Light yellow crystal bead blank and preparation method thereof

A technology of crystal bead embryo and color, applied in the field of light yellow crystal bead embryo and its preparation, can solve the problems of uneven color, low production efficiency, poor colorability, etc. Effect

Active Publication Date: 2016-11-09
浙江鑫伟兴水晶有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Light yellow color crystal bead embryos are semi-finished products used to manufacture black crystal products. In the existing technology of light yellow color crystal bead embryos, crucibles are often used to make them. There are poor coloring properties, uneven colors, patterns, unstable product quality, and low production efficiency. , not suitable for continuous mass production. In addition, it contains aluminum, and the use of coal is easy to cause environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of preparation method of the crystal bead embryo of light yellow color, comprises the following steps:

[0017] 1) Take 120 parts of fire throwing powder, 100 parts of quartz sand, 100 parts of soda ash, 70 parts of broken glass, 1.5 parts of sodium chloride, 30 parts of sodium nitrate, 18 parts of calcium carbonate, 5 parts of caustic soda, 1.3 parts of sodium chlorate, 20 parts of borax decahydrate, 3 parts of cerium oxide, 4.8 parts of high titanium slag and 3.9 parts of titanium concentrate, mix well;

[0018] 2) put into granulator and carry out granulation, particle size is 0.5cm;

[0019] 3) Put it into the crystal pool by the feeder, keep the liquid level stable during melting, and control the temperature at 1320°C;

[0020] 4) After 12 hours in the crystal pool, enter the clarification tank for 2 hours, molded after cooling in the feeding channel, and the temperature is controlled at 900 °C;

[0021] 5) After being polished and shaped by the fire throw...

Embodiment 2

[0024] A kind of preparation method of the crystal bead embryo of light yellow color, comprises the following steps:

[0025] 1) Take 200 parts of fire throwing powder, 150 parts of quartz sand, 250 parts of soda ash, 170 parts of cullet, 11 parts of sodium chloride, 75 parts of sodium nitrate, 50 parts of calcium carbonate, 35 parts of caustic soda, 27 parts of sodium chlorate, 40 parts of borax decahydrate, 10 parts of cerium oxide, 40 parts of high titanium slag and 13 parts of titanium concentrate, mix well;

[0026] 2) put into granulator and carry out granulation, particle size is 2.5cm;

[0027] 3) Throw it into the crystal pool by the feeder, keep the liquid level stable during melting, and control the temperature at 1380°C;

[0028] 4) After 12 hours in the crystal pool, enter the clarification tank for 2 hours, molded after cooling in the feeding channel, and the temperature is controlled at 1000 °C;

[0029] 5) After being polished and shaped by the fire throwing ...

Embodiment 3

[0032] A kind of preparation method of the crystal bead embryo of light yellow color, comprises the following steps:

[0033] 1) Take 150 parts of fire throwing powder, 115 parts of quartz sand, 175 parts of soda ash, 115 parts of cullet, 6 parts of sodium chloride, 50 parts of sodium nitrate, 30 parts of calcium carbonate, 20 parts of caustic soda, 14 parts of sodium chlorate, 25 parts of borax decahydrate, 5 parts of cerium oxide, 20 parts of high titanium slag and 7 parts of titanium concentrate, mix well;

[0034] 2) put into granulator and carry out granulation, particle size is 1.5cm;

[0035] 3) Throw it into the crystal pool by the feeder, keep the liquid level stable during melting, and control the temperature at 1350°C;

[0036] 4) After 12 hours in the crystal pool, enter the clarification tank for 2 hours, molded after cooling in the feeding channel, and the temperature is controlled at 950 °C;

[0037] 5) After being polished and shaped by the fire throwing furn...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a light yellow crystal bead blank. The light yellow crystal bead blank is prepared from 100-200 parts by weight of fire polishing powder, 80-150 parts by weight of quartz sand, 100-250 parts by weight of sodium carbonate, 60-170 parts by weight of cullet, 1-11 parts by weight of sodium chloride, 22-75 parts by weight of sodium nitrate, 10-50 parts by weight of calcium carbonate, 4-35 parts by weight of caustic soda flake, 1-27 parts by weight of sodium chlorate, 10-40 parts by weight of borax decahydrate, 1-10 parts by weight of cerium oxide, 3-40 parts by weight of high titanium slag and 2-13 parts by weight of ilmenite concentrate. The light yellow crystal bead blank has good stainability, stable quality and high production benefits, is suitable for mass production and does not cause environmental pollution.

Description

technical field [0001] The invention specifically relates to a light yellow crystal bead embryo and a preparation method thereof. Background technique [0002] Light yellow color crystal bead embryos are semi-finished products used to manufacture black crystal products. In the existing technology of light yellow color crystal bead embryos, crucibles are often used to make them. There are poor coloring properties, uneven colors, patterns, unstable product quality, and low production efficiency. , not suitable for continuous mass production. In addition, it contains aluminum, and the use of coal is easy to cause environmental pollution. Contents of the invention [0003] The object of the present invention is to address the deficiencies of the prior art and provide a light yellow crystal bead embryo with good colorability, stable quality, high production efficiency, suitable for mass production, and no environmental pollution and a preparation method thereof. [0004] In or...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C6/06C03C12/00C03C4/02
CPCC03C1/002C03C4/02C03C12/00
Inventor 杨鑫法
Owner 浙江鑫伟兴水晶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com