A high-weather-resistant comprehensive exterior wall special paint and its preparation method

A comprehensive, high-weather-resistant technology, applied in the field of building decoration materials, can solve the problems of poor anti-fouling, poor friction resistance, affecting the decorative effect and use value, fading, etc. performance, the effect of prolonging the service life

Inactive Publication Date: 2017-06-09
SHENYANG SHUNFENG NEW MATERIAL CO LTD
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the currently generally used exterior wall paints only serve to decorate and protect the wall from external environmental influences, and do not have the functions of heat insulation and heat preservation, and the weather resistance and waterproof performance of exterior wall paints need to be further improved. improvement, so the current exterior wall paints have certain limitations in use; the existing exterior wall paints are generally composed of water, pigments, film-forming aids, dispersants, defoamers, thickeners, It is formulated with wetting agent, filler, antifreeze, etc., and its stain resistance and friction resistance are poor; in summer, due to strong ultraviolet radiation, the paint film is very easy to age, and loses light, fades, changes color, cracks, Chalking phenomenon seriously affects the decorative effect and use value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] This embodiment provides a high weather resistance comprehensive exterior wall special paint, which is prepared from the following raw materials in weight percentage: 18% superfine ground calcium carbonate, 14% covering polymer, 25% acrylate emulsion, ethylene-acetic acid Ethylene copolymer emulsion 10%, silicon acrylic emulsion 35%, propylene glycol methyl ether acetate 7%, hydroxy ethyl cellulose 5.5%, barite powder 6.5% and auxiliary materials 55%.

[0029] Described auxiliary material comprises the raw material of following percentage by weight: wollastonite powder 13%, rutile titanium dioxide 17%, wetting and dispersing agent 9%, associative thickener 13%, antifoaming agent 2.5%, film-forming aid 2.3% %, hydrophobic agent 4.5%, leveling agent 3%, 1,2-benzisothiazol-3-one 1.4%, ammonia 1.1%, water 25%.

Embodiment 2

[0031] This embodiment provides a high weather resistance comprehensive exterior wall special paint, which is prepared from the following raw materials in weight percentage: 19% superfine ground calcium carbonate, 14% covering polymer, 27% acrylate emulsion, ethylene-acetic acid Ethylene copolymer emulsion 11%, silicon acrylic emulsion 37%, propylene glycol methyl ether acetate 8%, hydroxy ethyl cellulose 5.5%, barite powder 7% and auxiliary materials 55%.

[0032] The auxiliary materials include the following raw materials in weight percentage: 14% of wollastonite powder, 18% of rutile titanium dioxide, 9% of wetting and dispersing agent, 13% of associative thickener, 2% of defoamer, and 2.4% of film-forming aid , hydrophobic agent 5%, leveling agent 3%, 1,2-benzisothiazol-3-one 1.8%, ammonia 1.2%, water 25%.

Embodiment 3

[0034] This embodiment provides a high weather resistance comprehensive exterior wall special paint, which is prepared from the following raw materials in weight percentage: 18% superfine ground calcium carbonate, 14% covering polymer, 27% acrylate emulsion, ethylene-acetic acid Ethylene copolymer emulsion 15%, silicon acrylic emulsion 38%, propylene glycol methyl ether acetate 8%, light ethyl cellulose 6%, barite powder 7% and auxiliary materials 60%.

[0035] The auxiliary materials include the following raw materials in weight percentage: 13% wollastonite powder, 17% rutile titanium dioxide, 9% wetting and dispersing agent, 14% associative thickener, 2.5% defoamer, and 2.3% film-forming aid , hydrophobic agent 4%, leveling agent 3%, 1,2-benzisothiazol-3-one 1.4%, ammonia 1.1%, water 30%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-weather-resistance comprehensive exterior wall special paint and its preparation method, which belong to the technical field of building decoration materials. Polymer 13%~15%, Acrylate emulsion 20%~30%, Ethylene-vinyl acetate copolymer emulsion 5%~15%, Silicon acrylic emulsion 30%~40%, Propylene glycol methyl ether acetate 5%~9%, 4%-7% of light ethyl cellulose, 5%-8% of barite powder and 50%-60% of auxiliary materials; the invention has high weather resistance, good stain resistance, friction resistance, powder resistance, The advantages of aging, waterproof performance, etc., long service life.

Description

technical field [0001] The invention belongs to the technical field of building decoration materials, and in particular relates to a high-weather-resistance comprehensive exterior wall special paint and a preparation method thereof. Background technique [0002] Exterior wall paint is mainly used in buildings, and it is a kind of paint for painting the facade of buildings. It has two functions: one is to protect the building from the external environment or minimize its impact. After the exterior wall paint is applied to the building, it can form a continuous coating film on its surface. This coating film has corrosion resistance , anti-pollution, anti-ultraviolet radiation, and anti-bacterial erosion, protect the steel bars from corrosion, and protect the concrete from carbonization and chlorination, so as to prolong the life of the building; the second is to decorate and beautify the building, and the exterior wall paint is painted on the surface of the building Finally, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D123/08C09D101/28C09D7/12C09D5/32C09D5/33C09D5/08
Inventor 刘春峰张伟陈栋张程程徐林
Owner SHENYANG SHUNFENG NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap