Preparation method of special nano calcium carbonate for polyurethane sealant

A polyurethane sealant and nano calcium carbonate technology, applied in the field of nano materials, can solve the problems of difficult mechanical strength, poor compatibility, weak binding force, etc., and achieve the effects of increasing mechanical properties, improving mechanical strength, and good mechanical properties.

Inactive Publication Date: 2016-08-24
GUANGXI PINGNAN COUNTY HENGXIANG CALCIUM CARBONATE CO LTD
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the treatment agent used in this product is an inorganic condensation acid and a silane-based coupling agent, which have poor compatibility with the polyurethane system, weak binding force, and difficult to effectively improve the mechanical strength.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The preparation method of nano calcium carbonate special for polyurethane sealant of the present invention includes the following steps:

[0026] A. To 10kgCa(OH) 2 Add the crystal form control agent to the solution, stir and mix evenly, and introduce CO 2 The gas undergoes bubbling carbonization reaction until the pH of the solution is 7 to obtain a cooked slurry; the crystal form control agent is a mixture of sucrose and citric acid, and the addition amount is 0.01 kg;

[0027] B. After the cooked pulp is sieved, the temperature is raised to 60°C, and the mixture of saturated fatty acid sodium and bismuth carboxylate is added as a surfactant under stirring, and the pH is adjusted to 7, and the stirring is continued for 45 minutes;

[0028] C. The cooked slurry after stirring in step B is subjected to pressure filtration to obtain a filter cake, and the filter cake is dried, pulverized and further dried to obtain.

[0029] Ca(OH) in the step A 2 The preparation method of the so...

Embodiment 2

[0038] The preparation method of nano calcium carbonate special for polyurethane sealant of the present invention includes the following steps:

[0039] A. To 10kgCa(OH) 2 Add the crystal form control agent to the solution, stir and mix evenly, and introduce CO 2 The gas undergoes bubbling carbonization reaction until the pH of the solution is 7.3 to obtain a cooked slurry; the crystal form control agent is a mixture of sodium citrate and EDTA, and the addition amount is 0.05 kg;

[0040] B. After the cooked pulp is sieved, the temperature is raised to 65°C, and the mixture of saturated fatty acid sodium and bismuth carboxylate is added as a surfactant under stirring, and the pH is adjusted to between 7.5, and stirring is continued for 50 minutes;

[0041] C. The cooked slurry after stirring in step B is subjected to pressure filtration to obtain a filter cake, and the filter cake is dried, pulverized and further dried to obtain.

[0042] Ca(OH) in the step A 2 The preparation method o...

Embodiment 3

[0051] The preparation method of nano calcium carbonate special for polyurethane sealant of the present invention includes the following steps:

[0052] A. To 10kgCa(OH) 2 Add the crystal form control agent to the solution, stir and mix evenly, and introduce CO 2 The gas undergoes bubbling carbonization reaction until the pH of the solution is 7.5 to obtain a cooked slurry; the crystal form control agent is a mixture of sucrose and aluminum sulfate, and the addition amount is Ca(OH) 2 0.1kg of mass;

[0053] B. After the cooked pulp is sieved, the temperature is raised to 70°C, and the mixture of saturated fatty acid sodium and bismuth carboxylate is added as a surfactant under stirring, and the pH is adjusted to 8, and stirring is continued for 55 minutes;

[0054] C. The cooked slurry after stirring in step B is subjected to pressure filtration to obtain a filter cake, and the filter cake is dried, pulverized and further dried to obtain.

[0055] Ca(OH) in the step A 2 The preparatio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of special nano calcium carbonate for a polyurethane sealant. The method comprises steps as follows: A, a crystal form control agent is added to a Ca(OH)2 solution, the mixture is evenly mixed, CO2 is introduced for a bubbling carbonation reaction until the pH of the solution is 7-8, and boiled pulp is obtained; B, the boiled pulp is heated to 60-85 DEG C after being sieved, a mixture of saturated fatty acid sodium and bismuth carboxylate is added to be used as a surfactant in the stirring state, the pH value is adjusted to range from 7 to 9, and the mixture is continuously stirred for 45-60 min; C, the stirred boiled pulp in the step B is subjected to filter pressing, a filter cake is obtained, dried, crushed and further dried, and the special nano calcium carbonate is obtained. The prepared nano calcium carbonate has the higher binding force with a polyurethane system, the mechanical property of the polyurethane sealant can be significantly improved, and the tensile strength, the elongation at break and the tear strength of the polyurethane sealant can be improved after the special nano calcium carbonate is applied to the polyurethane sealant.

Description

Technical field [0001] The invention relates to the technical field of nano materials, in particular to a preparation method of nano calcium carbonate special for polyurethane sealants. Background technique [0002] Nano calcium carbonate (NaHO-CaCO 3 ) Is a new type of functional nano-level filler with excellent performance. It can not only fill and compatibilize, reduce costs, but also improve the surface color of the product and improve the comprehensive mechanical properties of the product. At present, in developed countries, nano-calcium carbonate has been widely used in medium and high-grade rubber, plastic products, sealants, coatings, inks, etc. In China, the area with the largest amount of nano-calcium carbonate is silicone sealant, followed by polyurethane sealant. The performance of polyurethane sealant is better than that of silicone sealant, but it is difficult to prepare. The amount of polyurethane sealant abroad is about the same as that of silicone sealant, mainl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01F11/18B82Y40/00C09J175/08C09J11/04
CPCC01F11/181C01F11/183C01P2006/12C08K3/26C08K2003/265C08K2201/011C09J11/04C09J175/08
Inventor 杨光贵
Owner GUANGXI PINGNAN COUNTY HENGXIANG CALCIUM CARBONATE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com