Masterbatch of bending-resistant highly pressure-bearing corrugated tube and preparing method thereof

A high-pressure, corrugated pipe technology, applied in the field of materials, can solve problems such as low bending strength, affecting the performance of corrugated pipes, and affecting the safe use of pipes, and achieve the effect of excellent comprehensive performance

Active Publication Date: 2016-08-10
江门市蓬江区高威塑胶颜料有限公司
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the ring stiffness is low, the pipe will be easily deformed or twisted, which will affect the normal and safe use of the pipe
However, if the pipe is guaranteed to have good ring stiffness, its bending strength must not be high, which affects the performance of the entire bellows

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A method for preparing a bend-resistant high-pressure-bearing corrugated pipe masterbatch includes the following preparation steps:

[0023] S1. Weigh the raw materials of each component according to the above weight parts: 38 parts of polybutene resin, 13 parts of PA66 resin, 8 parts of biogas mud, 1 part of tin butyl mercaptan, 4 parts of chitosan, tributyl phosphate 2 parts, 4 parts polyacrylonitrile, 3 parts molybdenum sulfide, 4 parts polyaluminum chloride, 6 parts acetyl triethyl citrate, 1 part tantalum powder, 4 parts naina white carbon powder, 0.5 parts oxidized polyethylene wax, 0.5 part of titanate coupling agent KR-38S, 1 part of zinc stearate, 1 part of maleic anhydride;

[0024] S2. Add biogas mud, butyl tin mercaptan, tributyl phosphate, polyaluminum chloride, tantalum powder, molybdenum sulfide, nano white carbon powder, titanate coupling agent KR-38S, and maleic anhydride into the mix In the machine, mixing at a speed of 1000rpm and a temperature of 110°C f...

Embodiment 2

[0028] A method for preparing a bend-resistant high-pressure-bearing corrugated pipe masterbatch includes the following preparation steps:

[0029] S1. Weigh the raw materials of each component according to the above weight parts: 55 parts of polybutene resin, 26 parts of PA66 resin, 17 parts of biogas mud, 5 parts of tin butyl mercaptan, 11 parts of chitosan, tributyl phosphate 6 parts, 10 parts polyacrylonitrile, 9 parts molybdenum sulfide, 12 parts polyaluminum chloride, 13 parts acetyl triethyl citrate, 8 parts tantalum powder, 9 parts naina white carbon powder, 2 parts oxidized polyethylene wax, Titanate coupling agent KR-38S -3 parts, zinc stearate 4 parts, maleic anhydride 5 parts;

[0030] S2. Add biogas mud, butyl tin mercaptan, tributyl phosphate, polyaluminum chloride, tantalum powder, molybdenum sulfide, nano white carbon powder, titanate coupling agent KR-38S, and maleic anhydride into the mix In the machine, mixing at a speed of 1600rpm and a temperature of 130°C for...

Embodiment 3

[0034] A method for preparing a bend-resistant high-pressure-bearing corrugated pipe masterbatch includes the following preparation steps:

[0035] S1. Weigh the raw materials of each component according to the above weight parts: 47 parts of polybutene tree, 20 parts of PA66 resin, 12 parts of biogas mud, 3 parts of tin butyl mercaptan, 7 parts of chitosan, tributyl phosphate 4 parts, 7 parts polyacrylonitrile, 6 parts molybdenum sulfide, 8 parts polyaluminum chloride, 10 parts acetyl triethyl citrate, 4 parts tantalum powder, 6 parts naina white carbon powder, 1.2 parts oxidized polyethylene wax, 1.8 parts of titanate coupling agent KR-38S, 2 parts of zinc stearate, 3 parts of maleic anhydride;

[0036] S2. Add biogas mud, butyl tin mercaptan, tributyl phosphate, polyaluminum chloride, tantalum powder, molybdenum sulfide, nano white carbon powder, titanate coupling agent KR-38S, and maleic anhydride into the mix In the machine, mixing at a speed of 1300rpm and a temperature of 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Ring stiffnessaaaaaaaaaa
Bending strengthaaaaaaaaaa
Login to View More

Abstract

A masterbatch of a bending-resistant highly pressure-bearing corrugated tube and a preparing method thereof are disclosed. The masterbatch comprises polybutylene resin, PA66 resin, biogas mud, butylmercaptooxo stannane, chitosan, tributyl phosphate, polyacrylonitrile, molybdenum sulfide, polyaluminium chloride, triethyl acetyl citrate, tantalum powder, white charcoal powder, oxidized polyethylene wax, a titanate coupling agent KR-38S, zinc stearate and maleic anhydride according to weight parts. The ring rigidity of the corrugated tube prepared from the masterbatch is 13.5-14.6 KN / m2, the bending strength of the corrugated tube is 27-34 MPa, the corrugated tube after a flattening deformation test is free of cracks, and the corrugated tube has excellent comprehensive performance, and improves performance disadvantages of traditional corrugated tube materials.

Description

Technical field [0001] The invention belongs to the technical field of materials, and specifically relates to a bend-resistant high-pressure-bearing corrugated pipe master batch and a preparation method thereof. Background technique [0002] The bellows is a cylindrical thin-walled elastic shell with transverse corrugations, which has the functions of conversion, compensation, connection and energy storage. Compared with pipes made of the same material, corrugated pipes have the advantages of light weight, beautiful appearance, durability, low cost, and good elasticity. They play an irreplaceable role in the fields of medium transmission, power threading, machine tools, and home appliances. [0003] The materials of traditional corrugated pipes are mainly PE, PP or PA, and the performance of corrugated pipes made of different materials is not the same. As the application range of corrugated pipes becomes wider and wider, the performance requirements of corrugated pipes are getting...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/20C08L77/06C08L5/08C08K13/02C08K5/521C08K3/30C08K5/098C08K3/16F16L9/12
CPCC08L23/20C08L2203/18C08L2205/035F16L9/12C08L77/06C08L5/08C08K13/02C08K5/521C08K2003/3009C08K5/098C08K2003/164
Inventor 姚振红
Owner 江门市蓬江区高威塑胶颜料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products