Antibacterial oil paint
A technology of paint and antibacterial agent, applied in the field of chemical coatings, can solve the problems of poor antibacterial performance and achieve the effects of low cost, good compatibility, good elongation and heat resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0015] The antibacterial paint of this embodiment is prepared from the following raw materials in parts by weight: 20 parts of phenolic resin, 25 parts of epoxy resin, 1 part of phosphoric acid, 1 part of sodium silicate, 0.5 part of zinc isooctanoate, 2 parts of boric acid, 1 part of aluminum sulfate 2.5 parts of citric acid monohydrate, 1 part of glass powder, 30 parts of toluene, 3 parts of hydroquinone, and 0.1 part of sulfadiazine.
[0016] The preparation method of the antibacterial paint of the present embodiment is: firstly mix phenolic resin, epoxy resin, phosphoric acid, sodium silicate, zinc isooctanoate, boric acid, aluminum sulfate, citric acid monohydrate, glass powder, toluene, terephthalate Phenol and sulfadiazine were put into the dispersion tank, and kept stirring evenly for 20 minutes. When the solid content reached 85 wt%, the stirring was stopped, and the obtained paint product was weighed and packaged.
Embodiment 2
[0018] The present embodiment antibacterial paint is prepared from the following raw materials in parts by weight: 25 parts of phenolic resins, 20 parts of epoxy resins, 2 parts of phosphoric acid, 3 parts of sodium silicate, 1 part of zinc isooctanoate, 3 parts of boric acid, 2 parts of aluminum sulfate 2 parts, 2 parts of citric acid monohydrate, 3 parts of glass powder, 35 parts of toluene, 4 parts of hydroquinone, 0.5 parts of sulfadiazine.
[0019] The preparation method of the antibacterial paint of the present embodiment is: firstly mix phenolic resin, epoxy resin, phosphoric acid, sodium silicate, zinc isooctanoate, boric acid, aluminum sulfate, citric acid monohydrate, glass powder, toluene, terephthalate Phenol and sulfadiazine were put into the dispersion tank and kept uniformly stirring for 25 minutes. When the solid content reached 85 wt%, the stirring was stopped, and the obtained paint product was weighed and packaged.
Embodiment 3
[0021] The antibacterial paint of this embodiment is prepared from the following raw materials in parts by weight: 30 parts of phenolic resin, 15 parts of epoxy resin, 3 parts of phosphoric acid, 5 parts of sodium silicate, 2 parts of zinc isooctanoate, 5 parts of boric acid, 0.5 parts of aluminum sulfate 3 parts of citric acid monohydrate, 5 parts of glass powder, 40 parts of toluene, 6 parts of hydroquinone, 1 part of urotropine.
[0022] The preparation method of the antibacterial paint of the present embodiment is as follows: according to the formula requirements, phenolic resin, epoxy resin, phosphoric acid, sodium silicate, zinc isooctanoate, boric acid, aluminum sulfate, citric acid monohydrate, glass powder, toluene, terephthalate Put phenol and urotropine into the dispersing tank, keep uniform stirring for 18 minutes, stop stirring when the solid content reaches 83wt%, weigh the obtained paint product, and pack.
PUM
| Property | Measurement | Unit |
|---|---|---|
| diameter | aaaaa | aaaaa |
| antibacterial rate | aaaaa | aaaaa |
Abstract