Dehumidifying rotor manufacturing environmental pulp fiber composite board

A pulp fiber and environment-friendly technology, which is applied in the field of environment-friendly pulp fiber composite paperboard for the manufacture of dehumidifying rotors, achieves the effects of improving strength and toughness, prolonging service life and satisfying high efficiency

Active Publication Date: 2017-03-15
PURESCI ENVIRONMENTAL TECH CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, brominated flame retardants have not been used in desiccant rotors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The mass fraction of each component of the composite paperboard is: 40% of asbestos-free mineral fiber, 10% of carbon fiber, 10% of polyester fiber, 5% of wood pulp, 5% of straw pulp, 10% of bamboo pulp, and 10% of brominated flame retardant. %, sizing agent 5%, additives 5%; non-asbestos mineral fiber is a mixture of silica and alumina, wherein the mass ratio of silica and alumina is 1:1.1; the brominated flame retardant is decabromine A mixture of diphenylethane, brominated epoxy resin, and brominated polystyrene, wherein the mass ratio of decabromodiphenylethane, brominated epoxy resin, and brominated polystyrene is 1.2:1.3:1; additives It is a mixture of aluminum hydroxide, sodium hydroxide and calcium sulfate, wherein the mass ratio of aluminum hydroxide, sodium hydroxide and calcium sulfate is 1.2:1.5:1.

Embodiment 2

[0014] The mass fraction of each component of the composite paperboard is: 35% of asbestos-free mineral fiber, 15% of carbon fiber, 8% of polyester fiber, 7% of wood pulp, 7% of straw pulp, 8% of bamboo pulp, 6% of brominated flame retardant %, sizing agent 8%, auxiliary agent 6%; asbestos-free mineral fiber is a mixture of silica, alumina, calcium oxide and boria, wherein the mass ratio of silica, alumina, calcium oxide and boria is 1.4: 1.4: 1.2: 1; brominated flame retardants are mixtures of decabromodiphenylethane, brominated epoxy resin, and brominated polystyrene, of which decabromodiphenylethane, brominated epoxy resin, bromine The mass ratio of polystyrene is 1.3:1.4:1; the auxiliary agent is a mixture of aluminum hydroxide, sodium hydroxide, and calcium sulfate, and the mass ratio of aluminum hydroxide, sodium hydroxide, and calcium sulfate is 1.2:1.3:1 .

Embodiment 3

[0016] The mass fraction of each component of the composite paperboard is: 30% of asbestos-free mineral fiber, 10% of carbon fiber, 10% of polyester fiber, 5% of wood pulp, 10% of straw pulp, 8% of bamboo pulp, and 12% of brominated flame retardant. %, sizing agent 6%, auxiliary agent 9%; asbestos-free mineral fiber is a mixture of alumina, calcium oxide and boron oxide, wherein the mass ratio of alumina, calcium oxide and boron oxide is 1.4:1.2:1; bromine series The flame retardant is a mixture of brominated epoxy resin and brominated polystyrene, wherein the mass ratio of brominated epoxy resin and brominated polystyrene is 1.4:1; the additives are aluminum hydroxide, sodium hydroxide, sulfuric acid A mixture of calcium, wherein the mass ratio of aluminum hydroxide, sodium hydroxide, and calcium sulfate is 1.5:1.5:1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a dehumidifying rotor manufacturing environmental pulp fiber composite board. The dehumidifying rotor manufacturing environmental pulp fiber composite board is composed of, by weight percentage, 30%-40% of non-asbestos mineral fiber, 8%-20% of carbon fiber, 8%-20% of polyester fiber, 5%-15% of wood pulp, 5%-15% of straw pulp, 5%-15% of bamboo pulp, 8%-15% of brominated flame retardant, 5%-10% of sizing agent and 5%-10% of auxiliaries. The dehumidifying rotor manufacturing environmental pulp fiber composite board is prepared from the environmentally-friendly raw materials and can improve the strength and tenacity, and meanwhile through the fire retardant, prolong the service life of dehumidifying rotors.

Description

technical field [0001] The invention relates to the field of manufacturing dehumidification rotors, in particular to an environment-friendly pulp fiber composite paperboard for manufacturing dehumidification rotors. Background technique [0002] Rotary dehumidifiers are often used in underground buildings, pharmaceuticals, food, operating rooms and other occasions. They operate in conjunction with air conditioning systems to bring the environment to the required temperature and humidity. As the core component of the rotary dehumidifier, the raw material of the dehumidification wheel, that is, the quality of the cardboard directly determines its dehumidification effect. However, the existing cardboard often has the problems of low strength and poor toughness. [0003] At the same time, nearly 80% of the flame retardants used in the dehumidification wheel are halogen-containing flame retardants, among which polybrominated diphenyl ethers and polybrominated biphenyls are the r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H15/12D21H17/67D21H21/34D21H21/16
CPCD21H15/12D21H17/675D21H17/74D21H21/16D21H21/34
Inventor 贾东新焦德华何玲丽
Owner PURESCI ENVIRONMENTAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com