Water-based ink

A technology of water-based ink and water-based polyurethane, which is applied in the direction of ink, household utensils, applications, etc., can solve problems affecting the appearance of packaging products, production equipment pollution, ink deterioration, etc., to improve storage stability, reduce usage, and good adhesion degree of effect

Active Publication Date: 2016-09-21
CANGNAN BAOFENG PRINTING
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although many types of water-based inks have been developed on the market, they often have a single function, and there are many problems in dispersibility, gloss and stability. In addition, water-based inks may be produced by raw materials during production and storage. Microorganisms brought in, contaminated by production equipment, introduced by the outside due to improper storage, and the finished printed matter is polluted by the microorganisms introduced by the outside, because the water in the water-based ink is more suitable for the survival and reproduction of microorganisms, making the ink very easy Susceptible to microbial erosion and deterioration, seriously affecting the appearance of packaging products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based ink

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] Preparation of Waterborne Polyurethane Binder

[0023] (1) Raw material pretreatment: first decompress and remove water from poly(ethylene succinate suberate)-1,4-butylene glycol ester diol at 90° C. and 0.1 MPa vacuum for 1 hour, and the polyoctylene succinate The number-average molecular weight of diacid ethylene glycol-1,4-butanediol ester diol is 3000, and xylylene diisocyanate is dehydrated and dried with activated molecular sieves;

[0024] (2) Preparation of prepolymer: 30 parts by weight of polyethylene succinate suberate glycol-1,4-butanediol ester diol is added in the flask, which is equipped with agitator, condenser, thermometer And ventilation pipe, pass into dry argon to reaction system, then start agitator, add the dimethylol propionic acid of 30 weight parts, add the xylylene diisocyanate of 8 weight parts and the diisocyanate of 0.03 weight part Dibutyltin laurate, slowly warming up to 70°C, constant temperature reaction for 2h;

[0025] (3) Cross-link...

Embodiment 1

[0031] 40 parts by weight of waterborne polyurethane;

[0032] 10 parts by weight of polypropylene emulsion;

[0033] 1 part by weight of polyamide wax;

[0034] 0.5 parts by weight of polystyrene-maleic acid triethanolamine salt;

[0035] 0.1 parts by weight of hydroxymethylcellulose;

[0036] 0.2 parts by weight of tributyl phosphate;

[0037] 2,6-di-tert-butyl-4-methylphenol: 0.2 parts by weight;

[0038] 0.3 parts by weight of sodium alkylsulfonate;

[0039] 10 parts by weight of pigment;

[0040] 15 parts by weight of water;

[0041] 5 parts by weight of ethanol;

[0042] 0.3 parts by weight of oregano oil;

[0043] 0.2 parts by weight of pine red plum essential oil.

Embodiment 2

[0045] 45 parts by weight of waterborne polyurethane;

[0046] 15 parts by weight of polypropylene emulsion;

[0047] 2 parts by weight of polyamide wax;

[0048] 1 weight part of polystyrene-maleic acid triethanolamine salt;

[0049] 0.8 parts by weight of hydroxymethylcellulose;

[0050] 0.6 parts by weight of tributyl phosphate;

[0051] 0.5 parts by weight of 2,6-di-tert-butyl-4-methylphenol;

[0052] 1 part by weight of sodium alkylsulfonate;

[0053] 20 parts by weight of pigment;

[0054] 30 parts by weight of water;

[0055] 15 parts by weight of ethanol;

[0056] 0.5 parts by weight of oregano oil;

[0057] 0.4 parts by weight of pine red plum essential oil.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses water-based ink. A formula range with the excellent comprehensive performance is provided through the comprehensive effect of effective selection and proportion combination of all components, so that all the components fully play roles; a water-based polyurethane connection material is obtained through the steps that polymerizing is conducted by taking polysuccinic acid octanedioic acid ethylene glycol-1,4-butylene adipate glycol and dimethylolpropionic acid as raw materials under catalysis of xylylene diisocynate, crosslinking is conducted through polyethylene glycol 200 under the action of dibutyl tin diacetate, and then chain extension is conducted through 1,4-butanediol. The adhesive force and stability of the obtained water-based polyurethane connection material are both improved; the obtained water-based ink has the advantages of being free of toxicity, preventing mildew, resisting oxidation and the like and has the very good adhesion and the high printing speed, added origanum oil and leptospermum scoparium essential oil have the broad-spectrum antibacterial effect, and therefore the problem that the storage time of a printed product is influenced by mildew is effectively solved.

Description

technical field [0001] The invention belongs to the field of ink, and more specifically relates to a water-based ink. Background technique [0002] PM2.5 is a pollutant in the atmosphere. Volatile organic compounds account for 21% of the substances that form PM2.5, and about 18% of the volatile organic compounds are produced by solvent-based coatings and ink emissions. Solvent-based coatings and inks need to be diluted with organic solvents, which not only consume fossil energy, but also contain a large amount of toxic and harmful substances such as benzene, toluene, xylene, and formaldehyde, and some of them have a volatilization period of more than ten years. Studies have shown that long-term inhalation of these volatile gases can lead to serious diseases such as aplastic anemia and leukemia. [0003] Water-based inks use water as the diluent and do not contain benzene, toluene, and xylene. Compared with traditional solvent-based inks, they can greatly reduce the emission...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/102C09D11/108C09D11/03C08G18/66C08G18/42C08G18/12
CPCC08G18/12C08G18/4238C08G18/664C08G18/6659C09D11/03C09D11/102C09D11/108C08G18/3206
Inventor 林福亮
Owner CANGNAN BAOFENG PRINTING