Method for resourceful treatment of industrial solid waste

A treatment method and technology for industrial solid waste, applied in solid waste management, sustainable waste treatment, climate sustainability, etc., can solve the problems of complex welding dust composition, pollution of soil and groundwater environment, and difficulty in comprehensive reuse, etc. Achieve the effect of lowering production and construction costs, reducing environmental pollution, improving mechanical properties and flame retardant properties

Active Publication Date: 2016-07-20
辽宁绿源再生能源开发有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The composition of welding dust is complex, and it is difficult to comprehensively reuse it. After the dust is collected by the dust collector, the dust is disposed of by landfill or transfer, which causes immeasurable pollution to the soil and groundwater environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for resourceful treatment of industrial solid waste

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Prepare welding dust with a mass fraction of 80%, straw powder with a mass fraction of 10% in the particle size range of 5-10mm, and a mass percentage of 10% coal chemical crystal salt with a particle size in the range of 1-5mm, and fully mix them in a mixer , add calcium stearate accounting for 0.1% of the weight of the mixture, add magnesium-aluminum hydrotalcite accounting for 0.5% of the weight of the mixture, add sodium lignosulfonate accounting for 0.1% of the weight of the mixture and stir and mix evenly; the treated mixture The material is fully mixed with cement powder according to the mass percentage of 85%, and activated alumina accounting for 0.1% of the weight of the mixed material is added, and then an appropriate amount of water is added to stir and mix to form a slurry; the slurry is injected into the trial mold and cast into shape; The test mold after the slurry is placed on a vibrating machine for 5 minutes to remove air bubbles and accelerate the hydro...

Embodiment 2

[0033] Prepare welding dust with a mass fraction of 60%, straw powder with a mass fraction of 20% in the particle size range of 5-10mm, and a mass percentage of 20% coal chemical crystallization salt with a particle size in the range of 1-5mm, and fully mix them in a mixer , add calcium stearate accounting for 0.5% of the weight of the mixture, add magnesium-aluminum hydrotalcite accounting for 0.1% of the weight of the mixture, add sodium lignosulfonate accounting for 0.5% of the weight of the mixture and stir and mix evenly; the treated mixture The material is fully mixed with cement powder according to the mass percentage of 100%, and activated alumina accounting for 1% of the weight of the mixed material is added, and then an appropriate amount of water is added to stir and mix to form a slurry; the slurry is injected into the trial mold and cast into shape; The test mold after the slurry is placed on a vibrating machine for 5 minutes to remove air bubbles and accelerate th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a method for resourceful treatment of industrial solid waste.Welding dust, straw powder and coal chemical crystalline salt are solidified into a composite plate at normal temperature through surface modification, inflaming retarding and cement solidification, and auxiliary adding, stir-mixing, room temperature curing, casting molding, bubble removal, surface treatment, demolding and drying are conducted on welding dust with particle size smaller than 100 microns, straw powder with particle size being 5-10 micrometers, and coal chemical crystalline salt with particles size being 1-5 micrometers so as to obtain the composite plate.The manufacturing process is free of pollution, the technology is simple, cost is low, the manufactured plate is high in practical value, and resourceful utilization of industrial solid waste is achieved.

Description

Technical field: [0001] The invention relates to a resource recovery treatment method for industrial solid waste, which belongs to the technical field of solid waste treatment and resource recovery in the field of environmental protection. technical background: [0002] With the rapid development of my country's economy, the output of solid waste is also showing an increasing trend. The harmfulness of solid waste pollution to the environment and human body cannot be ignored. It directly affects people's lives and seriously affects the environment and human health. [0003] Biomass resources are abundant and cheap, and its utilization has become a global research hotspot. Biomass resources are widely used as fuel, but rarely used as building materials. Biomass contains three main components of cellulose, hemicellulose and lignin, so it has the function of improving and optimizing the performance of building materials and endowing them with new characteristics. [0004] The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/02C04B18/04C04B18/24C04B22/06C04B24/04C04B24/18
CPCC04B28/02C04B2111/00017C04B2111/00767C04B18/0481C04B18/24C04B18/0463C04B24/04C04B24/18C04B22/06Y02W30/91
Inventor 周益辉
Owner 辽宁绿源再生能源开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap