Double-component conductive ink and preparing method thereof

A conductive ink and two-component technology, which is applied in the field of two-component conductive ink and its preparation, can solve the problems of conductive ink preparation process and long preparation cycle, so as to facilitate production operation and production cost control, reduce production cost, Improve the effect of printing thickness

Inactive Publication Date: 2016-04-20
DEYANG CARBONENE TECH
View PDF2 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the above-mentioned problems existing in the prior art, provide a kind of two-component conductive ink and preparation method thereof, the first of the present invention solves the problem of the preparation process and the long preparation period of the conductive ink in the prior art, The second is to make the conductive ink have better conductivity and easy dispersibility

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double-component conductive ink and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A two-component conductive ink, comprising the following components in parts by mass: 6-30 parts of conductive filler, 6-15 parts of resin, 0.5-1.5 parts of dispersant, 1-5 parts of auxiliary agent, 48.5-85 parts of solvent part; wherein, the conductive filler includes component one and component two mixed together, the component one is graphene, and the component two is one of graphite, carbon black, carbon fiber, carbon nanotube Or a mixture of several, the mass ratio of the first component to the second component is 1:0.2-8.

[0025] The resin is one or more of epoxy resin, polyamide resin, ethyl cellulose, acrylic resin, polyurethane resin, unsaturated polyester resin, cellulose acetate propionate, cellulose acetate butyrate .

[0026] The dispersant is polyethylene wax dispersant, BYK-163 dispersant or BYK-110 dispersant.

[0027] The auxiliary agent is one or a mixture of stabilizers, defoamers, thixotropic agents and curing agents.

[0028] Described solvent i...

Embodiment 2

[0034] A two-component conductive ink, including the following components in parts by mass: 6 parts of two-component conductive filler composed of graphene and graphite in a mass ratio of 1:0.2, 6 parts of epoxy resin, BYK-110 0.5 parts of dispersant, 2.5 parts of mixing aids composed of stabilizer, curing agent and thixotropic agent in a mass ratio of 0.5:1:0.5, composed of terpineol, diethylene glycol butyl ether acetate and diethylene glycol 85 parts of mixed solvents composed of butyl ether in a mass ratio of 2:2:5.

[0035] The present invention also provides a kind of preparation method of two-component conductive ink, and it comprises the steps:

[0036] (1) Take part of the solvent, first heat the solvent to 60 degrees, and then add the resin under the condition of stirring, after the resin is completely dissolved, a transparent binder is obtained;

[0037] (2) Add binders, conductive fillers, additives, dispersants and remaining solvents into the ball mill, the diame...

Embodiment 3

[0040] A two-component conductive ink, including the following components in parts by mass: 30 parts of two-component conductive filler composed of graphene and carbon black in a mass ratio of 1:8, 15 parts of epoxy resin, BYK- 1.5 parts of 110 dispersant, 5 parts of mixing aid composed of stabilizer, curing agent and defoamer in a mass ratio of 0.5:1:0.5, composed of terpineol, diethylene glycol butyl ether acetate and n-butyl acetate 48.5 parts of a mixed solvent composed of esters in a mass ratio of 2:2:5.

[0041] The present invention also provides a kind of preparation method of two-component conductive ink, and it comprises the steps:

[0042] (1) Take part of the solvent, first heat the solvent to 60 degrees, and then add the resin under the condition of stirring, after the resin is completely dissolved, a transparent binder is obtained;

[0043] (2) Add binders, conductive fillers, additives, dispersants and remaining solvents into the ball mill, the diameter of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a double-component conductive ink and a preparing method thereof. The double-component conductive ink is prepared from, by mass, 6-30 parts of conductive filler, 6-15 parts of resin, 0.5-1.5 parts of a dispersing agent, 1-5 parts of an auxiliary and 48.5-85 parts of a solvent. The preparing method of the double-component conductive ink comprises the following steps that firstly, a part of the solvent is taken and mixed with the resin through stirring until a transparent bonding material is obtained; secondly, the bonding material, the conductive filler, the auxiliary, the dispersing agent and the rest of the solvent are added into a ball grinder, and ball milling beads are added for grinding for 3-10 h after the conductive filler is wetted; thirdly, the ground material is filtered, and the finished product conductive ink is obtained. By means of the double-component conductive ink and the preparing method thereof, the problem that the preparing process and the preparing period of conductive ink are long in the prior art is solved, and the conductive ink has better conductivity and higher dispersibility.

Description

technical field [0001] The invention relates to the technical field of electronic material printing, in particular to a two-component conductive ink and a preparation method thereof. Background technique [0002] Conductive ink is a kind of ink with conductive ability. It conducts current by means of conductive materials dispersed in the ink carrier. It is mainly composed of conductive materials, linking agents (organic carriers), additives and solvents. Current conductive inks mainly use micro-nano gold powder, silver powder, copper powder, carbon powder or other metal powders as conductive fillers. High rate, high molding curing temperature and other shortcomings. [0003] In order to solve the above-mentioned technical problems, the following technology of using graphene to prepare conductive ink is proposed in the prior art: [0004] For example, Chinese Patent No. "201510090294.6" disclosed "a conductive ink based on graphene composite material and its preparation met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/52C09D11/03C09D11/102C09D11/14C09D11/107C09D11/104
CPCC09D11/52C09D11/03C09D11/102C09D11/104C09D11/107C09D11/14
Inventor 尹天平姚林何洪泉简璐赵景浩
Owner DEYANG CARBONENE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com