Water-based waterproof base film for wallpaper and preparation method of water-based waterproof base film
A wallpaper and base film technology, applied in anti-corrosion coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problems of reduced adhesion between the base film and the wall, environmental and human hazards, loose base film, etc., to achieve strong hardness , The effect of less by-products and strong adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0043] A water-based wallpaper waterproof base film, comprising the following raw materials in parts by weight:
[0044] 30 parts of modified polyisocyanate,
[0045] 20 parts of long-chain dihydric alcohols,
[0046] Hydroxy-functionalized acrylate 35 parts,
[0047] Active diluent 25 parts,
[0048] Catalyst 0.5 part,
[0049] Silica powder 20 parts,
[0050] 4.5 parts of silane coupling agent,
[0051] 1.5 parts of coagulant,
[0052] Leveling agent 0.5 parts,
[0053] 0.1 parts of curing agent,
[0054] Wherein, the curing agent is composed of dibenzoyl peroxide and a curing accelerator in a weight ratio of 3:4, and the curing accelerator is tert-butyl peroxide.
[0055] Wherein, the modified polyisocyanate is mixed with polyester polyol, diisocyanate, stannous octoate and organic solvent at a mass fraction ratio of 1:2.5:0.2:0.1, and reacted at 60-90°C for 4 hours under nitrogen protection, Then evaporate the solvent under reduced pressure and cool to room temper...
Embodiment 2
[0063] A water-based wallpaper waterproof base film, comprising the following raw materials in parts by weight:
[0064] 35 parts of modified polyisocyanate,
[0065] 30 parts of long-chain dihydric alcohols,
[0066] Hydroxy-functionalized acrylate 40 parts,
[0067] 40 parts of active diluent,
[0068] 1.8 parts of catalyst,
[0069] 30 parts of silica powder,
[0070] 8 parts of silane coupling agent,
[0071] 0.5 parts of coagulant,
[0072] Leveling agent 1 part,
[0073] 1 part curing agent,
[0074] Wherein, the curing agent is composed of dibenzoyl peroxide and a curing accelerator in a weight ratio of 1:1, and the curing accelerator is an organosiloxane compound.
[0075] Wherein, the modified polyisocyanate is mixed with polyester polyol, diisocyanate, stannous octoate and organic solvent in a mass fraction ratio of 1.5:2.5:0.2:0.1, and reacted at 90°C for 8h under the protection of nitrogen, and then reduced The solvent was evaporated under pressure and coo...
Embodiment 3
[0083] A water-based wallpaper waterproof base film, comprising the following raw materials in parts by weight:
[0084] 30 parts of modified polyisocyanate,
[0085] 15 parts of long-chain dihydric alcohols,
[0086] Hydroxy-functionalized acrylate 30 parts,
[0087] Active diluent 25 parts,
[0088] Catalyst 0.2 part,
[0089] Silica powder 10 parts,
[0090] 4 parts of silane coupling agent,
[0091] 3.5 parts of coagulant,
[0092] Leveling agent 0.8 parts,
[0093] 2 parts curing agent,
[0094] Wherein, the curing agent is composed of dibenzoyl peroxide and a curing accelerator in a weight ratio of 3:4, and the curing accelerator is an organosiloxane compound.
[0095] Wherein, the modified polyisocyanate is mixed with polyester polyol, diisocyanate, stannous octoate and organic solvent in a mass fraction ratio of 1.5: 3: 0.5: 0.3, and reacted at 90°C for 8 hours under the protection of nitrogen, and then reduced The solvent was evaporated under pressure and coo...
PUM
Property | Measurement | Unit |
---|---|---|
viscosity | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
specific surface area | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com