A kind of modified high temperature resistant anticorrosion antirust paint

A technology of anti-corrosion, anti-rust and high temperature resistance, applied in the field of paint, can solve the problems of pungent smell, metal rust, not easy to dry, etc., to improve the comprehensive performance, improve the high-temperature anti-rust performance, improve the high-temperature anti-corrosion and anti-rust performance effect

Active Publication Date: 2018-11-20
胜利油田方圆防腐材料有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After the modern paint is painted, not only will there be a pungent smell, but it will not be easy to dry in a certain period of time, and the viscosity is very poor. If it is painted on the metal, it will react with the metal to make the metal oxidize and rust.
[0003] The high-temperature anti-corrosion and anti-rust properties of the paints in the prior art cannot meet the needs in actual production, so it is urgent to invent a paint with excellent high-temperature anti-corrosion anti-rust properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A modified high-temperature-resistant anti-corrosion and anti-rust paint proposed by the present invention, its raw materials include by weight: 100 parts of modified alkyd resin, 30 parts of dibutyltin dilaurate, 10 parts of phthalic anhydride polyester polyol, peroxide 5 parts of benzoyl, 6 parts of silicon acrylic emulsion, 3 parts of epoxy resin, 4 parts of xylene resin, 6 parts of modified sepiolite powder, 8 parts of barium sulfate, 5 parts of silicon carbide, 3 parts of organic bentonite, 4 parts of graphite , 2.5 parts of mica powder, 4.5 parts of xylene, 2.5 parts of mica iron oxide, 3.5 parts of zinc phosphate, 4.5 parts of nano-alumina, 3 parts of aluminum tripolyphosphate, 5 parts of chlorinated paraffin, 6 parts of chloromethyl styrene, 2.5 parts of triphenyl phosphate phosphate, 10 parts of dispersant.

[0017] The modified alkyd resin is prepared according to the following process: 5 parts of nano-silica, 4 parts of n-butyl acetate and 2.5 parts of propyl...

Embodiment 2

[0019] A kind of modified anticorrosion and antirust paint that the present invention proposes, its raw material comprises by weight: 80 parts of modified alkyd resin, 50 parts of dibutyltin dilaurate, 5 parts of phthalic anhydride polyester polyol, peroxide 8 parts of benzoyl, 3 parts of silicon acrylic emulsion, 5 parts of epoxy resin, 2 parts of xylene resin, 9 parts of modified sepiolite powder, 4 parts of barium sulfate, 8 parts of silicon carbide, 1 part of organic bentonite, 6 parts of graphite , 1 part of mica powder, 6 parts of xylene, 1 part of mica iron oxide, 5 parts of zinc phosphate, 3 parts of nano-alumina, 5 parts of aluminum tripolyphosphate, 2 parts of chlorinated paraffin, 9 parts of chloromethyl styrene, 1 part of triphenyl phosphate phosphate, 15 parts of dispersant.

[0020] The modified alkyd resin is prepared according to the following process: mix 2 parts of nano-silica, 5 parts of n-butyl acetate and 1 part of propylene glycol methyl ether acetate in ...

Embodiment 3

[0022] A kind of modified anti-corrosion and anti-rust paint that the present invention proposes, its raw material comprises by weight: 120 parts of modified alkyd resin, 10 parts of dibutyltin dilaurate, 15 parts of phthalic anhydride polyester polyol, peroxide 2 parts of benzoyl, 9 parts of silicon acrylic emulsion, 1 part of epoxy resin, 6 parts of xylene resin, 3 parts of modified sepiolite powder, 12 parts of barium sulfate, 2 parts of silicon carbide, 5 parts of organic bentonite, 2 parts of graphite , 4 parts of mica powder, 3 parts of xylene, 4 parts of mica iron oxide, 2 parts of zinc phosphate, 6 parts of nano-alumina, 1 part of aluminum tripolyphosphate, 8 parts of chlorinated paraffin, 3 parts of chloromethyl styrene, 4 parts of triphenyl phosphate phosphate, 5 parts of dispersant.

[0023] The modified alkyd resin is prepared according to the following process: 8 parts by weight of nano-silica, 3 parts of n-butyl acetate and 4 parts of propylene glycol methyl ethe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a modified high temperature resistant anti-corrosion and anti-rust paint. Resin, xylene resin, modified sepiolite powder, barium sulfate, silicon carbide, organic bentonite, graphite, mica powder, xylene, mica iron oxide, zinc phosphate, nano-alumina, aluminum tripolyphosphate, chlorinated paraffin, chlorine Methylstyrene, triphenyl phosphite phosphate and dispersant. The paint of the invention has excellent high temperature resistance, corrosion resistance and antirust performance.

Description

technical field [0001] The invention relates to the field of paints, in particular to a modified high-temperature-resistant, anti-corrosion, and anti-rust paint. Background technique [0002] Paint is a chemical mixture coating that can firmly cover the surface of objects for protection, decoration, marking and other special purposes. According to the classification of modern chemical products, coatings belong to fine chemical products. After the modern paint is painted, not only will there be a pungent smell, but it will not be easy to dry in a certain period of time, and the viscosity is very poor. If it is painted on the metal, it will react with the metal to make the metal oxidize and rust. [0003] The high-temperature resistance, anti-corrosion and anti-rust properties of the paints in the prior art cannot meet the needs in actual production, so it is urgent to invent a paint with excellent high-temperature resistance, anti-corrosion and anti-rust properties. Conten...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D167/08C09D5/08C09D7/61C09D7/63C09D7/65
CPCC08K2201/011C08K2201/014C08L2201/08C08L2205/035C09D5/08C09D7/61C09D7/63C09D7/65C09D167/08C08L33/04C08L63/00C08K13/06C08K3/34C08K2003/3045C08K3/346C08K3/04C08K2003/2227C08K5/526
Inventor 许盟凯
Owner 胜利油田方圆防腐材料有限公司