High-dielectric property BST (Barium Strontium Titanate), preparation method thereof and dielectric ceramic prepared by adopting same

A technology of strontium barium titanate and dielectric ceramics, applied in the field of its preparation, high dielectric performance strontium barium titanate, dielectric ceramics, can solve the problems of low electric strength, poor temperature stability and electric field stability, and achieve Excellent electrical properties, good uniformity, and high dielectric properties

Active Publication Date: 2017-04-26
MATERIAL INST OF CHINA ACADEMY OF ENG PHYSICS
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a high-dielectric ceramic material for the problems that the higher the dielectric constant is, the lower its electric strength is, and its temperature stability and electric field stability are worse. Electrical property barium strontium titanate, its preparation method and dielectric ceramic prepared by using it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-dielectric property BST (Barium Strontium Titanate), preparation method thereof and dielectric ceramic prepared by adopting same
  • High-dielectric property BST (Barium Strontium Titanate), preparation method thereof and dielectric ceramic prepared by adopting same
  • High-dielectric property BST (Barium Strontium Titanate), preparation method thereof and dielectric ceramic prepared by adopting same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] 1) Weigh chemically pure BaCO 3 (115.25g), SrCO 3 (46.31g), TiO 2 (79.80g), ZrO 2 (6.35g), CaO (2.30g), Bi 2 o 3 (11.65g) raw material, add 15.66g polyvinyl butyral as a dispersant, adopt wet method ball mill to mix evenly. The process parameters of wet ball milling are: the mass ratio of raw materials, zirconia balls, absolute ethanol and polyvinyl butyral is 1:5:6:0.06, and the ball milling time is 40 hours.

[0041] 2) After drying the ball-milled slurry in step 1) in the atmosphere, heat it at 1150° C. for 3 hours in the atmosphere to prepare barium strontium titanate raw material powder.

[0042] 3) then the raw material powder obtained in step 2 is ground and crossed a 60-mesh sieve to obtain (Ba 1-a Sr a ) 1-x- y Ca x Bi y Zr b Ti 1-b o 3 Raw material powder 235g.

[0043] 4) to step 3) gained (Ba 1-a Sr a ) 1-x-y Ca x Bi y Zr b Ti 1-b o 3 9.4 g of polyvinyl alcohol solution with a mass concentration of 3% was added to the raw material powd...

Embodiment 2

[0051] Weigh chemically pure BaCO 3 (108.84g), SrCO 3 (43.73g), TiO 2 (79.80g), ZrO 2 (6.35g), CaO (2.30g), Bi 2 o 3 (23.30g) raw material, add 15.66g polyvinyl butyral as a dispersant, adopt wet method ball mill to mix evenly. The process parameters of wet ball milling are: the mass ratio of raw materials, zirconia balls, absolute ethanol and polyvinyl butyral is 1:5:6:0.06, and the ball milling time is 40 hours.

[0052] 2) After drying the ball-milled slurry in step 1) in the atmosphere, heat it at 1150° C. for 3 hours in the atmosphere to prepare barium strontium titanate raw material powder.

[0053] 3) then the raw material powder obtained in step 2 is ground and crossed a 60-mesh sieve to obtain (Ba 1-a Sr a ) 1-x- y Ca x Bi y Zr b Ti1-b o 3 Raw material powder 235g.

[0054] 4) to step 3) gained (Ba 1-a Sr a ) 1-x-y Ca x Bi y Zr b Ti 1-b o 3 9.4 g of polyvinyl alcohol solution with a mass concentration of 3% was added to the raw material powder as...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-dielectric property BST (Barium Strontium Titanate), a preparation method thereof and dielectric ceramic prepared by adopting the same, and aims to solve the problems that the higher the dielectric constant of an existing dielectric ceramic material is, the electric strength is lower, and the temperature stability and the electric field stability of the existing dielectric ceramic material are poorer. According to the high-dielectric property BST disclosed by the invention, composition design of high-dielectric property BST ceramic is optimized starting from an ABO3 type perovskite crystal structure and a dielectric micromechanism; by improving a preparation method of raw material powder and microscopic structure regulation and control and performance optimization of a ceramic sample, homogeneity and fine grain of the prepared raw material powder are realized, and higher sintering activity is obtained. The invention provides BST dielectric ceramic having both high dielectric constant and low dielectric loss and a preparation method thereof. The BST dielectric ceramic is simple in preparation technology, lower in cost and short in period, is suitable for large-batch production and can meet the demands of industrial application, materials provided by the BST dielectric ceramic can be used in high-power microwave device systems, actual application requirements are met, and a relatively wide application prospect is obtained.

Description

technical field [0001] The invention relates to the field of materials, especially the field of high-performance dielectric materials, and specifically relates to a barium strontium titanate with high dielectric properties, a preparation method thereof and a dielectric ceramic prepared by using the same. The invention belongs to the field of inorganic material dielectric ceramics and its preparation, and provides a strontium barium titanate dielectric ceramic with high dielectric performance and low dielectric loss and a preparation method thereof, which has high application value. Background technique [0002] Ceramic dielectric materials can generally be divided into two categories: one is linear materials, and the other is nonlinear dielectric materials. Linear dielectric materials have high dielectric strength, but their dielectric constant is low, generally not more than 300. As for the nonlinear dielectric material, although it has a high dielectric constant (it can b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/49C04B35/468C04B35/622C04B35/626
CPCC04B35/4682C04B35/49C04B35/622C04B35/626C04B35/6261C04B35/6264C04B35/62675C04B2235/3208C04B2235/3213C04B2235/3215C04B2235/3244C04B2235/3298
Inventor 陈艳平李强杨晓峰李启寿唐贤臣谢金华蔡勇军
Owner MATERIAL INST OF CHINA ACADEMY OF ENG PHYSICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com