Imitated active paint printing adhesive, and preparation method and application method thereof

A paint printing and adhesive technology, applied in dyeing, textile and papermaking, etc., can solve the problems of waste of raw materials, low solid content, poor bonding effect, etc., to enhance application performance, improve performance indicators, and improve work efficiency Effect

Active Publication Date: 2017-05-31
苏州联胜化学有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In recent years, a kind of imitation active pigment printing adhesive has appeared on the market. Although this kind of product has a certain improvement in hand feeling, and the dry / wet rubbing fastness can also reach level 3, but due to the inherent defects of acrylate adhesive , under the condition that the adjusted formula is soft, the adhesive is easy to lose water and solidify
During the printing process, the adhesive is easy to attach to the printing screen. When the adhesive loses water, it is easy to appear the phenomenon of sticking and blocking the screen, which seriously affects the production efficiency of the printing and dyeing factory.
[0006] On the other hand, in the existing imitation active pigment printing adhesive processing technology, its raw material mixing is not very uniform, its mixture is easy to layer, and its follow-up reaction is not very sufficient
Therefore, the adhesive directly obtained by this process has a relatively low solid content, generally between 35% and 40%, which will cause waste of raw materials on the one hand; on the other hand, its bonding effect is relatively poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Imitated active paint printing adhesive, and preparation method and application method thereof
  • Imitated active paint printing adhesive, and preparation method and application method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Weigh 131 g of butyl acrylate, 54 g of isooctyl acrylate, 40 g of methyl methacrylate, 16 g of styrene, 8 g of acrylic acid, 10.3 g of N-methylol acrylamide, and 10 g of castor oil polyoxyethylene ether phosphate triethanolamine salt. 1.8 g of double bond group-containing bisalkylsulfosuccinate salt, 2.4 g of fatty alcohol polyoxyethylene ether, 0.52 g of sodium persulfate, and 80 g of deionized water are added to the first reaction vessel to obtain a raw material mixture;

[0048] Stir the raw material mixture continuously for 20 minutes at a speed of 1800 rpm to 2200 rpm at room temperature;

[0049] Using a high-pressure homogenizer to emulsify the raw material mixture for 30 minutes to prepare a milky white pre-emulsion without layering;

[0050] Weigh 40g of pre-emulsion into the second reaction vessel;

[0051] Adding 0.9 g of bis-alkyl sulfosuccinate containing double bond groups, 0.52 g of sodium persulfate and 145 g of deionized water into the second reaction vessel;

...

Embodiment 2

[0058] Weigh 131g butyl acrylate, 54g isooctyl acrylate, 20g acrylonitrile, 36g styrene, 8g acrylic acid, 10.3g N-methylol acrylamide, 10g castor oil polyoxyethylene ether phosphate triethanolamine salt, containing double bond 1.8 g of dialkyl sulfosuccinate salt, 2.4 g of fatty alcohol polyoxyethylene ether, 0.52 g of sodium persulfate, and 80 g of deionized water were added to the first reaction vessel to obtain a raw material mixture;

[0059] Stir the raw material mixture continuously for 20 minutes at a speed of 1800 rpm to 2200 rpm at room temperature;

[0060] Using a high-pressure homogenizer to emulsify the raw material mixture for 30 minutes to prepare a milky white pre-emulsion without layering;

[0061] Weigh 40g of pre-emulsion into the second reaction vessel;

[0062] Adding 0.9 g of bis-alkyl sulfosuccinate containing double bond groups, 0.52 g of sodium persulfate and 145 g of deionized water into the second reaction vessel;

[0063] Start stirring, continue to stir the...

Embodiment 3

[0069] Weigh 130g butyl acrylate, 53g isooctyl acrylate, 20g acrylonitrile, 36g styrene, 8g acrylic acid, 5g hydroxyethyl acrylate, 5g diacetone acrylamide, 12g fatty alcohol polyoxyethylene ether phosphate triethanolamine salt, containing 1.8 g of double-bond bis-alkyl sulfosuccinate salt, 2.4 g of castor oil polyoxyethylene ether, 0.52 g of sodium persulfate, and 80 g of deionized water are added to the first reaction vessel to obtain a raw material mixture;

[0070] Stir the raw material mixture continuously for 20 minutes at a speed of 1800 rpm to 2200 rpm at room temperature;

[0071] Using a high-pressure homogenizer to emulsify the raw material mixture for 30 minutes to prepare a milky white pre-emulsion without layering;

[0072] Weigh 40g of pre-emulsion into the second reaction vessel;

[0073] Adding 0.9 g of bis-alkyl sulfosuccinate containing double bond groups, 0.52 g of sodium persulfate and 145 g of deionized water into the second reaction vessel;

[0074] Start stirrin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an imitated active paint printing adhesive, and a preparation method and an application method thereof. The adhesive is prepared from the preparation raw materials: 44 to 50 percent of acrylic monomers, 3 to 9 percent of ethyl monomers, 1 to 3 percent of special surfactants, 0.5 to 2 percent of cross-linking agents, 0.1 to 0.5 percent of water-soluble initiators, 0.3 to 0.8 percent of anionic emulsifiers, 0.2 to 0.7 percent of nonionic emulsifiers and the balance of deionized water, wherein the raw ingredient percentage is the weight percentage.

Description

Technical field [0001] The invention belongs to the field of textile printing coating auxiliary agents, in particular to an imitation active pigment printing adhesive and a preparation method and application method thereof. Background technique [0002] Polyacrylate emulsion is a water-soluble polymer product formed by homopolymerization or copolymerization of acrylate monomers and special monomers. It has excellent film-forming properties, light stability and weather resistance, and good acid / alkali resistance. Water resistance, scratch resistance and adhesion. Therefore, it has a wide range of applications in the textile field, such as textile sizing, coating and pigment printing applications. [0003] my country has accumulated a lot of technology and literature in the research of water-based acrylic emulsion. With the continuous investment in technology research and development, the application requirements are becoming more and more refined, and the textile industry has also ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/18C08F220/06C08F220/48C08F220/14C08F212/08C08F283/06D06P1/52
CPCD06P1/525D06P1/5257C08F220/18C08F283/065C08F220/1804C08F220/1808C08F220/48C08F212/08C08F220/06C08F220/281C08F220/58C08F220/14
Inventor 施建刚黄祥凤罗武华涂胜宏
Owner 苏州联胜化学有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap