Method for preparing light ceramisite by means of electroplating sludge

A technology of light ceramsite and electroplating sludge, which is applied in the field of light ceramsite, can solve the problems of microbial toxicity and other problems, and achieve the effect of large amount of mud consumption, thorough detoxification and technical feasibility

Active Publication Date: 2016-02-24
ZHANGZHOU WEISHUI SOLID WASTE DISPOSAL CO LTD
View PDF4 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the toxicity of electroplating sludge itself to microorganisms, biological treatment is still in the exploratory stage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing light ceramisite by means of electroplating sludge
  • Method for preparing light ceramisite by means of electroplating sludge
  • Method for preparing light ceramisite by means of electroplating sludge

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Embodiment one: The electroplating sludge is wet ground to 150 mesh (the weight is 30wt% of the mixed mud before firing), added to dry to 5% moisture content and dry ground to 100 mesh city sludge, weathered rock, silt, clay or kaolin ( The weight is 55wt% of the mixed mud before firing), and then dry-milled to 100 mesh reducing agent (the weight is 10wt% of the mixed mud before firing) and the expanding agent (the weight is 5wt% of the mixed mud before firing), and mixed After uniform treatment, the mixed sample is pressed by a granulator into a long strip-shaped ceramsite raw material of 20 mm × width 10 mm × thickness 10 mm, dried in the low-temperature zone of the kiln tail of the double-cylinder rotary kiln 5 at 300 ° C for 40 minutes, and then in the The kiln head is calcined in the high temperature zone of 1200°C for 50 minutes, and the light ceramsite product is obtained after discharging and cooling.

Embodiment 2

[0045] Embodiment two: The electroplating sludge is wet ground to 160 mesh (the weight is 35wt% of the mixed mud before firing), added and dried to a moisture content of 6% and dry ground to 120 mesh urban sludge, weathered rock, silt or kaolin (the weight is 55wt% of the mixed mud before firing), then add dry grinding to 120 mesh reducing agent (9wt% of the mixed mud before firing) and bulking agent (1wt% of the mixed mud before firing), mix well, etc. After treatment, the mixed sample is pressed by a granulator to grow into a cylindrical ceramic raw material with a diameter of 20mm and a diameter of 10mm. It is dried in the low-temperature zone of the kiln tail of the double-cylinder rotary kiln 5 at 350°C for 40 minutes, and then heated at the kiln head at a high temperature of 1250°C. Calcined in the zone for 45 minutes, discharged and cooled to obtain light ceramsite finished product.

Embodiment 3

[0046] Embodiment three: The electroplating sludge is wet ground to 170 mesh (the weight is 40wt% of the mixed mud before firing), added and dried to a moisture content of 7% and dry ground to 130 mesh city sludge, weathered rock, silt or kaolin (the weight is 50wt% of the mixed mud before firing), then add dry grinding to 130 mesh reducing agent (8wt% of the mixed mud before firing) and bulking agent (2wt% of the mixed mud before firing), mix well, etc. After treatment, the mixed sample is pressed into a spherical ceramic raw material with a diameter of 10mm by a granulator, dried in the low temperature zone of 400°C at the kiln tail of the double-cylinder rotary kiln 5 for 35 minutes, and then calcined in the high temperature zone of 1250°C at the kiln head for 40 minutes , after discharging and cooling, the finished product of lightweight ceramsite is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing light ceramisite by means of electroplating sludge. The method comprises the following steps that 1, raw materials are supplied by weight; 2, the electroplating sludge is ground to 150-200 meshes in a wet mode, municipal sludge, decomposed rock, sludge and clay or kaolin are ground to 100-150 meshes in a dry mode, anthracite is ground to 100-150 meshes in a drying mode, and ferric oxide or hematite is ground to 100-150 meshes in a dry mode; 3, all the raw materials are mixed evenly; 4, the mixed materials are deep refined and then extruded into raw ceramisite through a granulating machine; 5, the raw ceramisite is preheated and calcined into light ceramisite through a double-barrel rotary kiln, and after discharging and cooling are performed, the finished light ceramisite is obtained. According to the method, the electroplating sludge is effectively utilized, toxin removing is thorough, the reliability is achieved, the technology is simple, the sludge consumption is large, heavy metal pollutants can be simultaneously treated, the production cost is low, and the prepared ceramisite can be reused in construction industry.

Description

technical field [0001] The invention relates to the field of electroplating sludge treatment, in particular to a method for harmlessly treating electroplating sludge through incineration by using a double-cylinder rotary kiln and firing it into lightweight ceramsite. Background technique [0002] Electroplating sludge refers to heavy metal-containing sludge waste generated after wastewater treatment in the electroplating industry, and is included in the seventeenth category of hazardous waste in the national hazardous waste list. As the "final state" of electroplating wastewater, although its amount is much less than that of wastewater, since heavy metals such as Cu, Ni, Cr, Zn, Fe in wastewater are transferred to sludge, in a sense, Electroplating sludge is more harmful to the environment than electroplating wastewater. If this extremely harmful electroplating sludge is not disposed of in any way, its damage to the ecological environment is self-evident. On the other hand,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/00C04B33/132
CPCY02P40/60
Inventor 孙辉跃舒建峰徐军富陈志峰严杏文
Owner ZHANGZHOU WEISHUI SOLID WASTE DISPOSAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More