the steps of Example 1, except that in the synthesis of water-based silicon-containing polyurethane, 22.4 parts of polysiloxane in Example 1 are replaced by 22.4 parts of POL-2345 (hydroxyl value 54-56mgKOH / g, produced by Qingdao Yutian Chemical Industry) Glycol, other are all with embodiment 1.

[0085]The polyacrylate / silicon-containing polyurethane composite emulsion prepared by the method of the present invention is prepared according to the following powder-free PVC glove coating formula: 40 parts of water-based aliphatic polyester polyurethane BAYHYDROL110 (35% solid content, Bayer company), polyacrylate / 10 parts of silicon-containing polyurethane composite emulsion, 2 parts of leveling agent 1120 (Momentive High-tech Materials Group), 1 part of defoamer foamstar330 (Koning Chemical Company), 4.5 parts of thickener ASE-60, 0.5 parts of ammonia water, deionized 42 parts of water.

[0086] The preparation method of the control sample is the same as above, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Glass transition temperatureaaaaaaaaaa
Particle sizeaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to an emulsion type antisticking slipping agent for powderless PVC glove coating. The emulsion type antisticking slipping agent is a polyacrylate / silicon-containing polyurethane composite emulsion. The composite emulsion consists of 30-80% of polyacrylate and 20-70% of silicon-containing polyurethane. The composite emulsion can be added into the formula of powderless PVC glove coating to effectively substitute wax and organic silicone oil to play a slip increasing role, also can completely or partly replace an inorganic rigid agent to endow gloves with good molding and antisticking properties, has the advantages of no generation of precipitate, no after-tack of gloves, no edge torsion and more excellent slip grade, and has greater practicability.

Description

technical field [0001] The present invention relates to an emulsion type anti-sticking and slipping agent and its preparation method, in particular to a polyacrylate / silicon-containing polyurethane composite emulsion anti-sticking and slipping agent and its preparation method, especially a powder-free PVC glove The invention relates to an emulsion type anti-adhesive and slip agent for coating to replace slip agents such as inorganic powder hard agents and waxes, and a preparation method thereof. Background technique [0002] PVC gloves are made of PVC paste resin, plasticizer, viscosity reducer and fatty acid salt stabilizer through plasticization. They have the characteristics of chemical corrosion resistance, flame retardancy, high strength and easy processing. However, due to the addition of a large amount of plasticizers, PVC gloves without surface treatment are not easy to release and have poor wearability. The traditional treatment method is to coat dry lubricating ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D7/12C08F283/00C08G18/66C08G18/61C08G18/42
Inventor 李延科
Owner LUOYANG SHENGJIA CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com