A kind of thickening profile control agent and preparation method thereof

A profile control agent and initiator technology, applied in chemical instruments and methods, drilling compositions, etc., can solve the problem that the profile control agent has no viscosity-increasing ability and can not play a displacement role, so as to ensure the strength and expansion performance, The effect of uniform cross-linked structure

Active Publication Date: 2019-02-22
CHINA NAT OFFSHORE OIL CORP +1
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The present invention aims to solve the technical problem that the existing profile control agent has no viscosity-increasing ability and cannot play a displacement role, and provides a viscosity-increasing profile-control agent and its preparation method. The profile-control agent can continuously increase the viscosity of formation water, play a certain role in displacing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of thickening profile control agent and preparation method thereof
  • A kind of thickening profile control agent and preparation method thereof
  • A kind of thickening profile control agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037]

[0038] Dissolve 30.00g of acrylamide in 94.00g of water, add 3.00g of the main crosslinking agent N,N-dimethylacrylamide and 0.52g of lithium magnesium silicate to the aqueous solution of acrylamide monomer in sequence, stir until clarified, then add 0.12 g of the secondary crosslinking agent polyethylene glycol diacrylate, mixed evenly to obtain a monomer solution; while uniformly stirring, nitrogen was passed through the polymerization system to remove oxygen for 30 minutes;

[0039] Take by weighing 0.06g potassium persulfate and dissolve in 6.00g water to prepare initiator solution;

[0040]Mix the monomer solution and the initiator solution, and put the mixed reaction solution in a water bath at 40°C for 10.0 hours, then raise the temperature to 60°C for 8.0 hours to increase the conversion rate;

[0041] The product obtained in the above steps was pulverized and dried in an oven at 60°C until constant weight;

[0042] Use a 12000r / min universal pulverizer to...

Embodiment 2

[0044]

[0045] Dissolve 30.00g of acrylamide in 94.00g of water, add 1.80g of the main crosslinking agent N,N-dimethylacrylamide and 2.60g of lithium magnesium silicate to the aqueous solution of acrylamide monomer in sequence, stir until clarified, then add 0.30 The secondary cross-linking agent polyethylene glycol diacrylate of g is mixed uniformly to obtain a monomer solution;

[0046] Take by weighing 0.06g potassium persulfate and dissolve in 6.00g water to prepare initiator solution;

[0047] Mix the monomer solution and the initiator solution, and deoxygenate with nitrogen for 30 minutes;

[0048] Put the mixed reaction solution after deoxygenation into a water bath at 40°C for 10.0 hours, then raise the temperature to 60°C for 8.0 hours to increase the conversion rate;

[0049] The product obtained in the above steps was pulverized and dried in an oven at 60°C until constant weight;

[0050] The dried product is pulverized by a 12000r / min universal pulverizer, an...

Embodiment 3

[0065] Take Example 3 as an example:

[0066] Dissolve 30.00g of acrylamide in 94.00g of water, add 0.90g of the main crosslinking agent N,N-dimethylacrylamide and 1.12g of lithium magnesium silicate to the aqueous solution of acrylamide monomer in sequence, stir until clarified, then add 0.21 The secondary cross-linking agent polyethylene glycol diacrylate of g is mixed uniformly to obtain a monomer solution;

[0067] Take by weighing 0.06g potassium persulfate and dissolve in 6.00g water to prepare initiator solution;

[0068] Mix the monomer solution and the initiator solution, and deoxygenate with nitrogen for 30 minutes;

[0069] Put the mixed reaction solution after deoxygenation into a water bath at 40°C for 10.0 hours, then raise the temperature to 60°C for 8.0 hours to increase the conversion rate;

[0070] The product obtained in the above steps was pulverized and dried in an oven at 60°C until constant weight;

[0071] Use a 12000r / min universal pulverizer to pul...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of a chemical reagent for oil production, and discloses a viscosity-increasable profile control agent and a preparation method thereof. The profile control agent is obtained through adding functional monomers, inorganic nanometer particles, main crosslinking agents and auxiliary crosslinking agents into an acrylamide monomer water solution, introducing nitrogen gas to remove dissolved oxygen and adding initiators under the water bath condition of 40 to 60 DEG C for polymerization; after the polymerization is completed, pelleting, drying and crushing are performed; a final product is obtained. The prepared profile control agent can realize the continuous viscosity increase on formation water to achieve a certain displacement effect; meanwhile, good anti-salt performance is realized; the water absorption swelling can be generated in the high-concentration salt brine; after the expansion, high intensity is still realized, so that the high seepage layer in an oil deposit can be effectively sealed and plugged; the profile control effect is achieved.

Description

technical field [0001] The invention belongs to the technical field of chemical reagents for oil recovery, in particular, it relates to a pre-crosslinked polymer particle capable of profile control and displacement, namely a viscosity-increasing profile control agent and a preparation method thereof . Background technique [0002] Most of the tertiary oil recovery in my country adopts the water flooding method. After decades of water injection development, the heterogeneity of the reservoir has been strengthened, and the displacement fluid has become increasingly serious along the high-permeability layer or between layers, and the sweep coefficient has been greatly reduced. The increase of water cut and the decrease of oil recovery rate make the cost of energy and equipment in the process of oil recovery continue to rise. The use of profile control agent can effectively reduce water cut and improve oil recovery efficiency. [0003] Common profile control agents are inorgani...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F283/06C08F220/56C08F220/54C08F220/58C08F226/10C08F222/14C08F226/02C08F220/34C08F2/44C09K8/512C09K8/588
CPCC08F2/44C08F220/56C08F283/065C09K8/512C09K8/588C08F220/54C08F226/10C08F222/102C08F226/02C08F220/34
Inventor 王成胜罗杰陈士佳冯玉军吴晓燕翁大丽易飞黄波胡陈张润芳吕鹏刘观军
Owner CHINA NAT OFFSHORE OIL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products