Graphene-modified water-based fluorine alkyd resin and preparation method thereof

A technology of graphene modification and alkyd resin, applied in the field of water-based synthetic resin, can solve the problems of aging resistance, poor self-cleaning function, poor antistatic performance, uneven dispersion of additives, etc., and achieve excellent performance and antistatic Excellent effect, good electrical conductivity

Inactive Publication Date: 2017-05-24
英德科迪颜料技术有限公司 +1
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The structure of ordinary alkyd resin only contains C-C and C-O bonds, so the surface tension of ordinary alkyd resin is high and the antistatic performance is not good. Although alkyd resin is cheap, it cannot meet the requirements of some special coatings ; And the aging resistance and self-cleaning function are relatively poor, so it is especially important to develop a multi-functional, cost-effective water-based resin
[0005] At present, alkyd resins used on the surfaces of plastic, wood, metal, etc. need to add other additives for anti-fouling, waterproof, and anti-static. The additives are prone to shortcomings such as uneven dispersion and limited performance in the coating. Therefore, an anti-fouling , Modified alkyd resin with antistatic function is imperative

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene-modified water-based fluorine alkyd resin and preparation method thereof
  • Graphene-modified water-based fluorine alkyd resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A graphene modified water-based fluoroalkyd resin, its preparation process is as follows:

[0032] a. Add 2.0 parts of graphene oxide and 2.0 parts of dimethylolpropionic acid into a four-port reactor equipped with a thermometer, condenser and stirrer, and add 8.0 parts of polyisocyanate dropwise at a constant speed of 60-70 ° C under stirring conditions, The dropping time is 1h, then continue to heat up to 80°C, and keep warm for 2h to obtain the active intermediate A, which is ready for use;

[0033] b. In a reactor with a stirring and dripping device, add 4.0 parts of acrylic monomer, 3.0 parts of fluoroolefin monomer and 0.07 part of catalyst azobisisobutyronitrile according to the recipe requirements, and stir evenly to obtain a monomer Mixture B, ready to use;

[0034]c. In a four-port reactor equipped with a thermometer, condenser, water separator, and agitator, add 8.0 parts of vegetable oil fatty acid, 2.5 parts of phthalic anhydride, 4.0 parts of neopentyl gl...

Embodiment 2

[0037] A graphene modified water-based fluoroalkyd resin, its preparation process is as follows:

[0038] a. Add 2.5 parts of graphene oxide and 2.0 parts of dimethylolpropionic acid into a four-port reactor equipped with a thermometer, condenser and stirrer, and add 8.5 parts of polyisocyanate dropwise at a constant speed of 60-70 ° C under stirring conditions, The dropping time is 1h, then continue to heat up to 80°C, and keep warm for 2h to obtain the active intermediate D, which is ready for use;

[0039] b. In the reactor with stirring and dripping device, add 4.5 parts of acrylic monomer, 3.5 parts of fluoroolefin monomer and 0.08 part of catalyst azobisisobutyronitrile according to the recipe requirements, and stir evenly to obtain a monomer Mixture E, ready to use;

[0040] c. In a four-port reactor equipped with a thermometer, condenser, water separator, and agitator, add 8.5 parts of vegetable oil fatty acid, 2.0 parts of phthalic anhydride, 4.5 parts of neopentyl g...

Embodiment 3

[0043] A graphene modified water-based fluoroalkyd resin, its preparation process is as follows:

[0044] a. Add 3.5 parts of graphene oxide and 1.5 parts of dimethylolpropionic acid into a four-port reactor equipped with a thermometer, condenser and stirrer, and add 9.5 parts of polyisocyanate dropwise at a constant speed of 60-70 ° C under stirring conditions, The dropping time is 1h, then continue to heat up to 80°C, and keep warm for 2h to obtain the active intermediate G, which is ready for use;

[0045] b. In a reactor with a stirring and dripping device, add 3.5 parts of acrylic monomer, 2.5 parts of fluoroolefin monomer and 0.06 part of catalyst azobisisobutyronitrile according to the recipe requirements, and stir evenly to obtain a monomer Mixture H, ready to use;

[0046] c. In a four-port reactor equipped with a thermometer, condenser, water separator, and agitator, add 9.5 parts of vegetable oil fatty acid, 2.5 parts of phthalic anhydride, 5.5 parts of neopentyl g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to graphene-modified water-based fluorine alkyd resin and a preparation method thereof. The graphene-modified water-based fluoroalate resin consists of vegetable oil fatty acid, organic acid anhydride, polyatomic alcohol, polybasic acid, dimethylolpropionic acid, a fluoroelene monomer, a neutralizing agent, polyisocyanate, grapheme, an acrylic monomer and deionized water. The graphene-modified water-based fluorine alkyd resin prepared by the preparation method provided by the invention has good adhesion, stain resistance, water resistance, alkali resistance and wear resistance, good electrical conductivity, excellent antistatic performance and the like, and is widely used for water-based wood coatings, water-based industrial coatings, water-based anti-fouling coatings, water-based anti-corrosion coatings and water-based special function coatings.

Description

technical field [0001] The invention relates to a preparation method of a modified water-based alkyd resin, in particular to a graphene-modified water-based fluoroalkyd with high hardness, low cost, extremely low surface tension, good electrical conductivity, anti-fouling and anti-static functions The resin belongs to the technical field of water-based synthetic resin. Background technique [0002] Alkyd resin was developed in the 1930s. It has the characteristics of good adhesion, brightness and plumpness of the paint film, and has good construction performance, but its paint film is soft, slow drying, long curing time, weather resistance, water resistance, Poor alkali resistance. Alkyd resins are resins that are widely used in coatings at present. [0003] With the continuous advancement of science and technology and the continuous enhancement of people's awareness of environmental protection, the environmental protection requirements for coatings are getting higher and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G63/682C08G63/685C08G18/34C08G63/49C08F283/01C08F220/00C08F220/22
CPCC08G63/6826C08F283/01C08G18/348C08G63/48C08G63/6856C08F220/00C08F220/22
Inventor 许钧强陆明张武刘敏徐业雄
Owner 英德科迪颜料技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap