A kind of polyacrylonitrile fiber-hemin biomimetic catalyst and preparation method thereof

A polyacrylonitrile fiber and biomimetic catalyst technology, applied in the field of biomimetic catalysis, can solve the problems of complex preparation process, high energy consumption, and unsatisfactory catalytic activity, and achieve the effect of simple process flow, low energy consumption, and improved catalytic activity

Active Publication Date: 2018-08-31
TIANJIN POLYTECHNIC UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

TiO 2 Materials such as thin films, graphene, and activated carbon fibers can be used to support metalloporphyrins to prepare catalysts, which can effectively activate H 2 o 2 Oxidative degradation of organic pollutants, but there are still problems such as complex preparation process, high energy consumption or unsatisfactory catalytic activity, which limit its further application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polyacrylonitrile fiber-hemin biomimetic catalyst and preparation method thereof
  • A kind of polyacrylonitrile fiber-hemin biomimetic catalyst and preparation method thereof
  • A kind of polyacrylonitrile fiber-hemin biomimetic catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0018] The present invention also provides a kind of polyacrylonitrile fiber-hemin biomimetic catalyst preparation method, and concrete steps are:

[0019] 1) Take polyacrylonitrile fiber and 2-aminoimidazole according to weight ratio 1: (0.83-4.165), add polyacrylonitrile fiber to 2-aminoimidazole aqueous solution, adjust pH value to 9.5 with sodium hydroxide, at 95 ° C React with stirring for 2-6 hours, then take it out and wash and dry it repeatedly with distilled water to obtain modified polyacrylonitrile fibers.

[0020] 2) Take the modified polyacrylonitrile fiber and hemin according to the weight ratio 1: (0.1-0.5), place the modified polyacrylonitrile fiber in the DMF solution of hemin, and react for 1-2.5 minutes at 40-60°C under stirring conditions After h, it was taken out, washed repeatedly with DMF and distilled water, and then dried to obtain a polyacrylonitrile fiber-hemin biomimetic catalyst.

[0021] The concentration of the 2-aminoimidazole aqueous solution ...

Embodiment 1

[0024] 1) Put accurately weighed 1.0g polyacrylonitrile fibers into 50ml of 2-aminoimidazole aqueous solution with a concentration of 83.3g / L, adjust the pH value to 9.5 with sodium hydroxide, and react at 95°C for 4h under stirring conditions, Then take it out and repeatedly wash and dry it with distilled water to obtain the modified polyacrylonitrile fiber.

[0025] 2) Weigh 1.0g of modified polyacrylonitrile fiber and place it in 100ml of hemin DMF solution with a concentration of 4.0g / L, react at 60°C for 2.5h under stirring conditions, take it out, wash it repeatedly with DMF and distilled water, and then dry it , to obtain the first polyacrylonitrile fiber-hemin biomimetic catalyst.

[0026] The nitrogen content of the modified polyacrylonitrile fiber before loading hemin was determined to be 34.5% by an elemental analyzer, so as to evaluate its imidazole ring group content. Determination of catalyst iron ion content: accurately weigh 0.1g catalyst, dissolve in V(HNO 3...

Embodiment 2

[0028] The concentration of 2-aminoimidazole in Step 1 of Example 1 was adjusted to 66.7 g / L, the concentration of hemin in Step 2 was adjusted to 2.0 g / L, and the rest was the same as in Example 1 to obtain the second polyacrylonitrile fiber-hemin biomimetic catalyst. Through measurement and calculation, the nitrogen content in the fiber carrier material is 30.1%, and the iron ion content of the catalyst is 10.2mg / g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polyacrylonitrile fiber-hemin bionic catalyst and a preparation method thereof. The bionic catalyst is in a fiber shape and is formed by reacting 2-aminoimidazole-modified polyacrylonitrile fiber with hemin, a natural iron porphyrin compound. The preparation method is: first use 2-aminoimidazole to modify the polyacrylonitrile fiber at pH=9.5 and temperature 95°C to obtain active groups containing imidazole ring structures, and then use the modified polyacrylonitrile obtained The fibers undergo a coordination reaction with hemin's DMF solution to obtain a polyacrylonitrile fiber-hemin biomimetic catalyst that simulates the structure of horseradish catalase. The bionic catalyst of the present invention is suitable for the oxidative degradation reaction of organic pollutants in water such as dyes. Compared with the treated hemin, the introduction of the polyacrylonitrile fiber carrier not only significantly enhances its catalytic activity, but also greatly improves its pH applicability and use. stability.

Description

technical field [0001] The invention belongs to the technical field of biomimetic catalysis, in particular to a polyacrylonitrile fiber-hemin biomimetic catalyst used in the field of oxidative degradation of organic pollutants such as dyes in waste water and a preparation method thereof. Background technique [0002] In recent years, biomimetic catalysis technology has attracted extensive attention in the treatment of refractory organic pollutants such as dyes in water. Among them, metalloporphyrins have variable valence metal ions and conjugated large π-electron structures, thus possessing redox properties, and are considered as a potential highly efficient biomimetic catalyst. However, in the treatment of organic pollutants in water, metalloporphyrin catalysts are prone to self-polymerization, resulting in a significant decrease in activity, and there are also shortcomings such as narrow pH range, poor stability, and difficulty in separation and recovery. Loading metallop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)