Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Permeating and curing inorganic mineral color dry powder paint for highway bridge

An inorganic mineral, highway bridge technology, applied in powder coatings, fire retardant coatings, cement coatings, etc., can solve the problems of difficult to master the ratio of liquid and powder, large differences in coating performance, difficult to make color, etc., to achieve acid and alkali resistance. Good, easy to use, easy to prepare effect

Inactive Publication Date: 2017-05-31
MOBAO CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the existing dry powder coating is used, it is difficult to master the ratio of liquid and powder. Different ratios will easily cause large differences in coating performance, and it is not easy to make colors. After a period of use, problems such as anti-alkali and peeling are easy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A permeation-curing inorganic mineral colored dry powder coating for highway bridges proposed by the present invention comprises the following raw materials in parts by weight: 25 parts of Portland cement, 20 parts of vinyl acetate copolymer, 22 parts of styrene copolymer, poly 9 parts of silylene disiloxane, 12 parts of quicklime and ceramic powder composition, 4 parts of coupling agent, 1.5 parts of curing agent, 3 parts of reinforcing agent, 2 parts of inorganic adhesive, 3 parts of antibacterial agent, mineral color stone 7 parts, 4 parts of pigment.

[0019] Its preparation method comprises the following steps:

[0020] S1. According to the specific gravity, weigh the above-mentioned raw materials respectively;

[0021] S2. Heat the vinyl acetate copolymer, styrene copolymer and polysilylene disiloxane weighed in step S1 to 140°C, add the weighed coupling agent and curing agent, Min speed stirring and mixing for 0.8h, mixing evenly and cooling to room temperature...

Embodiment 2

[0026] A permeation-curing inorganic mineral color dry powder coating for highway bridges proposed by the present invention comprises the following raw materials in parts by weight: 40 parts of Portland cement, 18 parts of vinyl acetate copolymer, 20 parts of styrene copolymer, poly 12 parts of siloxane, 20 parts of sand and hydroxyapatite composition, 5 parts of coupling agent, 3 parts of curing agent, 2 parts of reinforcing agent, 1 part of inorganic adhesive, 2.5 parts of antibacterial agent, 4 parts of mineral color stone, pigment 3 copies.

[0027] Its preparation method comprises the following steps:

[0028] S1. According to the specific gravity, weigh the above-mentioned raw materials respectively;

[0029] S2. Heat the vinyl acetate copolymer, styrene copolymer and polysiloxane weighed in step S1 to 135°C, add the weighed coupling agent and curing agent, and stir and mix at a speed of 160r / min 1.5h, mix uniformly and cool to room temperature to obtain mixture A;

...

Embodiment 3

[0034] A permeation-curing inorganic mineral colored dry powder coating for highway bridges proposed by the present invention comprises the following raw materials in parts by weight: 20 parts of Portland cement, 25 parts of vinyl acetate copolymer, 15 parts of styrene copolymer, poly 8 parts of carbosilane, 15 parts of the composition of alginite and titanium dioxide, 2 parts of coupling agent, 1 part of curing agent, 6 parts of reinforcing agent, 1.5 parts of inorganic adhesive, 2 parts of antibacterial agent, 5 parts of mineral color stone, 3.5 parts of pigment .

[0035] Its preparation method comprises the following steps:

[0036] S1. According to the specific gravity, weigh the above-mentioned raw materials respectively;

[0037] S2. Heat the vinyl acetate copolymer, styrene copolymer and polycarbosilane weighed in step S1 to 160°C, add the weighed coupling agent and curing agent, and stir and mix at a speed of 250r / min for 1h , mix uniformly and cool to room temperat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses permeating and curing inorganic mineral color dry powder paint for a highway bridge. The permeating and curing inorganic mineral color dry powder paint is prepared from, by weight, 20-40 parts of Portland cement, 15-25 parts of vinyl acetate copolymer, 15-25 parts of styrol copolymer, 8-12 parts of organosilicon compound, 10-20 parts of inorganic filler, 2-6 parts of coupling agent, 1-3 parts of curing agent, 2-6 parts of fortifier, 1-3 parts of inorganic adhesive, 1-3 parts of antibacterial agent, 4-8 parts of mineral colored stone and 3-5 parts of pigment. The permeating and curing inorganic mineral color dry powder paint for the highway bridge has good anti-leakage, antibacterial and anti-mold effects, is good in weather resistance, acid and alkali resistance and flame retardant effect, free of toxicity and smell, and releases no harmful substances; the preparing method is simple and low in preparing cost, and the color dry powder paint can effectively avoid alkali efflorescence and desquamation problems, prolongs the service life of the highway bridge when used in the highway bridge and is worthy of popularization.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a permeation-curing inorganic mineral color dry powder coating for highway bridges. Background technique [0002] The environmental pollution caused by the waste water, sludge, waste and waste residue discharged by the paint industry every year cannot be underestimated. In particular, a large amount of organic volatile compounds emitted during the production and use of coatings has attracted great attention from relevant state departments and the general public, and the advantages of environmentally friendly powder coatings have gradually emerged. Color dry powder coating is formulated with inorganic gelling materials and redispersible polymer resin powder as film-forming aids, adding composite inorganic fillers and pigments. It is a new cement-based modern building decoration material combining inorganic and organic. Dry powder coatings are compounded with common substances an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/08C09D5/03C09D5/14C09D5/18C09D7/12
CPCC09D1/08C09D5/033C09D5/14C09D5/18
Inventor 马从勇
Owner MOBAO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com