Preparation of a polyacrylonitrile-polyvinyl tetrazolium chelating resin

A technology of polyvinyltetrazolium and polyacrylonitrile, which is applied in water/sludge/sewage treatment, water pollutants, adsorbed water/sewage treatment, etc., and can solve difficult problems such as poor mechanical strength and limited coordination ability And other issues

Active Publication Date: 2018-07-17
QINGDAO AGRI UNIV +1
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the synthesis process of this type of resin, chloromethyl ether needs to be used, and the grafted ligand is generated by hydrogen chloride waste, which seriously pollutes the environment and the elution rate is not high.
Chelating resins based on natural raw materials, as disclosed in Chinese patents ZL201210430562.0 and ZL201010107973.7, have the advantages of wide sources, low price, and easy degradation. However, these materials have low stability, poor mechanical strength, and poor adsorption capacity. The amount is low, not easy to regenerate and other deficiencies so that its application is limited
Chelating resins synthesized by polycondensation mechanism, as announced in Chinese patents ZL200910058178.0, ZL201310083943.0, and CN200510044986.3, can partially remove heavy metal ions in water, but their coordination ability is limited, and the adsorption efficiency of heavy metal ions is not high. high, and the synthesis conditions are harsh, the preparation process is complicated, and it is difficult to meet various requirements. It is urgent to research and develop chelating resin materials that can meet the separation requirements of special environments.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation of a polyacrylonitrile-polyvinyl tetrazolium chelating resin
  • Preparation of a polyacrylonitrile-polyvinyl tetrazolium chelating resin
  • Preparation of a polyacrylonitrile-polyvinyl tetrazolium chelating resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] 1) Preparation of polyacrylonitrile-polyvinyl tetrazolium copolymer with chelating function:

[0032] Add 200ml of N,N-dimethylformamide (DMF) into a 500ml three-neck flask, weigh 10.6g of polyacrylonitrile (PAN) and add it to N,N-dimethylformamide, and pour it in turn after it is completely dissolved Add 10.7g of ammonium chloride (NH 4 Cl) and 13.0g sodium azide (NaN 3 ), heated to 60°C after it was completely dissolved, and reacted for 12 hours. After the reaction, cool to room temperature, then add the reaction solution dropwise to 0.5 mol / L hydrochloric acid solution to precipitate the polyacrylonitrile-polyvinyl tetrazolium copolymer, vacuum filter it; and wash it 3 times with distilled water , to remove Cl-, Na+ and H+ ions therein, dry under natural conditions, and finally obtain polyacrylonitrile-polyvinyl tetrazolium copolymer resin. The yield of the synthesized polyacrylonitrile-polyvinyl tetrazole copolymer is 63.1%, wherein the mass percentage of polyvin...

Embodiment 2

[0036] The preparation method of chelating resin, batching and preparation step are basically the same as embodiment 1, and difference is that the reaction temperature that polyacrylonitrile-polyvinyl tetrazolium copolymer prepares is respectively 70,80,105,120 ℃, prepares The polyacrylonitrile-polyvinyl tetrazolium copolymers with chelating function have a mass percentage of polyvinyl tetrazole of 39.8, 63.6, 80.5, 83.7%.

Embodiment 6

[0038] The preparation method of chelate resin, batching and preparation step are basically the same as embodiment 1, and difference is that dispersed phase is respectively heptane; Octane; Diphenyl ether.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of chemical materials, relates to preparation of chelate resin, and in particular relates to tetrazolyl-containing polyacrylonitrile-polyvinyltetrazole chelate resin with a function of adsorbing heavy metal ions in various water bodies. The preparation method is characterized by comprising the following steps: I, synthesizing a polyacrylonitrile-polyvinyltetrazole copolymer (PAN-PVT) through a reaction of polyacrylonitrile, sodium azide and ammonium chloride; and II, preparing spherical resin with a requested particle size from slurry of a copolymerization product under the action of a water-in-oil dispersing aid, and performing interstrand crosslinking at a rising temperature, thereby gelatinizing a liquid material into solid spherical resin. The preparation has the advantages that the chelate resin has extremely high adsorption properties through multi-point coordination of metal ions, a preparation process is simple, expensive equipment is not needed, and the application is wide.

Description

technical field [0001] The invention belongs to the technical field of chemical materials, in particular to a chelating resin, in particular to a polyacrylonitrile-polyvinyl tetrazolium chelating resin capable of absorbing heavy metal ions in various water bodies. Background technique [0002] With the rapid development of industrialization and urbanization, the problem of environmental pollution is becoming increasingly serious. The pollution of wastewater containing heavy metal ions such as lead, copper, chromium, and mercury from electrolytes, electroplating solutions, and mining and metal smelting processes is even more serious. It has become an urgent need to solve economic development, environmental protection, and drinking water safety. key problem. [0003] Chelating resin can selectively chelate specific metal ions in the form of ionic bonds or coordination bonds from a solution containing metal ions. Compared with ion exchange resins, chelating resins have a stron...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F120/44C08F8/30C08F8/00C08J3/12C02F1/28C02F101/20
Inventor 李建忠孟祥英于守晓
Owner QINGDAO AGRI UNIV