Red ceramic pigment and preparation method thereof

A ceramic coloring material and red technology, applied in the field of red ceramic coloring material and its preparation, and ceramic coloring material preparation, can solve problems such as limited application range and poor stability, and achieve simple production process, easy industrial production, and stable Good results

Inactive Publication Date: 2016-03-23
赖清甜
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is a shortcoming in the above patents, that is, the stability is not good under high temperature conditions, which limits its application range, and high temperature ceramics have irreplaceable unique effects in terms of material density and so on.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of red ceramic pigment, the parts by weight of each component are:

[0023] 0.35 parts of ferric oxide, 3 parts of chromium nitrate, 3 parts of aluminum nitrate, 0.5 parts of silicon dioxide, 5 parts of zinc oxide, 25 parts of urea, 0.1 part of sodium fluoride, and 15 parts of sodium fluorosilicate.

[0024] Its preparation method comprises the following steps:

[0025] Mix and stir the raw materials evenly to obtain a uniform mixture, then grind it thoroughly for 2.5 hours; calcinate the mixture at 700°C for 5 hours; after calcining, add the powder into purified water 20 times its weight, stir for 30 minutes, and filter out Moisture, drying; the dried solid is ground by a ball mill and passed through a 300-mesh sieve to obtain a red ceramic colorant.

Embodiment 2

[0027] A kind of red ceramic pigment, the parts by weight of each component are:

[0028] 0.45 parts of ferric oxide, 5 parts of chromium nitrate, 5 parts of aluminum nitrate, 0.75 parts of silicon dioxide, 7.5 parts of zinc oxide, 30 parts of urea, 0.25 parts of sodium fluoride, and 17.5 parts of sodium fluorosilicate.

[0029] Its preparation method comprises the following steps:

[0030] Mix and stir the raw materials evenly to obtain a uniform mixture, then grind it thoroughly for 2.5 hours; calcinate the mixture at 700°C for 5 hours; after calcining, add the powder into purified water 20 times its weight, stir for 30 minutes, and filter out Moisture, drying; the dried solid is ground by a ball mill and passed through a 300-mesh sieve to obtain a red ceramic colorant.

Embodiment 3

[0032] A kind of red ceramic pigment, the parts by weight of each component are:

[0033] 0.1 part of ferric oxide, 1 part of chromium nitrate, 5 parts of aluminum nitrate, 0.5 part of silicon dioxide, 10 parts of zinc oxide, 35 parts of urea, 0.1 part of sodium fluoride, 20 parts of sodium fluorosilicate.

[0034] Its preparation method comprises the following steps:

[0035] Mix and stir the raw materials evenly to obtain a uniform mixture, then grind the mixture thoroughly for 2.75 hours; calcinate the mixture at 725°C for 5.5 hours; after calcining, add the powder into pure water that is 22.5 times its weight, stir for 45 minutes, and then filter Remove water and dry; grind the dried solid with a ball mill and pass through a 325-mesh sieve to obtain a red ceramic colorant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to red ceramic pigment and a preparation method thereof and belongs to the technical field of ceramic pigment preparation. The red ceramic pigment is prepared from, by weight, 0.1-0.5 part of ferric oxide, 1-5 parts of chromic nitrate, 1-5 parts of aluminum nitrate, 0.5-1 part of silicon dioxide, 5-10 parts of zinc oxide, 25-35 parts of urea, 0.1-0.5 part of sodium fluoride and 15-20 parts of sodium fluosilicate. The preparation method includes the steps that the raw materials are evenly mixed and stirred to obtain a uniform mixture, and the mixture is fully ground for 2.5-3 hours; the mixture is forged for 5-6 hours at the temperature of 700-750 DEG C; after forging, the powder is added into pure water with the weight 20-25 times that of the powder, stirred for 30-60 min, drained and dried; the dried solid is ground through a ball mill, passes a screen with 300-350 meshes, and the red ceramic pigment is obtained. The ceramic pigment is narrow in particle size distribution, stable in color generation, little in color difference change and good in stability at high temperature. Meanwhile, the production technology is simple in process, equipment requirements are low, and industrial production is easy to achieve.

Description

technical field [0001] The invention relates to a ceramic color material, in particular to a red ceramic color material and a preparation method thereof, belonging to the technical field of ceramic color material preparation. Background technique [0002] Ceramic pigments, also known as pigments or color materials, are powdery decorative materials for colored ceramics formulated with color bases and fluxes or additives. Pigment = color base + flux, the color base is the chromogenic substance and other raw materials, and the flux is the silicate substance with a low melting point. [0003] The role of ceramic pigments includes three aspects: (1) body coloring: mixing the colorant with the body to make the body present a certain color after firing; (2) coloring of the glaze: the coloring agent and the basic glaze can be used Blending various color glazes and artistic glazes; (3) Drawing patterns: it is widely used for manual painting on the surface and under glaze of the glaz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09C1/00
CPCC09C1/0009
Inventor 赖清甜
Owner 赖清甜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More