Ceramic glaze with water activating function, preparation method thereof, ceramic prepared by ceramic glaze and preparation method of ceramic

A technology for ceramic glaze and functional ceramics, applied in the field of ceramics, can solve the problems of non-absorption and health damage, and achieve the effects of strong function, stability and easy stability.

Active Publication Date: 2017-05-10
ZIBO BAIKANG ECONOMIC & TRADE
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

No matter how pure this water is, it cannot be well absorbed by the cells and chromosomes in the human body and organisms
At the same time, the water with this ring-shaped condensation structure can easily contain toxic and harmful organic substances, which will damage the health of the human body.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] (1) The ceramic glaze with the function of activating water is made of the following raw materials in mass percentage:

[0032] Ceramic glaze base material 66%, activated water functional ceramic additive 5%, nano zirconia 8%, silver phosphate 3%, nano cesium oxide 3%, yttrium oxide 5%, nano titanium dioxide 5% and tourmaline 5%;

[0033] (2) The activated water functional ceramic additive is made of the following raw materials in mass percentage:

[0034] 13% silicon dioxide, 8% aluminum oxide, 18% tourmaline ceramsite, 12% sodium boronite, 15% montmorillonite, 8% tin oxide, 8% zinc oxide, 10% strontium carbonate and germanite Block 8%.

[0035] (3) The ceramic glaze base material is made according to the following steps from the raw materials of the following mass percentages:

[0036]Feldspar 21%, quartz 23%, boric acid 11%, borax 13%, aluminum hydroxide 5%, cooked talc 6%, barium carbonate 5%, zinc oxide 8%, strontium carbonate 6% and lithium carbonate 2%, mixed ...

Embodiment 2

[0047] (1) The ceramic glaze with the function of activating water is made of the following raw materials in mass percentage:

[0048] Ceramic glaze base material 74.5%, activated water functional ceramic additive 10%, nano-zirconia 5%, copper phosphate 0.5%, nano-cerium oxide 1%, yttrium oxide 3%, nano-titanium dioxide 3% and tourmaline 3%;

[0049] (2) The activated water functional ceramic additive is made of the following raw materials in mass percentage:

[0050] 12% silicon dioxide, 14% aluminum oxide, 14% tourmaline ceramsite, 16% sodium boronite, 12% montmorillonite, 12% tin oxide, 9% zinc oxide, 5% strontium carbonate and germanite Block 6%.

[0051] (3) The ceramic glaze base material is made according to the following steps from the raw materials of the following mass percentages:

[0052] Feldspar 21%, quartz 23%, boric acid 11%, borax 13%, aluminum hydroxide 5%, cooked talc 6%, barium carbonate 5%, zinc oxide 8%, strontium carbonate 6% and lithium carbonate 2%, ...

Embodiment 3

[0063] (1) The ceramic glaze with the function of activating water is made of the following raw materials in mass percentage:

[0064] Ceramic glaze base material 60%, activated water functional ceramic additive 16%, nano-zirconia 6%, silver phosphate 5%, nano-cerium oxide 5%, yttrium oxide 2%, nano-titanium dioxide 1% and tourmaline 5%;

[0065] (2) The activated water functional ceramic additive is made of the following raw materials in mass percentage:

[0066] 18% silicon dioxide, 10% aluminum oxide, 10% tourmaline ceramsite, 19% sodium boronite, 8% montmorillonite, 9% tin oxide, 10% zinc oxide, 8% strontium carbonate and germanite Block 8%.

[0067] (3) The ceramic glaze base material is made according to the following steps from the raw materials of the following mass percentages:

[0068] Feldspar 21%, quartz 23%, boric acid 11%, borax 13%, aluminum hydroxide 5%, cooked talc 6%, barium carbonate 5%, zinc oxide 8%, strontium carbonate 6% and lithium carbonate 2%, mixed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of ceramic and particularly relates to ceramic glaze with a water activating function, a preparation method thereof, ceramic prepared by the ceramic glaze and a preparation method of the ceramic. The ceramic glaze is prepared by, by mass percentage, 60-80% of ceramic glaze base material, 5-20% of ceramic additives with the water activating function, 5-8% of nano-zirconia, 0.5-5% of phosphate, 1-5% of nano cesium oxide, 2-8% of yttrium oxide, 1-5% of nano titanium dioxide and 3-8% of tourmaline. The preparation method of the ceramic glaze includes: ball milling the ceramic glaze base material until all the ceramic glaze base material can pass a 250-mesh sieve, adding the rest of components, adding water and ceramic diluent to prepare slurry, ball milling, and discharging. The ceramic glaze has the advantages that the ceramic glaze can acts on water molecular cluster structures to allow the hydrogen bonds to be destroyed and chemical bonds to break, large molecular clusters become small molecular clusters only containing 5-6 water molecules, toxic gas dissolved in water is released at the same time, the water become slightly alkaline, and the activity of the water is increased.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to a ceramic glaze with the function of activating water, its preparation method, the prepared ceramics and the preparation method of the ceramics. Background technique [0002] The most abundant substance in the human body is water, which accounts for about 75% of the human body. For the human body, water participates in human metabolism, eliminates harmful toxins in the body, maintains aerobic respiration, etc. Therefore, the role and function of water are unique. Since all metabolic reactions take place in aqueous media, water is an essential substance for life. In daily life, the ordinary water that people generally drink without special process treatment is actually a kind of complex macromolecular water. The angle between the O-H bonds of water is about 105°. When the outside world acts, the bonds between them Corners are prone to change. Because the negative p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20C03C1/00C04B35/447C04B41/86C04B35/622
CPCC03C1/00C03C8/20C03C2205/00C03C2209/00C04B35/447C04B35/622C04B41/009C04B41/5022C04B41/86C04B2235/3418C04B2235/3463C04B2235/349C04B41/4535
Inventor 宗伟李世国刘金龙李安洋
Owner ZIBO BAIKANG ECONOMIC & TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com