A degradable composite surgical suture

A technique for surgery and sutures, applied in the field of degradable composite surgical sutures, can solve problems such as unreported, and achieve the effects of good mechanical properties, simplified handling, good biological activity and biocompatibility

Active Publication Date: 2019-11-26
LINGNAN NORMAL UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There have been reports on the preparation of composite materials such as chitosan and gelatin, polyvinyl alcohol, AgNPs, etc., but the preparation of CT / GO / AgNPs composite surgical sutures has not been reported yet.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A degradable composite surgical suture

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] (1) Preliminary purification of CT. CT was used in hydrochloric acid (1mol / L) and sodium hydroxide (0.2mol / L) to remove inorganic salts and proteins, each for 1h. Wash in distilled water until neutral and dry. In addition, the GO aqueous solution was prepared by the Hummers method.

[0036] (2) CT and GO purified in step 1 are dissolved in dispersion liquid, wherein the composition of dispersion liquid is the aqueous solution of sodium hydroxide and urea, and the mass percentage of sodium hydroxide (NaOH) is 11wt% in this aqueous solution, urea ( The mass percent of Urea) is 4%.

[0037] In the mixed solution, the total amount of CT and GO added accounted for 6% of the aqueous solution mass (saturated state), wherein GO accounted for 6% of the total amount of CT and GO added (in terms of mass percentage). Then freeze-thaw at ultra-low temperature (-80°C) overnight. After melting at room temperature and stirring evenly, filter with 200-mesh silk cloth. Then mix the ...

Embodiment 2

[0043] Embodiment 2: The method is the same as in Example 1, except that GO accounts for 8% of the total amount added of CT and GO in step (2), and all the other steps are the same.

Embodiment 3

[0044] Embodiment 3: The method is the same as in Example 1, except that GO accounts for 10% of the total amount added of CT and GO in step (2), and all the other steps are the same.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention provides a degradable composite surgical suture, wherein the surgical suture is prepared by a method comprising the following steps: S1, adding chitin and graphene oxide to dispersion liquid, so that a saturated solution is formed; freezing and thawing the saturated solution at low temperature, performing uniform stirring after melting, so that a mixed solution is obtained; S2, adding epoxy chloropropane, which serves as a cross-linking agent, to the mixed solution obtained in the step S1, conducting stirring and standing, so that a cross-linked product is obtained; S3, purifying the cross-linked product obtained in the step S2, dissolving the cross-linked product in formic acid, so that a spinning collagen solution is prepared, and spinning and shaping the spinning collagen solution; and S4, soaking a shaped product obtained in the step S3 in a nano silver solution, performing drawing and drying, and disinfecting, so that the surgical suture is obtained. The suture prepared by the invention can solve the problem of existing chitosan polysaccharide sutures which are relatively weak in mechanical strength; the surgical suture is relatively good in mechanical performance; and meanwhile, the surgical suture is capable of satisfying a suturing demand under an in vivo polar environment.

Description

technical field [0001] The invention belongs to the technical field of medical materials, and more specifically relates to a degradable composite surgical suture. Background technique [0002] Existing CT sutures are generally prepared after acetylation of chitosan sutures, and chitosan and its derivative sutures are basically still used. The preparation and processing process is cumbersome, which limits the industrial application. [0003] At the same time, the existing CT or CTS sutures have poor mechanical properties, especially weak tensile strength, and cannot meet the clinical needs of high-strength sutures, especially for suturing in the strong acid environment of the stomach in vivo. Therefore, it is particularly important to seek and prepare a chitin surgical suture with proper mechanical strength properties. There have been reports on the preparation of composite materials such as chitosan, gelatin, polyvinyl alcohol, and AgNPs, but the preparation of CT / GO / AgNPs...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L17/00
CPCA61L17/00
Inventor 张卫陈道海
Owner LINGNAN NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products