White polyolefin glue film with good water resistance performance, and preparation method thereof

A technology for encapsulating adhesive films and polyolefins, which can be used in adhesives, film/sheet adhesives, photovoltaic power generation, etc., which can solve the problem of prolonging the power generation cycle of solar double-glass modules, reducing the service life of double-glass modules, and increasing potential-induced attenuation. Probability and other issues, to achieve excellent anti-ultraviolet performance, reduce water vapor transmission rate, difficult to move and diffuse effects

Active Publication Date: 2017-05-31
GUANGZHOU LUSHAN NEW MATERIALS +1
View PDF5 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the traditional double-glass high-reflection module is mainly EVA film, and the back is a white high-reflection EVA film, but the long-term use temperature of solar cells is about 70°C. At this temperature, EVA will creep. It will gradually decompose under the environment, and the water vapor transmission rate of EVA is 10-30g / m 2 Day, water vapor easily penetrates through the side of the double-glass high-reflective module, and EVA is hydrolyzed to release acetic acid, which causes the cell to be corroded, increases the probability of potential-induced decay (PID) and snail marks, and reduces the service life of the double-glass module , so it is necessary to develop a high anti-encapsulation material with low water permeability to prolong the power generation cycle of solar double glass modules

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • White polyolefin glue film with good water resistance performance, and preparation method thereof
  • White polyolefin glue film with good water resistance performance, and preparation method thereof
  • White polyolefin glue film with good water resistance performance, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A white polyolefin encapsulating adhesive film with good water-blocking performance, comprising the following components in parts by weight: 100 parts of polyolefin resin A with a melt index of 3 g / 10 min and a melting point of 115°C; 20 parts of a melt index of 10 g / 10 min , polyolefin resin B with a melting point of 100°C; 2.0 parts of carbaperoxyacid-O,O-(1,1-dimethylethyl)-O-(2-ethylhexyl) ester, 0.6 parts of triallyl Base isocyanurate, 0.8 parts of vinyltriethoxysilane, 25 parts of color masterbatch, 0.4 parts of bis(2,2,6,6-tetramethyl-4-piperidinol) sebacate, 0.6 parts of [2-hydroxy-4-(octyloxy)phenyl] phenyl ketone, mix the above components evenly through the mixing tank, put them into the casting machine and set the parameters, after plasticizing extrusion, casting , traction, and winding to make a white polyolefin encapsulation film for solar cells with high water resistance.

[0040]Wherein, the color masterbatch is a mixture of 40% titanium dioxide and 60% ...

Embodiment 2

[0042] A white polyolefin encapsulating adhesive film with good water blocking performance, comprising the following components in parts by weight: 100 parts of polyolefin resin A with a melting index of 10 g / 10 min and a melting point of 105°C; 25 parts of a polyolefin resin A with a melting index of 15 g / 10 min , polyolefin resin B with a melting point of 90°C; 1.5 parts of tert-butyl peroxycarbonate-2-ethylhexyl, 0.8 parts of triallyl isocyanurate, 0.7 parts of ethylene triethoxysilane, 22 1 part of masterbatch, 0.1 part of bis(2,2,6,6-tetramethyl-4-piperidinol) sebacate, 0.5 part of [2-hydroxy-4-(octyloxy)phenyl]benzene Base ketone, mix the above components evenly through the mixing tank, put them into the tape casting machine and set the parameters, after plasticizing extrusion, casting, pulling, and winding, it is made into a white high-resistance polyolefin for solar cells Packaging film.

[0043] Wherein, the color masterbatch is a mixture of 46% titanium dioxide and ...

Embodiment 3

[0045] A white polyolefin encapsulating adhesive film with good water-blocking performance, comprising the following components in parts by weight: 100 parts of polyolefin resin A with a melt index of 15 g / 10 min and a melting point of 95°C; 30 parts of a melt index of 25 g / 10 min , polyolefin resin B with a melting point of 80°C; 1.2 parts of tert-butyl peroxy 2-ethylhexyl carbonate, 1.0 parts of 1,3,5-tri-2-propenyl-1,3,5-triazine -2,4,6(1H,3H,5H)-trione, 0.6 parts of triethoxyethylene silane, 20 parts of masterbatch, 0.3 parts of bis(2,2,6,6-tetramethyl-4- Piperidinol) sebacate, 0.4 parts of [2-hydroxy-4-(octyloxy) phenyl] phenyl ketone, mix the above components evenly through the mixing tank, put them into the casting machine and set the parameters , after plasticizing extrusion, casting, pulling, and winding, it is made into a white polyolefin encapsulation film for solar cells with high water resistance.

[0046] Wherein, the color masterbatch is a mixture of 52% titani...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melting pointaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a white polyolefin glue film with good water resistance performance. The white polyolefin glue film comprises the following components in parts by weight: 100 parts of polyolefin resin A, 20-50 parts of polyolefin resin B, 0.6-2.0 parts of an organic peroxide initiator, 0.5-2.5 parts of a cross-linking aid, 0.3-0.8 part of a tackifying coupling agent, 15-25 parts of a color master batch, 0.1-0.6 part of a light stabilizer, and 0.1-0.6 part of an ultraviolet absorber. The white polyolefin glue film with the good water resistance performance effectively reduces the penetration rate of water vapor, thus improving the permeation of the water vapor through the side face of a solar cell dual-glass assembly, avoiding corrosion of a cell piece, effectively preventing generation of snail patterns, achieving the anti-PID effect, and prolonging the service life of the dual-glass assembly. The invention also discloses a preparation method of the white polyolefin glue film with the good water resistance performance. The process is simple, the operation is simple and convenient, and the cost is low.

Description

technical field [0001] The invention relates to the technical field of packaging materials for solar cell modules, in particular to a white polyolefin packaging adhesive film with good water resistance and a preparation method thereof. Background technique [0002] With the continuous development of society, environmental pollution and energy shortage have become the biggest challenges faced by human beings. Using solar cells to convert clean and renewable solar energy into electrical energy is one of the most effective ways to solve these two problems. The life of ordinary solar cells is 30 years, while the use of components is only 25 years, so the high service life of solar cell components has become the focus of people's increasing attention, and double-glass high-reflective components have a higher power generation in the life cycle Glass components are more than 10% higher, and the service life is more than 5 years longer than ordinary single glass components. The att...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/00C09J123/00C09J11/04C09J11/06H01L31/049
CPCH01L31/0481C09J7/00C09J11/04C09J11/06C09J123/00C08L2201/08C08L2203/204C08L2205/025C08L2205/03C09J2203/322C09J2301/408C08L23/00C08K13/02C08K2003/2241C08K2003/2227C08K5/3435C08K5/132Y02E10/50
Inventor 阳志荣李伟博郭森余鹏唐舫成汪加胜
Owner GUANGZHOU LUSHAN NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap