Glazed brick with ultrafine aluminum oxide or ultrafine aluminum hydroxide for improving glaze abrasion resistance and preparation method of glazed brick

A technology of ultra-fine aluminum hydroxide and ultra-fine alumina is applied in the field of polished glazed tiles, which can solve the problems of poor wear resistance of polished glazed tiles, and it is difficult to meet the needs of high wear resistance of glazed surfaces, and achieves low cost and is beneficial to The effect of industrial production and expansion of production

Inactive Publication Date: 2016-12-07
FOSHAN UNIVERSITY +1
View PDF1 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because the surface of the glazed tile is "glazed", the crystal content in the glaze is less, so the finished glazed tiles obtained by the existing glazed tile production process have poor wear resistance, and it is difficult to meet the requirements of the customer for laying the ground. The need for higher wear resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] In this embodiment, ultrafine aluminum oxide or ultrafine aluminum hydroxide is introduced to improve the wear resistance of glazed tiles. The raw materials for firing glazed tiles include: 92% raw material glaze and 8% frit. The quality of glaze is 0.02% carboxymethyl cellulose, 0.3% sodium tripolyphosphate and 0.03% polyvinyl alcohol, and the base glaze is 2.3% superfine alumina;

[0029] Raw glaze raw material ratio: feldspar 33%, quartz 8%, limestone 12%, dolomite 5%, burnt talc 10%, wollastonite 5%, clay 12%, zinc oxide 5%, barium carbonate 10% ;

[0030] Frit ratio: 40% feldspar, 5% quartz, 8% limestone, 7% dolomite, 5% burnt talc, 30% borax, 2% clay, and 3% barium carbonate.

[0031] The preparation steps of polished glazed tiles that introduce ultra-fine alumina or ultra-fine aluminum hydroxide to improve the wear resistance of the glaze are as follows:

[0032] (1) According to the mass ratio of mixed glaze: ball: water = 1.5:3:0.8 (mixed glaze refers to raw ...

Embodiment 2

[0035] This embodiment introduces superfine aluminum oxide or superfine aluminum hydroxide to improve the wear resistance of glazed glazed tiles. The firing raw materials for glazed tiles include: 100% raw material glaze, which is the basic glaze, and the quality of the basic glaze is 0.02% carboxymethyl Cellulose, 0.3% sodium tripolyphosphate and 0.04% polyvinyl alcohol, 4.6% alumina precursor (ultrafine aluminum hydroxide) in the base glaze quality;

[0036] Raw glaze raw material ratio: feldspar 28%, quartz 8%, limestone 18%, dolomite 5%, burnt talc 10%, wollastonite 4%, clay 10%, zinc oxide 4%, barium carbonate 10% , Spodumene 3%.

[0037] The preparation steps of polished glazed tiles that introduce ultra-fine alumina or ultra-fine aluminum hydroxide to improve the wear resistance of the glaze are as follows:

[0038] (1) According to the mass ratio of mixed glaze: ball: water = 1:2:0.8 (mixed glaze refers to raw glaze and superfine aluminum hydroxide), put the raw materia...

Embodiment 3

[0041] This embodiment introduces superfine aluminum oxide or superfine aluminum hydroxide to improve the wear resistance of glazed tiles. The firing raw materials for the glazed tile glaze include: 100% raw material glaze, which is the basic glaze, and the quality of the basic glaze is 0.01% carboxymethyl Cellulose, 0.5% sodium tripolyphosphate and 0.05% polyvinyl alcohol, 6.9% superfine aluminum oxide in the base glaze quality;

[0042] Raw glaze raw material ratio: feldspar 28%, quartz 8%, limestone 18%, dolomite 7%, burnt talc 10%, wollastonite 5%, clay 10%, zinc oxide 4%, barium carbonate 10% .

[0043] The preparation steps of polished glazed tiles that introduce ultra-fine alumina or ultra-fine aluminum hydroxide to improve the wear resistance of the glaze are as follows:

[0044] (1) According to the mass ratio of mixed glaze: ball: water = 1:2:0.8 (mixed glaze refers to raw glaze and superfine alumina), put the raw materials into the ball mill, and add the glaze prop...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of building ceramic production and particularly relates to a glazed brick with ultrafine aluminum oxide or ultrafine aluminum hydroxide for improving glaze abrasion resistance and a preparation method of the glazed brick. A glaze of the glazed brick is prepared from, by mass, 0-10% of raw glaze, 0-100% of basic glaze formed by frits, ultrafine aluminum oxide or ultrafine aluminum hydroxide being 0.1-15% of the mass of the basic glaze, and a glaze property regulator. By adoption of existing glazing process and existing firing process of building ceramic factories, extensive raw material sources and fine composition adjustment of formulation are realized, the glaze of the fired glazed brick is smooth and flat and has high hardness and high abrasion resistance basically comparable to abrasion resistance of a polished ceramic brick, original rheological colorfulness is maintained, industrial production is benefited, and the preparation method is an important way of large-scale glazed brick production.

Description

technical field [0001] The invention belongs to the technical field of building ceramic production, and specifically relates to a polished glazed tile which introduces superfine alumina or superfine aluminum hydroxide to improve the wear resistance of the glazed surface and a preparation method thereof. Background technique [0002] Ceramic tiles have a wide range of applications in decoration, and can be widely used in walls and floors of homes or offices. According to people's aesthetic needs, they can be used for large-area laying, and can also be used for small-area decorative screens. Different applications require Different styles of products. Fully polished glazed tiles are a brand new ceramic tile product that has only appeared in recent years. The characteristic of its glaze is that the surface glaze is transparent and does not cover the underlying glaze layer and various decorative flower glazes. When the glaze is polished, only a thin layer of transparent glaze i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/14C03C8/02C04B41/86
CPCC03C8/02C03C8/14C04B41/5022C04B41/86C04B41/4539C04B41/4543
Inventor 胡晓洪詹长春柯美云
Owner FOSHAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More