Modified anticorrosion and antirust paint with high temperature resistance

An anti-corrosion, anti-rust and high-temperature resistance technology, applied in the field of paint, can solve problems such as pungent smell, not easy to dry, metal rust, etc., to improve comprehensive performance, improve high-temperature anti-corrosion and anti-rust performance, and improve high-temperature resistance and anti-rust. performance effect

Active Publication Date: 2016-06-29
胜利油田方圆防腐材料有限公司
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After the modern paint is painted, not only will there be a pungent smell, but it will not be easy to dry in a certain period of time, and the viscosity is very poor. If it is painted on the metal, it will react with the metal to make the metal oxidize and rust.
[0003] The high-temperature anti-corrosion and anti-rust properties of the paints in the prior art cannot meet the needs in actual production, so it is urgent to invent a paint with excellent high-temperature anti-corrosion anti-rust properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The modified high-temperature, anti-corrosion and anti-rust paint proposed by the present invention comprises raw materials by weight: 100 parts of modified alkyd resin, 30 parts of dibutyltin dilaurate, 10 parts of phthalic anhydride polyester polyol, peroxide 5 parts of benzoyl, 6 parts of silicone acrylic emulsion, 3 parts of epoxy resin, 4 parts of xylene resin, 6 parts of modified sepiolite powder, 8 parts of barium sulfate, 5 parts of silicon carbide, 3 parts of organic bentonite, 4 parts of graphite , 2.5 parts of mica powder, 4.5 parts of xylene, 2.5 parts of mica iron oxide, 3.5 parts of zinc phosphate, 4.5 parts of nano-alumina, 3 parts of aluminum tripolyphosphate, 5 parts of chlorinated paraffin, 6 parts of chloromethyl styrene, 2.5 parts of triphenyl phosphate phosphate and 10 parts of dispersant.

[0017] The modified alkyd resin is prepared according to the following process: by weight, 5 parts of nano-silica, 4 parts of n-butyl acetate and 2.5 parts of p...

Embodiment 2

[0019] The modified high-temperature-resistant, anti-corrosion and anti-rust paint provided by the present invention comprises, in parts by weight, raw materials: 80 parts of modified alkyd resin, 50 parts of dibutyl tin dilaurate, 5 parts of phthalic anhydride polyester polyol, and 5 parts of peroxide. 8 parts of benzoyl, 3 parts of silicone acrylic emulsion, 5 parts of epoxy resin, 2 parts of xylene resin, 9 parts of modified sepiolite powder, 4 parts of barium sulfate, 8 parts of silicon carbide, 1 part of organic bentonite, 6 parts of graphite , 1 part of mica powder, 6 parts of xylene, 1 part of mica iron oxide, 5 parts of zinc phosphate, 3 parts of nano alumina, 5 parts of aluminum tripolyphosphate, 2 parts of chlorinated paraffin, 9 parts of chloromethyl styrene, 1 part of triphenyl phosphate phosphate and 15 parts of dispersant.

[0020] The modified alkyd resin is prepared according to the following process: by weight, 2 parts of nano-silicon dioxide, 5 parts of n-but...

Embodiment 3

[0022] The modified high-temperature resistant, anti-corrosion and rust-proof paint proposed by the present invention comprises, in parts by weight, raw materials: 120 parts of modified alkyd resin, 10 parts of dibutyl tin dilaurate, 15 parts of phthalic anhydride polyester polyol, and 10 parts of peroxide 2 parts of benzoyl, 9 parts of silicone acrylic emulsion, 1 part of epoxy resin, 6 parts of xylene resin, 3 parts of modified sepiolite powder, 12 parts of barium sulfate, 2 parts of silicon carbide, 5 parts of organic bentonite, 2 parts of graphite , 4 parts of mica powder, 3 parts of xylene, 4 parts of mica iron oxide, 2 parts of zinc phosphate, 6 parts of nano alumina, 1 part of aluminum tripolyphosphate, 8 parts of chlorinated paraffin, 3 parts of chloromethyl styrene, 4 parts of triphenyl phosphate phosphate and 5 parts of dispersant.

[0023] The modified alkyd resin is prepared according to the following process: by weight, 8 parts of nano-silicon dioxide, 3 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses modified anticorrosion and antirust paint with high temperature resistance. The paint comprises following raw materials: modified alkyd resin, dibutyltin dilaurate, a diethylene glycol phthalic anhydride polymer, benzoyl peroxide, a silicone acrylic emulsion, epoxy resin, xylene resin, modified sepiolite powder, barium sulfate, silicon carbide, organic bentonite, graphite, mica powder, xylene, micaceous iron oxide, zinc phosphate, nano-alumina, aluminum triphosphate, chlorinated paraffin, vinylbenzyl chloride, triphenyl phosphite phosphate and a dispersing agent. The paint has excellent high temperature resistance and anticorrosion and antirust performance.

Description

technical field [0001] The invention relates to the field of paint, in particular to a modified high-temperature-resistant, anti-corrosion and anti-rust paint. Background technique [0002] Paint is a chemical mixture coating that can firmly cover the surface of objects for protection, decoration, signs and other special purposes. According to the classification of modern chemical products, coatings belong to fine chemical products. After the modern paint is painted, it will not only emit a pungent smell, but also will not be easy to dry within a certain period of time, and the viscosity is very poor. When painted on the metal, it will react with the metal and cause the metal to oxidize and rust. [0003] The high-temperature, anti-corrosion and anti-rust properties of the paints in the prior art cannot meet the needs in actual production. Therefore, it is urgent to invent a paint with excellent high-temperature, anti-corrosion and anti-rust properties. SUMMARY OF THE INV...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D167/08C09D5/08C09D7/12
CPCC08K2201/011C08K2201/014C08L2201/08C08L2205/035C09D5/08C09D7/61C09D7/63C09D7/65C09D167/08C08L33/04C08L63/00C08K13/06C08K3/34C08K2003/3045C08K3/346C08K3/04C08K2003/2227C08K5/526
Inventor 许盟凯
Owner 胜利油田方圆防腐材料有限公司