High-uniformity colored polyester industrial yarn and preparation method thereof
A colored polyester, uniform technology, applied in the field of polyester fiber, can solve the problems of uneven fineness, difficulty in silk processing, uneven strength, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0055] Example 1
[0056] A method for preparing modified polyester specifically includes the following steps:
[0057] (1) Preparation of glycol terephthalate:
[0058] The terephthalic acid with a molar ratio of 1:1.3 and 2-pentyl-1,3 propylene glycol were prepared into a slurry and added to the reactor at a concentration of 50% by weight and the added amount was 0.3% by weight of terephthalic acid. Under the catalysis of sulfuric acid, the esterification reaction is carried out. The esterification reaction is pressurized in a nitrogen atmosphere. The pressurization pressure is normal pressure and the temperature is 180°C. When the amount of water distilled in the esterification reaction reaches 90% of the theoretical value When is the end point of the esterification reaction, the diol terephthalate is obtained;
[0059] (2) Preparation of ethylene terephthalate:
[0060] The terephthalic acid and ethylene glycol were prepared into a slurry with a molar ratio of 1:1.2 and then added...
Example Embodiment
[0066] Example 2
[0067] The preparation method of the modified polyester of Example 2, wherein the preparation process of the modified polyester is the same as that of Example 1, and the main technical parameters are shown in Table 1. After adding the glycol terephthalate in step (3), Stir and mix for 16 minutes. Under the action of adding 0.011% of the total weight of terephthalic acid to the catalyst antimony trioxide and adding 0.02% of the total weight of terephthalic acid to stabilizer triphenyl phosphate, the negative Under the condition of low pressure, the polycondensation reaction in the low-vacuum stage was started. The pressure in this stage was smoothly pumped from normal pressure to an absolute pressure of 490Pa, the temperature was controlled at 262°C, and the reaction time was 31 minutes; The reaction pressure is reduced to an absolute pressure of 90 Pa, the reaction temperature is controlled at 276° C., and the reaction time is 51 minutes to obtain a modified po...
Example Embodiment
[0069] Example 3
[0070] The preparation method of the modified polyester of Example 3, wherein the preparation process of the modified polyester is the same as that of Example 1, and the main technical parameters are shown in Table 1. After adding the glycol terephthalate in step (3), Stir and mix for 16 minutes. Under the action of adding 0.03% of the total weight of terephthalic acid to the catalyst antimony trioxide and adding 0.02% of the total weight of terephthalic acid to stabilizer triphenyl phosphate, the negative Start the polycondensation reaction in the low vacuum stage under the condition of low pressure, the pressure in this stage is smoothly pumped from normal pressure to an absolute pressure of 498 Pa, the temperature is controlled at 263°C, and the reaction time is 32 minutes; then the vacuum is continued to perform the polycondensation reaction in the high vacuum stage. The reaction pressure was reduced to an absolute pressure of 90 Pa, the reaction temperatur...
PUM
Property | Measurement | Unit |
---|---|---|
Breaking strength | aaaaa | aaaaa |
Breaking strength | aaaaa | aaaaa |
Breaking strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap