A technology of plastic masterbatch and environmental response, which is applied in the field of preparation of environmentally responsive functional plastic masterbatch, can solve the problems of limited application prospect, complicated preparation process and high cost, and achieves expansion of application scope, simple preparation process and low cost. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] The preparation method of a kind of environment-responsive functional plastic master batch according to the present invention, the preparation process is as follows: the formula ratio is calculated by mass percentage:
[0024] (1) Mix 50% PP (polypropylene), 10% sodium chlorite, and 2% dioctyl phthalate in a high-speed mixer at 500 rpm for 5 minutes;
[0025] (2) Add 3% simethicone, 1% paraffin, 10% talc, and 8% calcium carbonate to step (1), and mix in a high-speed mixer at 800 rpm for 2 minutes. Put the above mixture into a twin-screw extruder, control the temperature at 150-190°C, then put the product into a granulator for granulation.
[0026] Using this masterbatch as a raw material can be used in the field of environmentally responsive daily-use plastic products and film products.
Embodiment 2
[0028] The preparation method of a kind of environment-responsive functional plastic master batch according to the present invention, the preparation process is as follows: the formula ratio is calculated by mass percentage:
[0029] (1) 70% LDPE (low-density polyethylene), 0.2% sodium chlorate, 5% sodium perchlorate, 3% PE wax (polyethylene wax), mixed 2 minutes at 1000 rpm in a high-speed mixer;
[0030] (2) Add 5% paraffin and 20% kaolin into step (1), and mix for 3 minutes in a high-speed mixer at 500 rpm. Put the above mixture into a twin-screw extruder, control the temperature at 130-220°C, then put the product into a granulator for granulation.
[0031] Using this masterbatch as a raw material can be used in fields such as environment-responsive functional plastic masterbatch products and hollow containers.
Embodiment 3
[0033] The preparation method of a kind of environment-responsive functional plastic master batch according to the present invention, the preparation process is as follows: the formula ratio is calculated by mass percentage:
[0034] (1) 80% LLDPE (linear low-density polyethylene), 1% citric acid, 1% stearic acid, 1% zinc stearate, 2% simethicone oil, in a high-speed mixer at 1000 rpm Mix for 6 minutes;
[0035] (2) Add 5% simethicone, 1% dioctyl phthalate, 5% kaolin, and 5% silicon powder to step (1), and mix in a high-speed mixer at 500 rpm for 2 minutes. Put the above mixture into a twin-screw extruder, control the temperature at 130-220°C, then put the product into a granulator for granulation.
[0036] Using this masterbatch as a raw material, it can be used in fields such as environmentally responsive healthcare, automotive interiors, and home improvement.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com