Corrosion-resisting austenitic stainless steel submerged-arc welding wire and production method thereof

A technology of austenitic stainless steel and production method, applied in welding medium, welding equipment, welding/cutting medium/material, etc., can solve the problems of insufficient tensile strength, insufficient mechanical properties of welds, high cost, and avoid intergranular Corrosion, simple process, effect of improving strength

Inactive Publication Date: 2017-04-19
DANYANG HUALONG SUPERIOR STEEL
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If conventional stainless steel welding wire is used in tailor welding of this type of steel, the welded joint will have insufficient tensile strength.
[0003] Chinese patent application CN201310531804.X discloses a high-strength austenitic stainless steel submerged arc welding wire, which can be used for welding key com...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Corrosion-resisting austenitic stainless steel submerged-arc welding wire and production method thereof
  • Corrosion-resisting austenitic stainless steel submerged-arc welding wire and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0039] In this example, 3 batches of welding wires were trial-produced, and the welding wires of the comparative example were prepared through the same production process, all of which went through batching→vacuumizing→filling with argon→powering→full melting→cooling→adding ferrosilicon→adding carbon→adding titanium→ Power outage → pouring, steel ingot steelmaking process after cooling, and then forging, the initial forging temperature is 1230 ° C, the final forging temperature is 950 ° C, and rolling is carried out after air cooling. After multi-pass rolling, a semi-finished product with a diameter of 5.5 mm is obtained. The intermediate annealing temperature is 1150°C; after the annealing is completed, surface grinding treatment is carried out to treat surface cracks; the semi-finished product with a diameter of 5.5mm is drawn to 2.5mm, and solution heat treatment is performed at a temperature of 1150°C to obtain a finished welding wire. Its chemical composition is shown in T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a corrosion-resisting austenitic stainless steel submerged-arc welding wire and a production method thereof. The corrosion-resisting austenitic stainless steel submerged-arc welding wire is composed of, by mass, 0.015%-0.025% of C, 1.00% of Si or the less, 2.50% of Mn or the less, 0.020% of P or the less, 0.010% of S or the less, 12.00%-14.00% of Ni, 18.00%-20.00% of Cr, 2.00%-3.00% of Mo, 0.05%-0.10% of N and 0.05%-0.10% of Ti. The production method comprises the following steps that dosing, vacuumizing, argon gas filling, energizing, fine melting, cooling, ferrosilicon adding, carbon adding, titanium adding, power cutting and pouring are conducted, and a steel ingot is obtained after cooling; and then steel forging, steel rolling, welding wire finishing drawing and finished product heat treatment are carried out. According to the corrosion-resisting austenitic stainless steel submerged-arc welding wire, an element Nb is replaced with an element Ti, coarsening of austenite crystal grains can be effectively prevented, refining of ferrite crystal grains is achieved, intercrystalline corrosion is avoided, and the corrosion resistance of a welding wire deposited metal is improved. Meanwhile, due to the effect of nickel equivalent elements such as Ni, Mn, C and N which are favorable for formation of austenitic stainless steel, strength of the welding wire deposited metal can be effectively improved, and additionally, the price of titanium is low, so that the production cost can be reduced.

Description

technical field [0001] The invention relates to the field of welding wire technology, in particular to a corrosion-resistant austenitic stainless steel submerged arc welding wire and a production method thereof. Background technique [0002] Austenitic stainless steel is widely used in petroleum, chemical, aerospace and energy fields due to its good ductility, cold and hot workability and localized corrosion resistance at high and very low temperatures. For example, the construction of nuclear power plants requires a large amount of austenitic stainless steel. At present, most of the nuclear power plants under construction in China are pressurized water reactor nuclear power plants, and the temperature inside the reactor is as high as 350°C, which puts forward higher and higher requirements for the high temperature resistance strength of materials. The materials currently used are mainly nitrogen-controlled austenitic stainless steel (304N, 316N, etc.), and this type of ste...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/30B23K35/40
CPCB23K35/0261B23K35/308B23K35/40
Inventor 蒋红军
Owner DANYANG HUALONG SUPERIOR STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap